高温型复合改性沥青灌缝胶正交试验研究
|
摘要
采用正交试验设计,通过极差和方差分析,研究高温型复合改性沥青灌缝胶的组配对其性能的影响规律,结果表明:岩沥青和SBS对高温型灌缝胶性能(尤其是高温性能)的影响较大;不同种类岩沥青改善灌缝胶高温性能的顺序为:青川岩沥青>北美岩沥青>新疆岩沥青>布敦岩沥青。综合分析得出高温型复合改性沥青灌缝胶最优组配(外掺法)为90#沥青∶青川岩沥青∶SBS∶废旧橡胶粉∶自制改性剂X∶相容剂∶自制改性剂Y=100∶6∶9∶20∶6∶25∶1。
引文
[1]孙柯.沥青路面裂缝冷灌缝浆液扩散规律与灌缝技术研究[D].山东大学硕士学位论文,2016.
[2]陈忠达.路基路面工程[M].北京:人民交通出版社,2009.
[3] Fang Huiming,Luo Hui,Zhu Hongping.The Feasibility of Continuous Construction of the Base and Asphalt Layers of Asphalt Pavement to Solve the Problem of Reflective Cracks[J].Construction and Building Materials,2016,119:80-88..
[4] Tu Shuai.Mechanical Property of Pavement with Crack in Base and High Modulus Asphalt Layer[J].Applied Mechanics and Materials,2013,256-259:1 785-1 788.
[5] Crovetti J A,Darter M I,Johnson K D,et al.Innovative Materials and Equipment for Pavement Surface Repairs,VolumeⅡ:Synthesis of Operational Deficiencies of Equipment Used for Pavement Surface Repairs[R].SHRP-M/UFR-91-505,1991.
[6]杨海兵.沥青路面裂缝修补材料研制及性能研究[D].合肥工业大学硕士学位论文,2015.
[7] Bulter William G,Bozkurt Diyar,Dempsey Barry J.Cost-Effectiveness of Paving Fabrics Used to Control Reflective Cracking[R].Transportation Research Record,2000,1 730:139-149.
[8]付强.岩改性沥青在乐宜高速中的应用技术研究[D].重庆交通大学硕士学位论文,2013.
[9]潘若妤,孙晓民,陈彦先,等.SBS/岩沥青复合改性沥青基本性能研究[J].重庆交通大学学报:自然科学版,2009(3).
[10]籍晓靖.基于预拌-增强技术的环保型沥青混合料研发与应用[D].长安大学硕士学位论文,2013.
[11]钟科.岩沥青路用性能研究[D].交通部公路科学研究院硕士学位论文,2006.
[12]汪托,郝培文,常睿.硅藻土/岩沥青复合改性沥青路用性能研究[J].中外公路,2018(1).
[13]游庆龙.废旧轮胎橡胶粉改性沥青SMA混合料性能的研究[D].长安大学硕士学位论文,2008.
[14]苏小雷,付跃松.高性能沥青路面灌缝胶的制作及应用[J].中国公路,2012(20).
[15]张博.钢桥面铺装浇筑式沥青混合料配合比设计研究[D].长安大学硕士学位论文,2012.
[16]王涛,才洪美,张玉贞.SBS改性沥青机理研究[J].石油沥青,2008(6).
[17]杨新春,刘应贵,邓毅,等.青川天然岩沥青对基质沥青性能影响分析[J].西南公路,2016(1).
[2]陈忠达.路基路面工程[M].北京:人民交通出版社,2009.
[3] Fang Huiming,Luo Hui,Zhu Hongping.The Feasibility of Continuous Construction of the Base and Asphalt Layers of Asphalt Pavement to Solve the Problem of Reflective Cracks[J].Construction and Building Materials,2016,119:80-88..
[4] Tu Shuai.Mechanical Property of Pavement with Crack in Base and High Modulus Asphalt Layer[J].Applied Mechanics and Materials,2013,256-259:1 785-1 788.
[5] Crovetti J A,Darter M I,Johnson K D,et al.Innovative Materials and Equipment for Pavement Surface Repairs,VolumeⅡ:Synthesis of Operational Deficiencies of Equipment Used for Pavement Surface Repairs[R].SHRP-M/UFR-91-505,1991.
[6]杨海兵.沥青路面裂缝修补材料研制及性能研究[D].合肥工业大学硕士学位论文,2015.
[7] Bulter William G,Bozkurt Diyar,Dempsey Barry J.Cost-Effectiveness of Paving Fabrics Used to Control Reflective Cracking[R].Transportation Research Record,2000,1 730:139-149.
[8]付强.岩改性沥青在乐宜高速中的应用技术研究[D].重庆交通大学硕士学位论文,2013.
[9]潘若妤,孙晓民,陈彦先,等.SBS/岩沥青复合改性沥青基本性能研究[J].重庆交通大学学报:自然科学版,2009(3).
[10]籍晓靖.基于预拌-增强技术的环保型沥青混合料研发与应用[D].长安大学硕士学位论文,2013.
[11]钟科.岩沥青路用性能研究[D].交通部公路科学研究院硕士学位论文,2006.
[12]汪托,郝培文,常睿.硅藻土/岩沥青复合改性沥青路用性能研究[J].中外公路,2018(1).
[13]游庆龙.废旧轮胎橡胶粉改性沥青SMA混合料性能的研究[D].长安大学硕士学位论文,2008.
[14]苏小雷,付跃松.高性能沥青路面灌缝胶的制作及应用[J].中国公路,2012(20).
[15]张博.钢桥面铺装浇筑式沥青混合料配合比设计研究[D].长安大学硕士学位论文,2012.
[16]王涛,才洪美,张玉贞.SBS改性沥青机理研究[J].石油沥青,2008(6).
[17]杨新春,刘应贵,邓毅,等.青川天然岩沥青对基质沥青性能影响分析[J].西南公路,2016(1).