研究了不同碱质量浓度、温度、加入催化剂等条件下聚羟基脂肪酸酯(PHA)纤维的碱降解动力学,并对降解速率曲线进行拟合,得到适合描述其反应行为的动力学模型:PHA质量浓度的增大、温度的升高以及催化剂的加入,都会使PHA
The alkali degradation kinetics of polyhydroxyalkanoates(PHA) fibers under conditions of different alkali concentration, different temperature and catalyst was studied. The degradation rate curve was fitted to obtain a suitable kinetic model for describing the reaction behavior. The alkali degradation kinetics of PHA fibers accorded with quasi-second-order kinetics model, and the fitting coefficient was more than 0.90. With the increase of alkali concentration, temperature and in the presense of catalyst, the degradation rate of PHA fiber increased.
引文
[1]卞士祥,王闻,周桂雄,等.生物合成聚羟基脂肪酸酯(PHA)的研究进展[J].新能源进展,2016,4(6):436-442.
[2]郭静,相恒学,王倩倩.聚羟基脂肪酸酯成纤技术的研究进展[J].合成纤维工业,2010,33(4):46-49.
[3]王延伟,杨柳,王治辉,等.PCL增韧PHA的结晶性能和力学性能研究[J].塑料科技,2016,44(8):29-32.
[4]于翔,王娜,王亚飞,等.PHA/nHA复合材料的结晶性能和流变性能研究[J].塑料科技,2015,43(12):69-73.
[5]熊玉翠.聚羟基脂肪酸酯纳米颗粒作为药物缓释载体的应用[D].汕头:汕头大学,2010.
[6]陈曦,高力,雷静.具有神经生长因子缓释功能的聚羟基脂肪酸酯膜片的制备及其对PC12细胞神经分化的研究[J].海南医学,2017,28(4):530-533.
[7]高天喜,常会敏,范敏杰,等.聚羟基脂肪酸酯的生物修饰及其生物相容性研究[J].中国修复重建外科,2014,28(8):1 023-1 029.
[8]王建清,李飞,金政伟,等.PHA/PLA生物降解共混膜的制备[J].包装工程,2011,32(1):36-39.
[9]李燕立,金玉顺,杨鑫.聚酯纤维的水解动力学研究[J].合成纤维工业,1997(4):15-19.
[10]郭静,童隆埙,徐德增,等.吸水涤纶碱水解及其动力学研究——聚酯-共聚酯纤维[J].合成纤维,1991(2):1-5.
[11]赵涛.染整工艺与原理[M].北京:中国纺织出版社,2005.