系统地评述了不同方法改性聚苯乙烯(PS)的机械性能与耐热性,包括(未官能化、官能化)无机填料直接填充或在聚合过程中原位填充改性;(未改性、改性)聚合物直接共混或在聚合过程中原位共混改性;离子交联、互穿聚合物交联网络、共价交联改性;从单体出发采用无规、接枝或嵌段共聚改性;以及同时使用两种方法的耦合改性(如共混-填充、共聚-共混、共聚-填充、离子交联-共混、离子交联-填充)等。在此基础上,对各种改性方法的优缺点进行了比较与讨论。
In this article,different methods to modify mechanical properties and heat resistance of polystyrene(PS)have systematically been reviewed.These include filling the PS directly or in situ during its polymerization with inorganic fillers,unfunctionalized or functionalized,blending the PS directly or in situ during its polymerization with polymers,unmodified or modified,cross-linkings(ionic cross-linking,interpenetrating polymer network,covalent cross-linking,etc.),random,graft or block copolymerization starting from monomers,two method coupled modifications(e.g.,blending-filling,copolymerization-blending,copolymerization-filling,ionic crosslinking-blending,and ionic crosslinkingfilling),etc.Based on the above,the advantages and disadvantages have been compared and discussed of various modification methods.
引文
[1]Gao Y,Liu L,Zhang Z.Acta Mech Solida Sin,2009,22(6):555~562.
[2]贾志永,强颖怀,王沛培.硅酸盐通报,2008,27(1):174~178.
[3]Zhou K,Yang W,Tang G,Wang B,Jiang S,Hu Y,Gui Z.RSC Adv,2013,3(47):25030~25040.
[4]Sun G,Chen G,Liu Z,Chen M.Carbon,2010,48(5):1434~1440.
[5]Bera O,Pilic'B,Pavlicˇevic'J,Jovicˇic'M,HollóB,Mészáros Szécsényi K,pirkova M.Thermochim Acta,2011,515(1):1~5.
[6]Qiu S,Hu W,Yu B,Yuan B,Zhu Y,Jiang S,Wang B,Song L,Hu Y.Ind Eng Chem Res,2015,54(13):3309~3319.
[7]Goyal R K,Jagadale P A,Mulik U P.J Appl Polym Sci,2009,111(4):2071~2077.
[8]Kausar A,Ullah W,Muhammad B,Siddiq M.Adv Mater Sci,2014,14(4):61~74.
[9]周一帆,王明明.绝缘材料,2010,43(1):28~33.
[10]Gu J,Zhang Q,Dang J,Yin C,Chen S.J Appl Polym Sci,2012,124(1):132~137.
[11]徐志峰,张坚,郑海忠,黄因慧.高分子材料科学与工程,2005,21(3):223~226.
[12]Ma C C M,Chen Y J,Kuan H C.J Appl Polym Sci,2006,100(1):508~515.
[13]Wu G,Wang Y,Wang K,Feng A.Rsc Adv,2016,6(104):102542~102548.
[14]Xing W,Yang W,Yang W,Hu Q,Si J,Lu H,Yang B,Song L,Hu Y,Yuen R K K,ACS Appl Mater Interfaces,2016,8(39):26266~26274.
[15]Zhou K,Wang B,Liu J,Jiang S,Shi Y,Zhang Q,Hu Y,Gui Z.Mater Res Bull,2014,53:272~279.
[16]Zhou K,Jiang S,Shi Y,Liu J,Wang B,Hu Y,Gui Z.RSC Adv,2014,4(76):40170~40180.
[17]Kundu D,Hazra C,Chatterjee A,Chaudhari A,Mishra S.Polym Degrad Stab,2014,107:37~52.
[18]Pereira P,Gaspar H,Fernandes L,Bernardo G.Polym Test,2015,47:130~136.
[19]Espejo C,Carrión-Vilches F J,Bermúdez M D.Polym Degrad Stab,2014,103:42~48.
[20]Xiao P,Xiao M,Gong K.Polymer,2001,42(11):4813~4816.
[21]熊传溪,闻获江,皮正杰.高分子材料科学与工程,1994,7(4):69~72.
[22]刘才林,李俊江,任先艳,杨海君,李福阳,雍辉.强激光与粒子束,2012,24(2):349~352.
[23]Lee J,Hong C K,Choe S,Shim S E.J Colloid Interf Sci,2007,310(1):112~120.
[24]林美娟,章文贡,王文.中国稀土学报,2001,20(2):107~110.
[25]王文,林美娟,章文贡.中国塑料,2003,17(3):68~71.
[26]Okamoto M,Morita S,Taguchi H,Kim Y H,Kotaka T,Tateyama H.Polymer,2000,41(10):3887~3890.
[27]门艳茹,杨贤金,朱胜利,崔振铎,桑晓明,盛京.功能材料,2005,12(36):1927~1930.
[28]Li X,Liu S,Zhao J,Otsuka H,Takahara A.J Wuhan Univ Technol,Mater Sci Ed,2010,25(2):184~187.
[29]Blanco I,Abate L,Bottino F A,Bottino P.Polym Degrad Stabil,2014,102(1):132~137.
[30]Hatui G,Bhattacharya P,Sahoo S,Dhibar S,Das C K.Compos Part A:Appl Sci Manufact,2014,56:181~191.
[31]Roghani-Mamaqani H,Haddadi-Asl V,Khezri K,Salami-Kalajahi M.RSC Adv,2014,4(47):24439~24452.
[32]Yu Y H,Lin Y Y,Lin C H,Chan C C,Huang Y C.Polym Chem,2014,5(2):535~550.
[33]Zheng Z,Li W,Sun H,Cheng Z,Yan J,Wang H,Cui X.Polym Compos,2013,34(7):1110~1118.
[34]Yang H,Zhang L,Ma W,Pu H,Gong F.J Appl Polym Sci,2015,132(9):41567~41575.
[35]Greesh N,Sinha Ray S,Bandyopadhyay J.Ind Eng Chem Res,2013,52(46):16220~16231.
[36]Fu X,Qutubuddin S.Polymer,2001,42(2):807~813.
[37]Botan R,Nogueira Caio T R,Ferrareso Lona L M.J Appl Polym Sci,2016,133(1):1~10
[38]Suresh K,Kumar M,Pugazhenthi G,Uppaluri R.J Sci:Adv Mater Devices,2017,2(2):245~254.
[39]陈燕丹,陈娟娟,章文贡.福建师范大学学报,2000,16(3):60~64.
[40]Tang Z,Lu D,Guo J,Su Z.Mater Lett,2008,62(26):4223~4225.
[41]侯桂香,姚少巍,桑晓明,唐鹏,蒋丽.中国塑料,2012,26(3):88~91.
[42]唐卫华,唐键,金日光.塑料工业,2002,30(1):15~17.
[43]Kim H R,Kim J K,Park J Y.Korea-Aust Rheol J,2001,13(2):83~87.
[44]赵海南,苗一,边重阳.当代化工,2015,44(3):555~557.
[45]高光辉,赵文卓,赵云娜,张会轩.复合材料学报,2007,24(2):33~37.
[46]夏新江,王炼石,顾为民,周奕雨,贾德民.中国塑料,1998,12(4):45~51.
[47]Neoh S B,Hashim A S.J Appl Polym Sci,2004,93(4):1660~1665.
[48]付锦锋,麦剑章,王炼石,蔡彤旻,张安强,曾祥斌,王霞.塑料工业,2010,38(12):21~25.
[49]马斐,陈洁,王颖,阚永乐,柯昌美,曾丹林,陈红祥.武汉科技大学学报,2010,33(5):553~556.
[50]邱大健,邹从炎,赵斌.应用化学,1995,12(1):34~37.
[51]谢文炳,王玮,茅芸,王晨,夏燕敏.石油化工,1998,(03):24~30.
[52]Tjong S C,Xu S A.J Appl Polym Sci,1998,68(7):1099~1108.
[53]Chen G,Liu J.J Mater Sci,1999,34(18):4375~4383.
[54]Villarreal M E,Tapia M,Nu1o-Donlucas S M,Puig J E,González-Nú1ez R.J Appl Polym Sci,2004,92(4):2545~2551.
[55]汤钧,刘凤歧,金美花,杨柏.高等学校化学学报,2000,21(12):1925~1927.
[56]Moscoso F J,Martínez L,Canche G,Rodrigue D,González-Nú1ez R.J Appl Polym Sci,2013,127(1):599~606.
[57]Poletto M,Poletto M.Matéria,2016,21(3):552~559.
[58]Nair K C M,Thomas S,Groeninckx G.Compos Sci Technol,2001,61(16):2519~2529.
[59]Fujisawa S,Ikeuchi T,Takeuchi M,Saito T,Isogai A.Biomacromolecules,2012,13(7):2188~2194.
[60]Poletto M,Zattera A J.J Thermoplast Compos,2015,14(4):185~189.
[61]常丽,胡雁鸣,李杨,史正海,吕权,王玉荣.石油化工,2011,40(08):850~855.
[62]Lourenco E,Goncalves M C,Felisberti M I.J Appl Polym Sci,2009,112(4):2280~2289.
[63]Eisenberg A,Hird B,Moore R B.Macromolecules,1990,23(18):4098~4107.
[64]Weiss R A,Fitzgerald J J,Kim D.Macromolecules,1991,24(5):1071~1076.
[65]Zhou N C,Burghardt W R,Winey K I.Macromolecules,2007,40(17):6401~6405.
[66]Weiss R A,Sen A,Willis C L,Pottick L A.Polymer,1991,32(10):1867~1874.
[67]Weiss R A,Sen A,Pottick L A,Willis C L.Polymer,1991,32(15):2785~2792.
[68]Qiao X,Weiss R A.Macromolecules,2013,46(6):2417~2424.
[69]Song J M,Ko K H,Kim J S,Shin K.J Polym Sci Part B:Polym Phys,2012,50(16):1181~1187.
[70]Navratil M,Eisenberg A.Macromolecules,1974,7(1):84~89.
[71]Ko K H,Luqman M,Kim Y W,Kim J S.J Polym Sci Part B:Polym Phys,2016,54(11):1043~1053.
[72]Bellinger M A,Sauer J A,Hara M.Macromolecules,1994,27(21):6147~6155.
[73]Iwakura K,Fujimura T.J Appl Polym Sci,1975,19(5):1427~1437.
[74]Mathew A P,Packirisamy S,Thomas S.Polym Degrad Stabil,2001,72(3):423~439.
[75]Dave V J,Patel H S.J Saudi Chem Soc,2013,21(1):18~24.
[76]李燕鸿,范云鸽,马建标.全国高分子学术论文报告会.2001.
[77]王久芬,周海骏,姜丽萍,冷国平.高分子材料科学与工程,2003,19(4):60~63.
[78]廖正福,李达凡,罗朝明.弹性体,2004,14(6):19~21.
[79]王俏,魏清波,刘勇.化学与黏合,2011,33(5):71~73.
[80]王国祥,刘永兵.高校化学工程学报,2014,28(2):365~369.
[81]高惠敏,吴梓新,陆懿,吕珏,揭元萍.化学试剂,2011,33(7):643~644.
[82]董建华,陈倩.高分子材料科学与工程,1999,15(3):75~77.
[83]Umar A,Naim A A,Sanagi M M.Mater Lett,2014,124:12~14.
[84]Ohta Y,Shirakura T,Yokoyama A,Yokozawa T.J Polym Sci Part A:Polym Chem,2013,51(8):1887~1892.
[85]戴璐,周勤灼,李伯耿,介素云.高分子学报,2017,(12):1930~1938.
[86]王继铭,单东,刘伟兴,郑安呐.高分子材料科学与工程,2015,31(10):99~104.
[87]李谷,麦堪成,王玉海,冯开才.高分子材料科学与工程,2006,22(2):227~230.
[88]袁绍彦,吕军,罗勇,黄锐.复合材料学报,2005,22(3):25~29.
[89]李耀波,李秀兰,王益波,魏丽娟,周明海,初小丽.中国塑料,2014,28(01):38~42.
[90]从日新,梁滔,郑红兵,吴宇,李炳泉,方伟,魏绪玲,胡才仲.工程塑料应用,2010,38(1):6~9.
[91]Hasegawa N,Okamoto H,Kawasumi M,Usaki A.J Appl Polym Sci,1999,74(14):3359~3364.
[92]Molnar A,Eisenberg A.Macromolecules,1992,25(21):5774~5782.
[93]Lu X,Weiss R A.Macromolecules,1992,25(23):6185~6189.
[94]He J,Liu J.Polymer,1999,40(4):959~969.
[95]Govindaiah P,Mallikarjuna S R,Ramesh C.Macromolecules,2006,39(21):7199~7203.