摘要
采用微波合成法制备La_(0.6)Sr_(0.4)Co_(0.2)Fe_(0.8)O_3阴极材料,并对材料进行XRD及SEM测试。研究结果表明最佳的微波合成工艺为:微波功率为720W,反应时间为50min。XRD测试结果表明:所制备出的阴极材料为单一的钙钛矿结构,无其他杂相生成。SEM研究结果表明:合成样品内粒子分布比较均匀,颗粒尺寸小于10μm,说明微波合成法能获得粒度较小且分布均匀的合成材料。
By using the microwave synthesis method, the paper prepares the cathode material La_(0.6)Sr_(0.4)Co_(0.2)Fe_(0.8)O_3, and conducts XRD and SEM test on them. The results show that the optimum microwave synthesis is 720 w microwave power and 50 min reaction time. The test XRD shows that the prepared cathode material has a single perovskite structure and no other impurities. The results of SEM show that the particle size of synthesized samples is less than 10 micro meter, which indicates that the microwave synthesized material with small particle size and uniform distribution can be obtained.
引文
[1]纪媛,刘江,贺天民等. 甘氨酸-硝酸盐法制备中温SOFC电解质及电极材料[J]. 高等学校化学学报,2002,23(7) :1227-1230.
[2]石纪军,吴也凡,罗凌虹等. 溶胶-凝胶法制备固体氧化物燃料电池阴极粉体及其电性能La0.6Sr0.4Co0.4Fe0.6O3[J]. 硅酸盐学报,2013,41(7) :944-948.
[3]张立德. 超微粉体制备与应用技术[M].北京:中国石化出版社,2001,22-24.
[4]江金国,崔崇. La0.6Sr0.4Co1-yFeyO3系阴极材料制备及表征[J]. 材料科学与工程学报,2005,23(5) :615-617.
[5]翟秀静,符岩,刘忠文等. 微波合成固体氧化物燃料电池阴极材料Lal-xSrxMnO3的研究[J],材料与冶金学报,2002,1(1):294-296.