油气井CO_2腐蚀主控因素及对策分析
|
摘要
高温高压高浓度CO_2介质下油气井管具腐蚀问题日趋严重,针对此问题,本文重点分析了CO_2腐蚀的主控因素及防腐对策。基于CO_2腐蚀环境主控因素、腐蚀类型,腐蚀机理及腐蚀评价方法,总结认为,CO_2分压、温度、流速是CO_2腐蚀的主要影响因素,且在有水的下,CO_2分压对腐蚀速率的影响最大,其次是温度,流速影响最小。防腐主要需通过缓蚀剂防护、涂层防护、化学镀层等措施来实现,咪唑啉类缓蚀剂、噻唑类缓蚀剂和硫脲类缓蚀剂具有很好的缓蚀效果,涂层防护主要包括环氧树脂防腐涂料、聚氨酯防腐涂料、聚苯胺防腐涂料、高固体分防腐涂料四种,也可以采用镍磷合金镀管或双层镀管的方法进行防护。
引文
[1] 王承陆,于川.川西须家河组气藏气井油管腐蚀机理及对策[J].科研,2016,4(10):88～91.
[2] 李同同.高CO2分压下井筒温度对井下工具用钢腐蚀行为的影响[J].石油化工腐蚀与保护,2017.3(10):34～36.
[3] 蒲江涛.双金属复合管焊接接头在CO2介质环境下的腐蚀分析[J].焊接技术,2016,3(14):34～36.
[4] Warrd C D, Milliams D E. Carbonic Acid Corrosion of Steel[ J] . Corrosion, 1975, 31( 5):131.
[5] Davies D H,Burstein G T.The Effects of Bicarbonate on the Corrosion of Passivation of Iron[J].Corrosion,1980,36(8):416.
[6] Ogundele G I ,White W E,Some observation on corrosion of carbon steel in aqueous environment containing carbon dioxide,Corrosion,1986,42 (2):71.
[7] S.Nesic,J.Postlethwaite,and S.01sen,“An Eleetroehemieal Predietion of Corrosion of Mild Steel in the Aqueous Carbon Dioxide Solutions,[J].Corrrosion,Vol.52,No.4.P280,1996.
[8] Linter B R,Burstein G T.Reactions of Pipeline Steels in Carbon Dioxide Solution.Corrosion Science.1999.42(2):117-139.
[9] C.DeWarrd,D .E.Milliams,Corrosion[J], Vol.31,No.5, P177,1975.
[10] G.Sehit Fundamental Aspeets of CO2 corrosion[J].eorrosion/83.NACE,1983(43).
[11] G.L.Ogundele and W.E.White, Some observations on Corrosion of Carbon of Carbon ste11 in Aqueous Environment Containing Carbon Dioxide[J].Corrosion,Vol.42,No.2,P71,1986.
[12] De warrd,U Lotz.Prediction of CO2 Corrosion of Carbon Steel[C].A Working Party Report on prediction CO2 Corrosion in Oil and Gas Industry,1994:30 58.22.
[13] Ikeda,M Ueda,S Mukai. CO2 Bhavior of Carbon and Cr Steels[C].NACE,Houston,1985:39～51.
[14] 姚鹏程.高温高压环境Cl-浓度和CO2分压对不锈钢油管的影响[J].全面腐蚀控制,2017,3(10):77～79.
[15] 田光. 流速对二氧化碳腐蚀速率影响的研究[D].西安石油大学,2010.
[16] 张忠铧,郭金宝.CO2对油气管材的腐蚀规律及国内外研究进展[J].宝钢技术,2000,(4):54～58.
[17] 刘小燕. 油井管材料流体诱导腐蚀研究[D].西安石油大学,2013.
[18] 孟玲.油气管材CO2腐蚀机理及其防护措施[J].热喷涂技术,2017,4(11):244～246.
[19] 刘鹤霞,郑家.气田气井缓蚀剂研究[J].四川化工与腐蚀控制,2003,(2):24～25+63.
[20] 刘烈炜. 咪唑啉缓蚀剂的合成及其协同效应的研究[A].中国腐蚀与防护学会缓蚀剂专业委员会.第八届全国缓蚀剂学术讨论会论文集[C].中国腐蚀与防护学会缓蚀剂专业委员会:中国腐蚀与防护学会缓蚀剂专业委员会,1993:3.
[21] 申成俊.南堡陆地油田二氧化碳腐蚀机理及防治措施[J].内蒙古石油化工,2016,3(14):45～47.
[22] 利进飞.油气管线的腐蚀与防护[J].石化技术,2017,3(11):88～90.
[23] 雷海.石油管道硫化氢腐蚀与防护对策分析[J].石化技术,2017,3(11):24～26.
[24] 付琬璐,史胜南,李娜.钢结构防腐涂料的研究现状及发展方向[J].辽宁化工,2017,46(07):731～734+738.
[25] 马明贤.油田管道防腐蚀的原因及对策[J].数字化用户,2017,3(11):255～256.
[26] 王秀娟. 高固体分环氧防腐涂料的制备[J].涂料技术与文摘,20120,(10)1672～2418.
[27] 文鸿基,刘军,廖江,等.油管钢的H2S/CO2动态腐蚀行为[J].石油化工腐蚀与防护,2010,12,25.
[28] 徐庆达.浅谈潮湿环境下金属腐蚀防护技术[J].化工管理,2016,(29):221.
[2] 李同同.高CO2分压下井筒温度对井下工具用钢腐蚀行为的影响[J].石油化工腐蚀与保护,2017.3(10):34～36.
[3] 蒲江涛.双金属复合管焊接接头在CO2介质环境下的腐蚀分析[J].焊接技术,2016,3(14):34～36.
[4] Warrd C D, Milliams D E. Carbonic Acid Corrosion of Steel[ J] . Corrosion, 1975, 31( 5):131.
[5] Davies D H,Burstein G T.The Effects of Bicarbonate on the Corrosion of Passivation of Iron[J].Corrosion,1980,36(8):416.
[6] Ogundele G I ,White W E,Some observation on corrosion of carbon steel in aqueous environment containing carbon dioxide,Corrosion,1986,42 (2):71.
[7] S.Nesic,J.Postlethwaite,and S.01sen,“An Eleetroehemieal Predietion of Corrosion of Mild Steel in the Aqueous Carbon Dioxide Solutions,[J].Corrrosion,Vol.52,No.4.P280,1996.
[8] Linter B R,Burstein G T.Reactions of Pipeline Steels in Carbon Dioxide Solution.Corrosion Science.1999.42(2):117-139.
[9] C.DeWarrd,D .E.Milliams,Corrosion[J], Vol.31,No.5, P177,1975.
[10] G.Sehit Fundamental Aspeets of CO2 corrosion[J].eorrosion/83.NACE,1983(43).
[11] G.L.Ogundele and W.E.White, Some observations on Corrosion of Carbon of Carbon ste11 in Aqueous Environment Containing Carbon Dioxide[J].Corrosion,Vol.42,No.2,P71,1986.
[12] De warrd,U Lotz.Prediction of CO2 Corrosion of Carbon Steel[C].A Working Party Report on prediction CO2 Corrosion in Oil and Gas Industry,1994:30 58.22.
[13] Ikeda,M Ueda,S Mukai. CO2 Bhavior of Carbon and Cr Steels[C].NACE,Houston,1985:39～51.
[14] 姚鹏程.高温高压环境Cl-浓度和CO2分压对不锈钢油管的影响[J].全面腐蚀控制,2017,3(10):77～79.
[15] 田光. 流速对二氧化碳腐蚀速率影响的研究[D].西安石油大学,2010.
[16] 张忠铧,郭金宝.CO2对油气管材的腐蚀规律及国内外研究进展[J].宝钢技术,2000,(4):54～58.
[17] 刘小燕. 油井管材料流体诱导腐蚀研究[D].西安石油大学,2013.
[18] 孟玲.油气管材CO2腐蚀机理及其防护措施[J].热喷涂技术,2017,4(11):244～246.
[19] 刘鹤霞,郑家.气田气井缓蚀剂研究[J].四川化工与腐蚀控制,2003,(2):24～25+63.
[20] 刘烈炜. 咪唑啉缓蚀剂的合成及其协同效应的研究[A].中国腐蚀与防护学会缓蚀剂专业委员会.第八届全国缓蚀剂学术讨论会论文集[C].中国腐蚀与防护学会缓蚀剂专业委员会:中国腐蚀与防护学会缓蚀剂专业委员会,1993:3.
[21] 申成俊.南堡陆地油田二氧化碳腐蚀机理及防治措施[J].内蒙古石油化工,2016,3(14):45～47.
[22] 利进飞.油气管线的腐蚀与防护[J].石化技术,2017,3(11):88～90.
[23] 雷海.石油管道硫化氢腐蚀与防护对策分析[J].石化技术,2017,3(11):24～26.
[24] 付琬璐,史胜南,李娜.钢结构防腐涂料的研究现状及发展方向[J].辽宁化工,2017,46(07):731～734+738.
[25] 马明贤.油田管道防腐蚀的原因及对策[J].数字化用户,2017,3(11):255～256.
[26] 王秀娟. 高固体分环氧防腐涂料的制备[J].涂料技术与文摘,20120,(10)1672～2418.
[27] 文鸿基,刘军,廖江,等.油管钢的H2S/CO2动态腐蚀行为[J].石油化工腐蚀与防护,2010,12,25.
[28] 徐庆达.浅谈潮湿环境下金属腐蚀防护技术[J].化工管理,2016,(29):221.