摘要
通过对多种市售有碱和无碱液体速凝剂产品的性能分析,分析总结了行业上速凝剂产品存在的不足之处。自制了一种无碱和一种有碱速凝剂产品,研究了不同辅料对速凝剂体系的协同增效作用,研究了环境温度、湿度、用水量、水泥种类等测试条件对速凝剂凝结时间的影响,总结了速凝剂在应用过程的注意事项及调整产品适应性的方法。
The performance of a variety of commercially available with and without alkali accelerator products was summarized and some shot-coming of professional accelerators was found. A non-alkali accelerating agent product and a alkaline accelerating agent product was prepared, and the effects of different excipients and the effect of the environmental temperature, humidity, water consumption, type of cement on the setting time of cemet paste were studied. Finally it was concluded that some matters need attention during the application and a few methods to adjust the adaptability of the accelerators.
引文
[1]蔡熠,刘晓勇,孔祥明.不同碱度液体速凝剂的高低温适应性及促凝机理[J].硅酸盐学报, 2016, 44(11):1563-1570.
[2]逄建军,魏中原.铝酸盐型碱性液体速凝剂的制备及性能[J].商品混凝土, 2016(10):27-28.
[3]杨力远,田俊涛,杨艺博.喷射混凝土液体速凝剂研究现状[J].隧道建设, 2017, 37(5):543-552.
[4]王龙飞,李茜茜,董树强.喷射混凝土用无碱速凝剂的制备及性能的研究[J].工程技术, 2017(5):103-104.
[5] Sheng Yanping, Xue Bin, Li Haibin. Preparation and performance of a new-type alkali-free liquid accelerator for shotcrete[J].Advances in Materials Science and Engineering, 2017:1-9.
[6]吴华明,张建纲,于诚.水泥特性对低碱液体速凝剂的适应性影响[J].隧道建设, 2016, 36(5):537-543.
[7]黄斌.无碱速凝剂的凝结时间测试方法研究[J].公路交通科技应用技术版, 2016(9):251-252.
[8]蒋敏,杨春明,尹成杰.无碱无氯液体速凝剂聚合硅酸硫酸铝的制备及机理研究[J].湖南师范大学自然科学学报, 2016,39(2):35-42.
[9]马强,夏义兵,王万金.新型ANS低碱液体速凝剂的研制与应用[J].混凝土与水泥制品, 2015, 11(11):25-28.
[10]杨力远,田俊涛,胡小峰.新型无碱液体速凝剂的制备与性能研究[J].新型建筑材料, 2017(5):29-32.
[11]张丰,蔡跃波,丁建彤.新型无碱液体速凝剂性能及作用机理分析[J].水电能源科学, 2017, 35(5):140-144.
[12]骆志超,李全堂.一种常温合成无碱速凝剂的方法及性能研究[J].商品混凝土, 2016(6):34-34.