一种钢质储罐防腐用氟碳涂料的制备及施工性的优化
|
摘要
研制了一种可高压无气喷涂的钢质储罐防腐用氟碳涂料,有效解决了高压无气喷涂不出漆或者出现流挂、痱子、针孔、橘皮等漆膜弊病。
A kind of barrier free high-pressure airless spraying fluorocarbon coating used on anti-corrosion steel storage tank was developed. The fluorocarbon coating effectively solved the high-pressure airless spray out of the paint or sagging, prickly heat, pinhole, peel film defects, etc.
A kind of barrier free high-pressure airless spraying fluorocarbon coating used on anti-corrosion steel storage tank was developed. The fluorocarbon coating effectively solved the high-pressure airless spray out of the paint or sagging, prickly heat, pinhole, peel film defects, etc.
引文
[1]徐建月.中国防水涂料机械化施工势在必行[J].中国涂料,2011,26(12):17-19.
[2]赵世红,戴惠新,薛海峰,等.不同喷涂工具对涂装质量的影响[J].现代涂料与涂装,2014,17(1):46-47.
[3]杜存山.“三分涂料,七分施工”的科学性[J].现代涂料与涂装,2013,16(2):20-21.
[4]孙振红,李华明,周晓红,等.W61-800各色有机硅耐高温涂料研究[J].中国涂料,2011,26(12):34-36.
[5]刘洪珠.氟含量与氟碳涂料性能关系浅析[J].现代涂料与涂装,2005,10(3):4-6.
[6]谢文峰,管颖超.室温固化钢结构防护用氟碳涂料的研制[J].合成材料老化与应用,2013,42(3):5-10.
[7]曾凡辉,周升,刘含茂.高原铁路捣固车用氟碳涂料耐候性能研究[J].涂料技术与文摘,2011(11):32-34.
[8]霁虹,戚鹏.常温固化型氟碳涂料交联体系的研究[J].中国涂料,2006,21(3):24-26.
[9]钟鑫,牛潼凤,胡文峰.常温固化氟碳涂料的研究[J].现代涂料与涂装,2008,11(12):4-7.
[10]刘国杰.氟碳树脂在反射隔热涂料中的应用前景[J].中国涂料,2011,26(11):21-25.
[11]孙道兴,古国华.高档涂料调制过程中的技术问题[J].现代涂料与涂装,2003,6(1):20-22.
[2]赵世红,戴惠新,薛海峰,等.不同喷涂工具对涂装质量的影响[J].现代涂料与涂装,2014,17(1):46-47.
[3]杜存山.“三分涂料,七分施工”的科学性[J].现代涂料与涂装,2013,16(2):20-21.
[4]孙振红,李华明,周晓红,等.W61-800各色有机硅耐高温涂料研究[J].中国涂料,2011,26(12):34-36.
[5]刘洪珠.氟含量与氟碳涂料性能关系浅析[J].现代涂料与涂装,2005,10(3):4-6.
[6]谢文峰,管颖超.室温固化钢结构防护用氟碳涂料的研制[J].合成材料老化与应用,2013,42(3):5-10.
[7]曾凡辉,周升,刘含茂.高原铁路捣固车用氟碳涂料耐候性能研究[J].涂料技术与文摘,2011(11):32-34.
[8]霁虹,戚鹏.常温固化型氟碳涂料交联体系的研究[J].中国涂料,2006,21(3):24-26.
[9]钟鑫,牛潼凤,胡文峰.常温固化氟碳涂料的研究[J].现代涂料与涂装,2008,11(12):4-7.
[10]刘国杰.氟碳树脂在反射隔热涂料中的应用前景[J].中国涂料,2011,26(11):21-25.
[11]孙道兴,古国华.高档涂料调制过程中的技术问题[J].现代涂料与涂装,2003,6(1):20-22.