一种硝基三氮杂蒄化合物的合成及性质研究
|
摘要
以氟磺酸为催化剂,通过成环反应合成出蒄中引入氮原子的目标化合物,并对产物进行了结构表征。对该化合物的性质测试表明,其可以作为发光器件分子用于制备电致发光材料。
The target compound with nitrogen atom introduced into coronene was synthesized by cyclic reaction with fluorosulfonic acid as catalyst,and its structure was characterized. The properties of the compound were tested,which showed that the compound could be used as a light-emitting device molecule to prepare the electroluminescent materials.
The target compound with nitrogen atom introduced into coronene was synthesized by cyclic reaction with fluorosulfonic acid as catalyst,and its structure was characterized. The properties of the compound were tested,which showed that the compound could be used as a light-emitting device molecule to prepare the electroluminescent materials.
引文
[1]徐叙瑢.发光材料与显示技术.北京:化学工业出版社,2003.
[2]黄春辉,李富友,黄维.有机电致发光材料与器件导论.上海:复旦大学出版社,2005.
[3]J M Schulman,R L Disch.J.Phys.Chem.A,1997,101:9176~9179.
[4]B K Spraul,S Suresh,S Glaser et al.J.Am.Chem.Soc.,2004,126:12772~12773.
[5]Y Shirota,H Kageyama.Chem.Rev.,2007,107:953~1010.
[6]W W H Wong,D J Jones,C Yan et al.Org.Lett.,2009,11:975~978.
[7]V Palermo,S Morelli,C Simpson et al.J.Mater.Chem.,2006,16:266~271.
[8]J L Wang,J Yan,Z M Tang et al.J.Am.Chem.Soc.,2008,130:9952~9962.
[9]A K Geim.Science,2009,324:1530~1534.
[10]A C Grimsdale,K L Chan,R E Martin et al.Chem.Rev.,2009,109:897~1091.
[11]R Rieger,M Kastler,V Enkelmann et al.Chem.Eur.J.,2008,14:6322~6325.
[12]马妍,赵蔡斌,王文亮等.中国科学:化学,2013,9:1172~1180.
[13]J F Wei,B Han,Q Guo et al.Angew.Chem.Int.Ed.,2010,44:8209~8213.
[14]A M van de Craats,J M Warman,A Fechtenkotter et al.Adv.Mater.,1999,11:1469~1472.
[15]P Calvo-Gredilla,J García-Calvo,J V Cuevas et al.Chem.Eur.J.,2017,23(56):13973~13979.
[16]M Takase,V Enkelmann,D Sebastiani et al.Angew.Chem.,2007,119:5620~5623.
[17]W Jiang,Y Li,W Yue et al.Org.Lett.,2010,12:228~231.
[18]Y Chen,T Marszalek,T Fritz et al.Chem.Commun.,2017,53:8474~8477.
[19]A Narita,X Y Wang,X L Feng et al.Chem.Soc.Rev.,2015,44:6616~6643.
[20]K S Novoselov,A K Geim,S V Morozov et al.Science,2004,306:666~669.
[21]P Calvo-Gredilla,J Garcia-Calvo,J V Cuevas et al.Chem.Eur.J.,2017,23,56:13973~13979.
[22]R Rieger,M Kastler,V Enkelmann et al.Chem.Eur.J.,2008,14:6322~6325.
[2]黄春辉,李富友,黄维.有机电致发光材料与器件导论.上海:复旦大学出版社,2005.
[3]J M Schulman,R L Disch.J.Phys.Chem.A,1997,101:9176~9179.
[4]B K Spraul,S Suresh,S Glaser et al.J.Am.Chem.Soc.,2004,126:12772~12773.
[5]Y Shirota,H Kageyama.Chem.Rev.,2007,107:953~1010.
[6]W W H Wong,D J Jones,C Yan et al.Org.Lett.,2009,11:975~978.
[7]V Palermo,S Morelli,C Simpson et al.J.Mater.Chem.,2006,16:266~271.
[8]J L Wang,J Yan,Z M Tang et al.J.Am.Chem.Soc.,2008,130:9952~9962.
[9]A K Geim.Science,2009,324:1530~1534.
[10]A C Grimsdale,K L Chan,R E Martin et al.Chem.Rev.,2009,109:897~1091.
[11]R Rieger,M Kastler,V Enkelmann et al.Chem.Eur.J.,2008,14:6322~6325.
[12]马妍,赵蔡斌,王文亮等.中国科学:化学,2013,9:1172~1180.
[13]J F Wei,B Han,Q Guo et al.Angew.Chem.Int.Ed.,2010,44:8209~8213.
[14]A M van de Craats,J M Warman,A Fechtenkotter et al.Adv.Mater.,1999,11:1469~1472.
[15]P Calvo-Gredilla,J García-Calvo,J V Cuevas et al.Chem.Eur.J.,2017,23(56):13973~13979.
[16]M Takase,V Enkelmann,D Sebastiani et al.Angew.Chem.,2007,119:5620~5623.
[17]W Jiang,Y Li,W Yue et al.Org.Lett.,2010,12:228~231.
[18]Y Chen,T Marszalek,T Fritz et al.Chem.Commun.,2017,53:8474~8477.
[19]A Narita,X Y Wang,X L Feng et al.Chem.Soc.Rev.,2015,44:6616~6643.
[20]K S Novoselov,A K Geim,S V Morozov et al.Science,2004,306:666~669.
[21]P Calvo-Gredilla,J Garcia-Calvo,J V Cuevas et al.Chem.Eur.J.,2017,23,56:13973~13979.
[22]R Rieger,M Kastler,V Enkelmann et al.Chem.Eur.J.,2008,14:6322~6325.