海洋环境下混凝土纯聚脲防护研究进展
|
摘要
阐述了海洋环境下混凝土防护的重要性。分析了海洋环境因素对混凝土结构的腐蚀影响,以及纯聚脲用于海洋混凝土防护的性能优势。列举了混凝土聚脲防护的应用实例,表明其防护效果突出。
The importance of concrete protection in marine environment was briefly described.The influence of marine environment on concrete structure corrosion and the performance advantage of concrete pure polyurea protection in marine environment were analyzed.The application examples of concrete pure polyurea protection were listed,which indicated its remarkable protecting effect.
The importance of concrete protection in marine environment was briefly described.The influence of marine environment on concrete structure corrosion and the performance advantage of concrete pure polyurea protection in marine environment were analyzed.The application examples of concrete pure polyurea protection were listed,which indicated its remarkable protecting effect.
引文
1薛焕,金祖权,王晓杰.混凝土在海洋暴露过程中的氯离子渗透研究[J].海洋工程,2015(5):60-65.
2 肖佳,勾成福.混凝土碳化研究综述[J].混凝土,2010(1):40-44,52.
3 Su X P,Guo J H.Study on the Durability of Normal Strength Concrete under the Action of Salt Corrosion and Dry-Wet Cycles[J].Advanced Materials Research,2014(919-921):1 849-1 852.
4 郭范波,蓝强,王海龙.不同海洋环境下玄武岩纤维混凝土力学性能研究[J].台州学院学报,2015(3):43-47.
5 吕建福,李杰,莫照兰,等.海洋潮差区混凝土表面微生物16 Sr DNA分子鉴定[J].哈尔滨工程大学学报,2010(10):1 386-1 392.
6 Arya C,Ofori-Darko F K.Influence of Crack Frequency on Re-inforcement Corrosion in Concrete[J].Cement and Concrete Research,1996,26(3):345.
7 黄泓嘉.海洋环境中氯离子侵蚀作用下混凝土结构耐久性试验研究[D].湖南长沙:长沙理工大学,2013.
8 Silva R V,Silva A,Neves R,et al.Statistical Modeling of Carbonation in Concrete Incorporating Recycled Aggregates[J].Journal of Materials in Civil Engineering,2015,28(1):04015082.
9 杨林,葛海艳,吕平.喷涂聚脲涂层混凝土抗氯离子渗透性能的研究[J].化学建材,2008(2):23-25.
10 黄微波,马红亮,李志高.聚氨酯和聚脲涂层对混凝土氯离子渗透性的影响[J].混凝土,2011(6):94-96.
11 Li W,Jiang Z,Yang Z,et al.Interactive Effect of Mechanical Fatigue Load and the Fatigue Effect of FreezeThaw on Combined Damage of Concrete[J].Journal of Materials in Civil Engineering,2014,27(8).
12 Duan A,Tian Y,Dai J G,et al.A Stochastic Damage Model for Evaluating the Internal Deterioration of Concrete Due to Freeze-Thaw Action[J].Materials and Structures,2014,47(6):1 025-1 039.
13 李志高,马红亮,黄微波.聚脲提高海工和水工混凝土抗冻性研究[J].大坝与安全,2010(5):1-5.
14 庞玉坤,李志高,马红亮.聚脲涂层和环氧涂层对混凝土抗冻性的影响[J].上海涂料,2009,47(9):7-8,24.
15 李福海,赵人达,叶跃忠.冻融环境下混凝土抗侵蚀性能研究[J].工业建筑,2010(6):1-4.
16 王宝柱,刘培礼,胡松霞.喷涂聚脲弹性体在防水工程中的应用[J].新型建筑材料,2009,36(12):59-63.
17 钟萍.聚脲涂层体系及其摩擦学性能研究[D].北京:机械科学研究总院,2009.
18 马红亮.海工混凝土纯聚脲防护涂层性能研究[D].山东青岛:青岛理工大学,2011.
19 黄微波,谢远伟,胡晓,等.海洋腐蚀环境下纯聚脲重防腐涂层耐久性研究[J].上海涂料,2013(4):1-5.
20 李全德,孟惠民.人工加速老化对聚脲涂料防护性能的影响[J].北京科技大学学报,2011(1):71-75.
21 吕平,徐研,黄微波.不同硬段含量聚天冬氨酸酯聚脲涂层耐海洋环境老化性能[J].腐蚀与防护,2008(3):116-118.
22 李国栋.聚脲弹性体的合成及其耐磨性能的改进[D].辽宁大连:大连海事大学,2015.
23 黄微波,向佳瑜,刘旭东,等.应用喷涂纯聚脲技术实现水工混凝土防护[J].混凝土,2011(11):138-140.
24 黄微波,谢远伟,胡晓,等.海洋大气环境下纯聚脲重防腐涂层耐久性研究[J].材料导报,2013,27(6):23-26.
25 张燕,邓智平,刘朝辉,等.聚脲在混凝土防护中的应用[J].表面技术,2013(2):116-118.
26 李海扬.港珠澳大桥混凝土聚脲防护技术应用的研究[D].山东青岛:青岛理工大学,2014.
27 张伶俐,杨金鑫,廖昔虬.喷涂聚脲技术在珠海长隆海洋王国水池防水工程中的应用[J].中国建筑防水,2014(2):22-26.
2 肖佳,勾成福.混凝土碳化研究综述[J].混凝土,2010(1):40-44,52.
3 Su X P,Guo J H.Study on the Durability of Normal Strength Concrete under the Action of Salt Corrosion and Dry-Wet Cycles[J].Advanced Materials Research,2014(919-921):1 849-1 852.
4 郭范波,蓝强,王海龙.不同海洋环境下玄武岩纤维混凝土力学性能研究[J].台州学院学报,2015(3):43-47.
5 吕建福,李杰,莫照兰,等.海洋潮差区混凝土表面微生物16 Sr DNA分子鉴定[J].哈尔滨工程大学学报,2010(10):1 386-1 392.
6 Arya C,Ofori-Darko F K.Influence of Crack Frequency on Re-inforcement Corrosion in Concrete[J].Cement and Concrete Research,1996,26(3):345.
7 黄泓嘉.海洋环境中氯离子侵蚀作用下混凝土结构耐久性试验研究[D].湖南长沙:长沙理工大学,2013.
8 Silva R V,Silva A,Neves R,et al.Statistical Modeling of Carbonation in Concrete Incorporating Recycled Aggregates[J].Journal of Materials in Civil Engineering,2015,28(1):04015082.
9 杨林,葛海艳,吕平.喷涂聚脲涂层混凝土抗氯离子渗透性能的研究[J].化学建材,2008(2):23-25.
10 黄微波,马红亮,李志高.聚氨酯和聚脲涂层对混凝土氯离子渗透性的影响[J].混凝土,2011(6):94-96.
11 Li W,Jiang Z,Yang Z,et al.Interactive Effect of Mechanical Fatigue Load and the Fatigue Effect of FreezeThaw on Combined Damage of Concrete[J].Journal of Materials in Civil Engineering,2014,27(8).
12 Duan A,Tian Y,Dai J G,et al.A Stochastic Damage Model for Evaluating the Internal Deterioration of Concrete Due to Freeze-Thaw Action[J].Materials and Structures,2014,47(6):1 025-1 039.
13 李志高,马红亮,黄微波.聚脲提高海工和水工混凝土抗冻性研究[J].大坝与安全,2010(5):1-5.
14 庞玉坤,李志高,马红亮.聚脲涂层和环氧涂层对混凝土抗冻性的影响[J].上海涂料,2009,47(9):7-8,24.
15 李福海,赵人达,叶跃忠.冻融环境下混凝土抗侵蚀性能研究[J].工业建筑,2010(6):1-4.
16 王宝柱,刘培礼,胡松霞.喷涂聚脲弹性体在防水工程中的应用[J].新型建筑材料,2009,36(12):59-63.
17 钟萍.聚脲涂层体系及其摩擦学性能研究[D].北京:机械科学研究总院,2009.
18 马红亮.海工混凝土纯聚脲防护涂层性能研究[D].山东青岛:青岛理工大学,2011.
19 黄微波,谢远伟,胡晓,等.海洋腐蚀环境下纯聚脲重防腐涂层耐久性研究[J].上海涂料,2013(4):1-5.
20 李全德,孟惠民.人工加速老化对聚脲涂料防护性能的影响[J].北京科技大学学报,2011(1):71-75.
21 吕平,徐研,黄微波.不同硬段含量聚天冬氨酸酯聚脲涂层耐海洋环境老化性能[J].腐蚀与防护,2008(3):116-118.
22 李国栋.聚脲弹性体的合成及其耐磨性能的改进[D].辽宁大连:大连海事大学,2015.
23 黄微波,向佳瑜,刘旭东,等.应用喷涂纯聚脲技术实现水工混凝土防护[J].混凝土,2011(11):138-140.
24 黄微波,谢远伟,胡晓,等.海洋大气环境下纯聚脲重防腐涂层耐久性研究[J].材料导报,2013,27(6):23-26.
25 张燕,邓智平,刘朝辉,等.聚脲在混凝土防护中的应用[J].表面技术,2013(2):116-118.
26 李海扬.港珠澳大桥混凝土聚脲防护技术应用的研究[D].山东青岛:青岛理工大学,2014.
27 张伶俐,杨金鑫,廖昔虬.喷涂聚脲技术在珠海长隆海洋王国水池防水工程中的应用[J].中国建筑防水,2014(2):22-26.