海洋浪溅区钢结构的腐蚀与防护研究进展
|
摘要
海洋浪溅区腐蚀环境苛刻,对海洋钢结构的腐蚀相当严重。介绍了海洋浪溅区的范围,以及钢铁在浪溅区的腐蚀行为和机理。着重从重防腐涂料保护、阴极保护、金属热喷涂保护、热浸镀层腐蚀防护以及包覆层保护等多个方面介绍了目前国内外常用的浪溅区腐蚀防护技术。
The marine splash zone is severely corrosive area in the marine environment,and the corrosion damage of steel structures is rather serious.The range of splash zone,the corrosion behavior and mechanism of steel structures in this area were introduced.The common protection methods including heavy-duty anticorrosive coatings,cathodic protection,metal thermal spraying protection,corrosion protection of hot dip coating and cover protection at home and abroad were introduced in detail.
The marine splash zone is severely corrosive area in the marine environment,and the corrosion damage of steel structures is rather serious.The range of splash zone,the corrosion behavior and mechanism of steel structures in this area were introduced.The common protection methods including heavy-duty anticorrosive coatings,cathodic protection,metal thermal spraying protection,corrosion protection of hot dip coating and cover protection at home and abroad were introduced in detail.
引文
1刘建国.海洋浪花飞溅区钢铁腐蚀过程和修复技术研究[D].北京:中国科学院研究生院,2010.
2 Zhu X R,Huang G Q,Liang C F.Study on the Corrosion Peak of Carbon Steel in Marine Splash Zone[J].Chinese Journal of Oceanology and Limnology,1997(4):378-380.
3 刘薇,王佳.海洋浪溅区环境对材料腐蚀行为影响的研究进展[J].中国腐蚀与防护学报,2010(6):504-512.
4 卢振永.氯盐腐蚀环境的人工模拟试验方法[D].浙江杭州:浙江大学,2007.
5 Bing R,Wang Y X.Experimental Study of Irregular Wave Impact on Structures in the Splash Zone[J].Ocean Eng.,2003,30(18):2 363.
6 Ren B,Wang Y X.Numerical Simulation of Random Wave Slamming on Structures in the Splash Zone[J].Ocean Eng.,2004,31(5-6):547-560.
7 Pohjanne P,Carpen L,Hakkarainen T,et al.A Method to Predict Pitting Corrosion of Stainless Steels in Evaporative Conditions[J].J.Constr.Steel Res.,2008,64(11):1 325-1 331.
8 侯保荣.海洋钢结构浪花飞溅区腐蚀控制技术[M].北京:科学出版社,2011:217.
9 朱相荣,王相润,黄桂桥.钢在海洋飞溅带的腐蚀与防护[J].海洋科学,1995(3):23-26.
10 魏向阳.新一代水性无机富锌涂料[J].涂料工业,2007(5):40-43.
11 李敏,王秀娟,刘宝成,等.海洋环境防腐蚀玻璃鳞片涂料的研制[J].涂料工业,2010(1):49-53.
12 黄微波,谢远伟,胡晓,等.海洋腐蚀环境下纯聚脲重防腐涂层耐久性研究[J].上海涂料,2013,51(4):1-5.
13 李鑫茂.聚脲防护涂层耐候老化及耐介质腐蚀性能研究[D].山东青岛:青岛理工大学,2011.
14 Shiwei William Guan,Nick Gritis,Adam Jackson,et al.先进的陆地和海底管道涂敷技术[J].油气储运,2005,24(增刊):110-114.
15 陈君.低碳钢浪花飞溅区腐蚀和防腐带保护技术研究[D].北京:中国科学院研究生院,2012.
16 黄彦良.一种浪花飞溅区钢铁设施腐蚀防护方法:中国,CN1477232[P].2004-02-25.
17 范卫国,李森林,韩秀兰.杭州湾某化工泊位改造工程钢管桩牺牲阳极阴极保护[A].第十二届中国海岸工程学术讨论会论文集[C].江苏南京:中国海洋工程学会,2005:771-773.
18 彭立涛.电弧喷涂锌、铝涂层防腐机理研究[D].黑龙江大庆:大庆石油学院,2010.
19 王真.铝合金电弧喷涂纯铝涂层及封孔方法研究[D].辽宁大连:大连理工大学,2009.
20 周学杰,张三平,付志勇,等.金属喷涂层在海水中的腐蚀研究[J].腐蚀科学与防护技术,2004,16(4):236-239.
21 李焰,邢少华,李鑫,等.热浸镀层在青岛站的海水腐蚀行为对比(III)——飞溅区[J].中国有色金属学报,2007,17(9):1 527-1 535.
22 Koji Tachibana,Yasufumi Moriniga,Masami Mayuzumi.Hot Dip Fine Zn and Zn-Al Alloy Double Coating for Corrosion Resistance at Coastal Area[J].Corrosion Science,2007(49):149-157.
23 侯保荣.钢铁设施在海洋浪花飞溅区的腐蚀行为及其新型包覆防护技术[J].腐蚀与防护,2007(4):174-175.
24 钱备.钢结构浪溅区腐蚀防护技术及缓蚀剂在干湿交替下的研究[D].北京:中国科学院研究生院,2014.
25 张坚彬,杨小刚.复层矿脂包覆技术在滨海电厂钢结构关键部位的防护应用[J].腐蚀与防护,2011(11):896-899.
26 陈君,黄彦良,侯保荣.低碳钢在浪花飞溅区的腐蚀防护研究进展[J].腐蚀科学与防护技术,2012(4):342-344.
2 Zhu X R,Huang G Q,Liang C F.Study on the Corrosion Peak of Carbon Steel in Marine Splash Zone[J].Chinese Journal of Oceanology and Limnology,1997(4):378-380.
3 刘薇,王佳.海洋浪溅区环境对材料腐蚀行为影响的研究进展[J].中国腐蚀与防护学报,2010(6):504-512.
4 卢振永.氯盐腐蚀环境的人工模拟试验方法[D].浙江杭州:浙江大学,2007.
5 Bing R,Wang Y X.Experimental Study of Irregular Wave Impact on Structures in the Splash Zone[J].Ocean Eng.,2003,30(18):2 363.
6 Ren B,Wang Y X.Numerical Simulation of Random Wave Slamming on Structures in the Splash Zone[J].Ocean Eng.,2004,31(5-6):547-560.
7 Pohjanne P,Carpen L,Hakkarainen T,et al.A Method to Predict Pitting Corrosion of Stainless Steels in Evaporative Conditions[J].J.Constr.Steel Res.,2008,64(11):1 325-1 331.
8 侯保荣.海洋钢结构浪花飞溅区腐蚀控制技术[M].北京:科学出版社,2011:217.
9 朱相荣,王相润,黄桂桥.钢在海洋飞溅带的腐蚀与防护[J].海洋科学,1995(3):23-26.
10 魏向阳.新一代水性无机富锌涂料[J].涂料工业,2007(5):40-43.
11 李敏,王秀娟,刘宝成,等.海洋环境防腐蚀玻璃鳞片涂料的研制[J].涂料工业,2010(1):49-53.
12 黄微波,谢远伟,胡晓,等.海洋腐蚀环境下纯聚脲重防腐涂层耐久性研究[J].上海涂料,2013,51(4):1-5.
13 李鑫茂.聚脲防护涂层耐候老化及耐介质腐蚀性能研究[D].山东青岛:青岛理工大学,2011.
14 Shiwei William Guan,Nick Gritis,Adam Jackson,et al.先进的陆地和海底管道涂敷技术[J].油气储运,2005,24(增刊):110-114.
15 陈君.低碳钢浪花飞溅区腐蚀和防腐带保护技术研究[D].北京:中国科学院研究生院,2012.
16 黄彦良.一种浪花飞溅区钢铁设施腐蚀防护方法:中国,CN1477232[P].2004-02-25.
17 范卫国,李森林,韩秀兰.杭州湾某化工泊位改造工程钢管桩牺牲阳极阴极保护[A].第十二届中国海岸工程学术讨论会论文集[C].江苏南京:中国海洋工程学会,2005:771-773.
18 彭立涛.电弧喷涂锌、铝涂层防腐机理研究[D].黑龙江大庆:大庆石油学院,2010.
19 王真.铝合金电弧喷涂纯铝涂层及封孔方法研究[D].辽宁大连:大连理工大学,2009.
20 周学杰,张三平,付志勇,等.金属喷涂层在海水中的腐蚀研究[J].腐蚀科学与防护技术,2004,16(4):236-239.
21 李焰,邢少华,李鑫,等.热浸镀层在青岛站的海水腐蚀行为对比(III)——飞溅区[J].中国有色金属学报,2007,17(9):1 527-1 535.
22 Koji Tachibana,Yasufumi Moriniga,Masami Mayuzumi.Hot Dip Fine Zn and Zn-Al Alloy Double Coating for Corrosion Resistance at Coastal Area[J].Corrosion Science,2007(49):149-157.
23 侯保荣.钢铁设施在海洋浪花飞溅区的腐蚀行为及其新型包覆防护技术[J].腐蚀与防护,2007(4):174-175.
24 钱备.钢结构浪溅区腐蚀防护技术及缓蚀剂在干湿交替下的研究[D].北京:中国科学院研究生院,2014.
25 张坚彬,杨小刚.复层矿脂包覆技术在滨海电厂钢结构关键部位的防护应用[J].腐蚀与防护,2011(11):896-899.
26 陈君,黄彦良,侯保荣.低碳钢在浪花飞溅区的腐蚀防护研究进展[J].腐蚀科学与防护技术,2012(4):342-344.