国内聚丁二酸丁二醇酯改性研究进展
|
摘要
从聚丁二酸丁二醇酯(PBS)共聚、共混、PBS/聚乳酸(PLA)复合体系、生物降解和PBS纤维研究等方面对国内PBS改性研究进行了述评,同时认为PBS有良好的发展应用前景。
The modification of polybutylene succinate(PBS)in China was reviewed from copolymerization,blending,PBS/PLA composite system,biodegradation and PBS fiber.It was considered that PBS had good development and application prospect.
The modification of polybutylene succinate(PBS)in China was reviewed from copolymerization,blending,PBS/PLA composite system,biodegradation and PBS fiber.It was considered that PBS had good development and application prospect.
引文
[1] YANG J,HAO Q,LIU X,et al.Novel biodegradable aliphatic poly(butylene succinate-co-cyclic carbonate)s with functionalizable carbonate building blocks.1.chemical synthesis and their structural and physical characterization[J].Biomacromolecules,2004,5(1):209-218.
[2] ISHII M,OKAZAKI M,SHIBASAKI Y,et al.Convenient synthesis of aliphatic polyesters by distannoxane-catalyzed polycondensation[J].Biomacromolecules,2001,2(4):1 267-1 270.
[3] LINDSTROM A,AIBERTSSON A C,HAKKARAINEN M.Quantitative determination of degradation products an effective means to study early stages of degradation in linear and branched poly(butylene adipate)and poly(butylene succinate)[J].Polymer Degradation&Stability,2004,83(3):487-493.
[4]许国志,高利斌,杨彪.全生物降解PBS的扩链改性研究[J].现代塑料加工应用,2007,19(1):22-25.
[5]丁晨.纤维增强聚丁二酸丁二醇酯复合材料的制备及性能研究[D].大连:大连理工大学,2014.
[6]杨金明,王波,田小燕,等.聚丁二酸丁二酯的研究进展[J].工程塑料应用,2015,(2):117-120.
[7]张敏,马晓宁,李成涛,等.PBS基共聚酯P(BS-coPeD)和P(BS-co-GA)的降解差异性研究[J].陕西科技大学学报,2018,(2):63-67.
[8]张敏,赵冬,李成涛,等.不同主链PBS基共聚酯的酶催化降解及分子模拟[J].塑料,2018,(1):13-17.
[9]段荣涛,董雪,李德福,等.含异山梨醇的全生物基PBS嵌段共聚酯的制备及性能[J].高分子学报,2016,(1):70-77.
[10]周晓明,武通浩,陈媛.聚乙二醇-聚丁二酸丁二醇酯-聚乙二醇嵌段共聚物的合成与表征[J].高分子材料科学与工程,2018,(1):6-11.
[11]张燕,杨杨,王建,等.硅醇和芳香酯共聚改性PBS材料的制备与性能研究[J].中国塑料,2017,(11):27-34.
[12]田琴,秦舒浩,杨明,等.EAA对PBS/OMMT复合材料结构和性能的影响[J].工程塑料应用,2017,45(9):13-17.
[13]杨昕,白海清,贾仕奎,等.超声辅助真空作用下石墨烯/PBS复合材料的制备及热性能[J].塑料工业,2016,44(8):29-33.
[14]孙炳新,韩春阳,张佰清,等.聚丁二酸丁二醇酯滑石粉填充改性研究[J].包装工程,2018,39(5):105-109.
[15]罗刘闯,杨会歌,范国超,等.PBS/氧化石墨烯复合薄膜的制备与性能[J].包装工程,2017,38(13):55-59.
[16]郭子豪.PBS/水曲柳木屑木塑复合材料制备和吸水性的研究[J].功能材料,2018,49(3):3 187-3 190.
[17]付瑶,李壮,曹国喜.PBS/竹粉复合材料的力学性能研究[J].化工新型材料,2016,(4):134-136.
[18]陈杰.木薯渣/PBS可生物降解复合材料的制备与性能研究[D].南宁:广西大学,2018.
[19]岳小鹏,刘鹏杰,雷丹.酯化淀粉改性木薯渣纤维/PBS复合材料性能研究[J].林产化学与工业,2017,37(5):119-125.
[20]潘庆功,刘丰田.PF/PBS/PLA可降解复合材料性能研究[J].山东理工大学学报(自然科学版),2017,31(6):63-66.
[21]葛正浩,魏悦涵,司丹鸽,等.PLA/PBS/秸秆粉可生物降解木塑复合材料制备及性能[J].塑料,2017,(3):18-22.
[22]夏胜娟,杨丹,马博谋,等.棉秆皮纤维增强聚丁二酸丁二醇酯复合材料的制备及降解性能研究[J].化工新型材料,2018,(3):147-151.
[23]迟丽萍,张婷婷,谭洪生.椰壳纤维/PBS可降解复合材料的研究[J].上海化工,2017,42(5):20-25.
[24]殷悦,曹有名.有机酸酸化淀粉用于聚丁二酸丁二醇酯/热塑性淀粉共混物的研究[J].广东化工,2017,44(11):25-26.
[25]宋洁,张敏,许小玲,等.植物虎杖及其提取物改性PBS的性能对比研究[J].工程塑料应用,2016,44(4):7-10.
[26]宋洁,延小雨,张敏,等.PBS/天然虎杖提取物复合材料的界面作用及其性能[J].工程塑料应用,2016,44(8):13-17.
[27]张诗嘉,张倩楠,夏依拉·开依赛尔,等.PBS/望江南提取物抗菌高分子材料的性能研究[J].中国塑料,2018,(1):27-33.
[28]宋洁,延小雨,王婷婷,等.五倍子/PBS复合材料的性能研究[J].陕西科技大学学报,2016,34(4):65-70.
[29]酒巧娜,卢玉献.PBS对两种新型聚乳酸复合材料性能的影响[J].山东化工,2018,47(18):22-23.
[30]田伟,于文海,罗鲲,等.PBS增韧改性MWNTs/PLA导电3D打印耗材的制备及性能[J].材料导报,2018,(31):274-277.
[31]苏桂仙,王佳伟,李佳,等.PLA/PBS/Nano-SiO2制备及性能研究[J].唐山师范学院学报,2017,39(5):9-12.
[32]张力,赵宇培,金叶玲,等.PLA-g-MAH的制备及其对PLA/PBS复合材料性能影响[J].现代塑料加工应用,2017,29(2):29-32.
[33]赵芸芳.吹膜级PBS/PLA复合材料的制备与性能研究[J].工程塑料应用,2016,44(1):41-44.
[34]辜婷,朱大勇,郑强,等.多巴胺改性滑石粉对聚乳酸/聚丁二酸丁二醇酯共混体系结晶行为及流变性能的影响[J].高分子材料科学与工程,2017,33(9):65-71.
[35]朱大勇,辜婷,于杰,等.环氧呋喃树脂反应性增容PLA/PBS共混体系的动态流变学表征[J].材料研究学报,2018,32(7):547-554.
[36]赵聪,司鹏翔,杨昆,等.聚多巴胺改性纳米二氧化硅对PLA/PBS共混复合材料性能的影响[J].塑料工业,2016,44(2):122-125.
[37]张也,张会良,李义,等.可完全生物降解PLA/PPA/PBS薄膜的制备与性能研究[J].塑料科技,2018,(3):78-83.
[38]徐文华,杨智韬,殷小春,等.拉伸形变作用下PLA/PBS增韧共混物力学性能研究[J].中国塑料,2016,30(1):34-38.
[39]唐海龙,陈惠灼,徐文华,等.体积拉伸形变对PLA/PBS共混物结构与性能的影响[J].塑料工业,2016,44(7):43-46.
[40]朱大勇,辜婷,郑强,等.亚磷酸三苯酯对聚乳酸/聚丁二酸丁二醇酯共混体系性能的影响[J].高分子材料科学与工程,2018,(4):43-47.
[41]贾仕奎,王忠,朱艳,等.原位增强PLA/PBS合金的微观形态及力学性能研究[J].塑料工业,2016,44(9):32-36.
[42]胡雪岩,毛海龙,苏婷婷,等.聚丁二酸丁二醇酯(PBS)生物降解的研究进展[J].微生物学杂志,2016,36(4):84-89.
[43]孙炳新,韩春阳,罗思,等.P(3HB-co-4HB)/PBS共混材料酶解性能研究[J].包装工程,2016,37(21):76-80.
[44]胡洁,李东风,臧红霞,等.PBS降解塑料降解性能的研究[J].化工新型材料,2016,(3):175-177.
[45]吴红艳,陈振宏,吕悦慈.静电纺PBS/熔喷复合滤材的制备及性能表征[J].纺织导报,2017,(9):70-73.
[46]阳知乾,刘建忠,吕进,等.POM/PBS共混纤维的结构与性能研究[J].合成纤维工业,2017,40(6):17-21.
[47]顾晶君.生物降解性聚酯聚丁二酸丁二醇酯(PBS)和聚对苯二甲酸-共-丁二酸丁二醇酯(PBST)的性能研究和纤维制备[D].上海:东华大学,2007.
[48]周邓飞.可生物降解PBS的合成及纤维制备[D].杭州:浙江理工大学,2016.
[49]常军,叶芳,李刚,等.含5-FU聚丁二酸丁二酯共聚物的合成及释药性研究[J].广州化工,2016,44(17):64-65.
[2] ISHII M,OKAZAKI M,SHIBASAKI Y,et al.Convenient synthesis of aliphatic polyesters by distannoxane-catalyzed polycondensation[J].Biomacromolecules,2001,2(4):1 267-1 270.
[3] LINDSTROM A,AIBERTSSON A C,HAKKARAINEN M.Quantitative determination of degradation products an effective means to study early stages of degradation in linear and branched poly(butylene adipate)and poly(butylene succinate)[J].Polymer Degradation&Stability,2004,83(3):487-493.
[4]许国志,高利斌,杨彪.全生物降解PBS的扩链改性研究[J].现代塑料加工应用,2007,19(1):22-25.
[5]丁晨.纤维增强聚丁二酸丁二醇酯复合材料的制备及性能研究[D].大连:大连理工大学,2014.
[6]杨金明,王波,田小燕,等.聚丁二酸丁二酯的研究进展[J].工程塑料应用,2015,(2):117-120.
[7]张敏,马晓宁,李成涛,等.PBS基共聚酯P(BS-coPeD)和P(BS-co-GA)的降解差异性研究[J].陕西科技大学学报,2018,(2):63-67.
[8]张敏,赵冬,李成涛,等.不同主链PBS基共聚酯的酶催化降解及分子模拟[J].塑料,2018,(1):13-17.
[9]段荣涛,董雪,李德福,等.含异山梨醇的全生物基PBS嵌段共聚酯的制备及性能[J].高分子学报,2016,(1):70-77.
[10]周晓明,武通浩,陈媛.聚乙二醇-聚丁二酸丁二醇酯-聚乙二醇嵌段共聚物的合成与表征[J].高分子材料科学与工程,2018,(1):6-11.
[11]张燕,杨杨,王建,等.硅醇和芳香酯共聚改性PBS材料的制备与性能研究[J].中国塑料,2017,(11):27-34.
[12]田琴,秦舒浩,杨明,等.EAA对PBS/OMMT复合材料结构和性能的影响[J].工程塑料应用,2017,45(9):13-17.
[13]杨昕,白海清,贾仕奎,等.超声辅助真空作用下石墨烯/PBS复合材料的制备及热性能[J].塑料工业,2016,44(8):29-33.
[14]孙炳新,韩春阳,张佰清,等.聚丁二酸丁二醇酯滑石粉填充改性研究[J].包装工程,2018,39(5):105-109.
[15]罗刘闯,杨会歌,范国超,等.PBS/氧化石墨烯复合薄膜的制备与性能[J].包装工程,2017,38(13):55-59.
[16]郭子豪.PBS/水曲柳木屑木塑复合材料制备和吸水性的研究[J].功能材料,2018,49(3):3 187-3 190.
[17]付瑶,李壮,曹国喜.PBS/竹粉复合材料的力学性能研究[J].化工新型材料,2016,(4):134-136.
[18]陈杰.木薯渣/PBS可生物降解复合材料的制备与性能研究[D].南宁:广西大学,2018.
[19]岳小鹏,刘鹏杰,雷丹.酯化淀粉改性木薯渣纤维/PBS复合材料性能研究[J].林产化学与工业,2017,37(5):119-125.
[20]潘庆功,刘丰田.PF/PBS/PLA可降解复合材料性能研究[J].山东理工大学学报(自然科学版),2017,31(6):63-66.
[21]葛正浩,魏悦涵,司丹鸽,等.PLA/PBS/秸秆粉可生物降解木塑复合材料制备及性能[J].塑料,2017,(3):18-22.
[22]夏胜娟,杨丹,马博谋,等.棉秆皮纤维增强聚丁二酸丁二醇酯复合材料的制备及降解性能研究[J].化工新型材料,2018,(3):147-151.
[23]迟丽萍,张婷婷,谭洪生.椰壳纤维/PBS可降解复合材料的研究[J].上海化工,2017,42(5):20-25.
[24]殷悦,曹有名.有机酸酸化淀粉用于聚丁二酸丁二醇酯/热塑性淀粉共混物的研究[J].广东化工,2017,44(11):25-26.
[25]宋洁,张敏,许小玲,等.植物虎杖及其提取物改性PBS的性能对比研究[J].工程塑料应用,2016,44(4):7-10.
[26]宋洁,延小雨,张敏,等.PBS/天然虎杖提取物复合材料的界面作用及其性能[J].工程塑料应用,2016,44(8):13-17.
[27]张诗嘉,张倩楠,夏依拉·开依赛尔,等.PBS/望江南提取物抗菌高分子材料的性能研究[J].中国塑料,2018,(1):27-33.
[28]宋洁,延小雨,王婷婷,等.五倍子/PBS复合材料的性能研究[J].陕西科技大学学报,2016,34(4):65-70.
[29]酒巧娜,卢玉献.PBS对两种新型聚乳酸复合材料性能的影响[J].山东化工,2018,47(18):22-23.
[30]田伟,于文海,罗鲲,等.PBS增韧改性MWNTs/PLA导电3D打印耗材的制备及性能[J].材料导报,2018,(31):274-277.
[31]苏桂仙,王佳伟,李佳,等.PLA/PBS/Nano-SiO2制备及性能研究[J].唐山师范学院学报,2017,39(5):9-12.
[32]张力,赵宇培,金叶玲,等.PLA-g-MAH的制备及其对PLA/PBS复合材料性能影响[J].现代塑料加工应用,2017,29(2):29-32.
[33]赵芸芳.吹膜级PBS/PLA复合材料的制备与性能研究[J].工程塑料应用,2016,44(1):41-44.
[34]辜婷,朱大勇,郑强,等.多巴胺改性滑石粉对聚乳酸/聚丁二酸丁二醇酯共混体系结晶行为及流变性能的影响[J].高分子材料科学与工程,2017,33(9):65-71.
[35]朱大勇,辜婷,于杰,等.环氧呋喃树脂反应性增容PLA/PBS共混体系的动态流变学表征[J].材料研究学报,2018,32(7):547-554.
[36]赵聪,司鹏翔,杨昆,等.聚多巴胺改性纳米二氧化硅对PLA/PBS共混复合材料性能的影响[J].塑料工业,2016,44(2):122-125.
[37]张也,张会良,李义,等.可完全生物降解PLA/PPA/PBS薄膜的制备与性能研究[J].塑料科技,2018,(3):78-83.
[38]徐文华,杨智韬,殷小春,等.拉伸形变作用下PLA/PBS增韧共混物力学性能研究[J].中国塑料,2016,30(1):34-38.
[39]唐海龙,陈惠灼,徐文华,等.体积拉伸形变对PLA/PBS共混物结构与性能的影响[J].塑料工业,2016,44(7):43-46.
[40]朱大勇,辜婷,郑强,等.亚磷酸三苯酯对聚乳酸/聚丁二酸丁二醇酯共混体系性能的影响[J].高分子材料科学与工程,2018,(4):43-47.
[41]贾仕奎,王忠,朱艳,等.原位增强PLA/PBS合金的微观形态及力学性能研究[J].塑料工业,2016,44(9):32-36.
[42]胡雪岩,毛海龙,苏婷婷,等.聚丁二酸丁二醇酯(PBS)生物降解的研究进展[J].微生物学杂志,2016,36(4):84-89.
[43]孙炳新,韩春阳,罗思,等.P(3HB-co-4HB)/PBS共混材料酶解性能研究[J].包装工程,2016,37(21):76-80.
[44]胡洁,李东风,臧红霞,等.PBS降解塑料降解性能的研究[J].化工新型材料,2016,(3):175-177.
[45]吴红艳,陈振宏,吕悦慈.静电纺PBS/熔喷复合滤材的制备及性能表征[J].纺织导报,2017,(9):70-73.
[46]阳知乾,刘建忠,吕进,等.POM/PBS共混纤维的结构与性能研究[J].合成纤维工业,2017,40(6):17-21.
[47]顾晶君.生物降解性聚酯聚丁二酸丁二醇酯(PBS)和聚对苯二甲酸-共-丁二酸丁二醇酯(PBST)的性能研究和纤维制备[D].上海:东华大学,2007.
[48]周邓飞.可生物降解PBS的合成及纤维制备[D].杭州:浙江理工大学,2016.
[49]常军,叶芳,李刚,等.含5-FU聚丁二酸丁二酯共聚物的合成及释药性研究[J].广州化工,2016,44(17):64-65.