新型低VOC常温固化氟碳涂料的研制
|
摘要
采用新型高性能氟丙烯乙烯基醚(FPVE)氟树脂作为基料,将N3390与Z4470复配作为体系的固化剂,辅以合适的颜填料、溶剂、助剂等,制备了一种高性能、低VOC(挥发性有机化合物)常温固化氟碳涂料。重点考察了不同固化剂、分散剂、流平剂等对涂料性能的影响。各项性能测试结果表明,制备的低VOC氟碳涂料具有优异的耐候性与防腐性能。
A high performance low VOC room temperature curing fluorocarbon coatings was prepared by using a new high performance FPVE(fluorine propene vinyl ether) fluorine resin as the base,the compound of N3390 and Z4470 as the curing agent,and supplemented with suitable pigments and fillers,additives,etc. The effects of different curing agents,dispersants and leveling agents on the properties of fluorocarbon coatings were emphatically investigated. Various performance test results showed that the prepared low VOC fluorocarbon coatings has excellent weatherability and anticorrosion performance.
A high performance low VOC room temperature curing fluorocarbon coatings was prepared by using a new high performance FPVE(fluorine propene vinyl ether) fluorine resin as the base,the compound of N3390 and Z4470 as the curing agent,and supplemented with suitable pigments and fillers,additives,etc. The effects of different curing agents,dispersants and leveling agents on the properties of fluorocarbon coatings were emphatically investigated. Various performance test results showed that the prepared low VOC fluorocarbon coatings has excellent weatherability and anticorrosion performance.
引文
[1]杜安梅.从10年来中国氟碳涂料的应用状况看其发展前景[J].涂料技术与文摘,2009(11):16-18.
[2]巩永忠,温嘉琪,王巧玲,等.溶剂型FEVE氟碳树脂质量控制与品质提升[J].涂料工业,2008,38(11):54-58.
[3]沈浩,卞大荣,戴海雄,等.从“绿色化学”到“绿色涂料”[J].中国涂料,2010,25(11):16-18.
[4]刘洪珠,李缙成,赵兴顺.我国水性氟碳树脂研究综述[J].上海涂料,2010,48(4):37.
[5]胡玮华.常温固化FEVE涂料的制备与性能研究[D].浙江杭州:浙江大学,2013.
[6]荆夕庆,武春梅,李永,等.水性/高固含/无溶剂工业防腐涂料产品全生命周期的环保分析[J].涂料工业,2018,48(1):63-69.
[7]刘长亮,曹亚成,朱东,等.分散助剂在大金GK系四氟树脂涂料中的应用[J].涂料工业,2009,39(5):69.
[8]王健,曾凡辉,刘含茂.氟碳涂料分散性能的研究[J].中国涂料,2011,26(2):21.
[9]高广民.助剂的特点及其在氟涂料中的应用[J].有机氟化工,2004(1):54.
[2]巩永忠,温嘉琪,王巧玲,等.溶剂型FEVE氟碳树脂质量控制与品质提升[J].涂料工业,2008,38(11):54-58.
[3]沈浩,卞大荣,戴海雄,等.从“绿色化学”到“绿色涂料”[J].中国涂料,2010,25(11):16-18.
[4]刘洪珠,李缙成,赵兴顺.我国水性氟碳树脂研究综述[J].上海涂料,2010,48(4):37.
[5]胡玮华.常温固化FEVE涂料的制备与性能研究[D].浙江杭州:浙江大学,2013.
[6]荆夕庆,武春梅,李永,等.水性/高固含/无溶剂工业防腐涂料产品全生命周期的环保分析[J].涂料工业,2018,48(1):63-69.
[7]刘长亮,曹亚成,朱东,等.分散助剂在大金GK系四氟树脂涂料中的应用[J].涂料工业,2009,39(5):69.
[8]王健,曾凡辉,刘含茂.氟碳涂料分散性能的研究[J].中国涂料,2011,26(2):21.
[9]高广民.助剂的特点及其在氟涂料中的应用[J].有机氟化工,2004(1):54.