摘要
铁粉芯是一种具有良好软磁特性和频率特性的材料。采用放电等离子烧结(SPS)的方法制备了镍锌铁氧体包覆还原铁粉的铁粉芯,研究了铁氧体含量对铁粉芯的包覆效果和磁性能的影响。结果表明,适量的铁氧体含量有利于Fe/NiZnFe_2O_4铁粉芯的包覆和磁性能,铁氧体含量为8%时,可较好的包覆在铁粉颗粒表面,制得的磁粉芯性能最佳,具有较高的振幅磁导率μa,较低的矫顽力Hc、视在功率Ss和损耗Ps。对其损耗进一步分析发现,当频率f≤30kHz时,涡流损耗Pe占总损耗的比例<40%,磁滞损耗Ph是总损耗的主要来源;当频率f>70kHz时,Pe所占的比例>60%,这一结果对于指导磁粉芯的应用提供了理论基础,也为进一步降低铁粉芯的损耗指明了努力的方向。
The iron powder core is a kind of materials with good soft magnetic properties and frequency characteristics.In this paper,the iron powder core of nickel-zinc ferrite coated reduced iron powder was prepared by spark plasma sintering(SPS)method.The consequence of ferrite content on the coating effect and magnetic properties of the iron powder core was investigated.The results show that the suitable ferrite content was conducive to coating effect and magnetic properties of Fe/NiZnFe_2O_4 powder core.When the ferrite content was 8%,it could be coated on the surface of powder particles and a good magnetic performance,such as high amplitude permeabilityμa,low coercive force Hc,apparent power Ssand loss Ps,was obtained.Further analysis of the loss shows that when the frequency f was less than 30 kHz,the eddy loss current Peaccounted for less than 40% of the total loss.When the frequency f was higher than 70 kHz,the proportion of Pewas more than 60%.The result provides a theroical basis which has made a great contribution to guiding the application of the magnetic powder core,and also indicates the direction of efforts to reduce the loss.
引文
[1]Shokrollahi H,Janghorban K.Soft magnetic composite materials(SMCs)[J].Journal of Materials Processing Technology,2012,189(1):1-12.
[2]Shokrollahi H,Janghorban K.Effect of warm compaction on the magnetic and electrical properties of Fe-based soft magnetic composites[J].Journal of Magnetism&Magnetic Materials,2007,313(1):182-186.
[3]Liu Feifei,Bakera P,Weng Lvqian,et al.Study of phosphate coatings for Fe based soft magnetic composites[J].Development and Application of Materials,2007,22(5):11-15(in Chinese).刘菲菲,Bakera P,翁履谦,等.铁粉基软磁复合材料绝缘包覆层的研究[J].材料开发与应用,2007,22(5):11-15.
[4]Geng K,Xie Y,Yan B.Fe-Si/ZrO2composites with coreshell structure and excellent magnetic properties prepared by mechanical milling and spark plasma sintering[J].Journal of Alloys&Compounds,2017,718:53-62.
[5]Wang M,Zan Z,Zhao Z.Preparation of pure iron/Ni-Zn ferrite high strength soft magnetic composite by spark plasma sintering[J].Journal of Magnetism&Magnetic Materials,2014,361(4):166-169.
[6]Taghvaei A,Shokrollahi H,Janghorban K.Properties of iron-based soft magnetic composite with iron phosphatesilane insulation coating[J].Journal of Alloys&Compounds,2009,481(1):681-686.
[7]Shokrollahi H,Janghorban K,Mazaleyrat F.Investigation of magnetic properties,residual stress and densification in compacted iron powder specimens coated with polyepoxy[J].Materials Chemistry&Physics,2009,114(2):588-594.
[8]Wu S,Sun A,Lu Z,et al.Magnetic properties of ironbased soft magnetic composites with SiO2,coating obtained by reverse microemulsion method[J].Journal of Magnetism&Magnetic Materials,2015,381:451-456.
[9]Weng Xingyuan.Application and market development of NiZn soft ferrite materials[J].Advanced Materials Industry,2002(4):23-24(in Chinese).翁兴园.NiZn软磁铁氧体材料应用与市场发展[J].新材料产业,2002(4):23-24.
[10]Gheisari K,Javadpour S,Shokrollahi H,et al.Magnetic losses of the soft magnetic composites consisting of iron and Ni-Zn ferrite[J].Journal of Magnetism&Magnetic Materials,2008,320(8):1544-1548.
[11]Peng Y,Nie J,Zhang W,et al.Preparation of soft magnetic composites for Fe particles coated with(NiZn)Fe2O4,via microwave treatment[J].Journal of Magnetism&Magnetic Materials,2015,395:245-250.
[12]Li X,Dong Y,Liu M,et al.New Fe-based amorphous soft magnetic composites with significant enhancement of magnetic properties by compositing with nano-(NiZn)Fe2O4[J].Journal of Alloys&Compounds,2016,696.:1323-1328.
[13]Bir ckovZ,Kollr P,Vojtek V,et al.Influence of vitroperm content on the energy losses in composite materials based on the mixture of two ferromagnets[J].Acta Physica Polonica,2014,126:114-115.
[14]Wu S,Fan J L,Liu J X,et al.Fabrication and properties of iron-based soft magnetic composites coated with NiZnFe2O4[J].Journal of Materials Engineering,2017,153(7):60-65
[15]Pluta W A.Some properties of factors of specific total loss components in electrical steel[J].IEEE Transactions on Magnetics Mag,2010,46(2):322-325.
[16]Kollr P,Bir ckovZ,Füzer J,et al.Power loss separation in Fe-based composite materials[J].Journal of Magnetism&Magnetic Materials,2013,327:146-150.