核电站安全壳涂层腐蚀试验及性能评价
|
摘要
通过在同等盐雾加速腐蚀环境下,对无机富锌底漆和热喷锌进行长期腐蚀对比试验研究,获得两种锌涂层的电化学行为及微观结构特征,用于评价无机富锌涂层的可靠性。
A comparative study on the long-term corrosion behavior of inorganic zinc-rich primer and hot-spraying zinc under the same salt spray accelerated corrosion environment has been carried out to obtain the electrochemical behavior and microstructure of the two coatings, which can be used to evaluate the reliability of inorganic zinc coating.
A comparative study on the long-term corrosion behavior of inorganic zinc-rich primer and hot-spraying zinc under the same salt spray accelerated corrosion environment has been carried out to obtain the electrochemical behavior and microstructure of the two coatings, which can be used to evaluate the reliability of inorganic zinc coating.
引文
[1]蒋艳林.CrFeAITi涂层抗高温氧化性及耐铅铋合金腐蚀性研究[D].衡阳:南华大学,2015.
[2]刘晓强,徐雪莲,孟凡江,等.非能动核电站安全壳涂层的设计与可靠性分析[J].涂料工业,2015,45(4):74-78.
[3]陈哲.核电站环氧树脂涂层老化机理及寿命分析[D].上海:上海交通大学,2013.
[4]张瑞.环氧丙聚涂层失效规律及剩余寿命预测研究[D].长沙:湖南大学,2016.
[5]马卫锋,费凡,刘冬梅,等.基于模糊理论的在役管道内涂层寿命评价方法[J].天然气与石油,2012,30(6):5-8.
[6]杨晓光,耿瑞,周燕佩.热障涂层氧化和热疲劳寿命实验研究[J].航空动力学报,2003,18(2):195-200.
[7]石江波.压水堆核电站关键材料的在线腐蚀监检测[D].天津:天津大学,2010.
[8]LEE S H,LEE J D,KIM M Y,et al.Evaluation of accelerated Ageing cables used in nuclear power plant[J].Proceedings Of2012 IEEE International Conference on Condition Monitoring and Diagnosis(IEEE CMD 2012),2012:681-684.
[9]VLCEK L.The current status of new Czech corrosion fatigue evaluation proposal for WWER nuclear power plants[J].Procedia Materials Science,2016,12:18-23.
[10]HORVATH D A,COLAIANNI R P.Updated aging assessment approach and use with electric cable insulation[J].Nuclear Technology,2003,143(143):161-170.
[2]刘晓强,徐雪莲,孟凡江,等.非能动核电站安全壳涂层的设计与可靠性分析[J].涂料工业,2015,45(4):74-78.
[3]陈哲.核电站环氧树脂涂层老化机理及寿命分析[D].上海:上海交通大学,2013.
[4]张瑞.环氧丙聚涂层失效规律及剩余寿命预测研究[D].长沙:湖南大学,2016.
[5]马卫锋,费凡,刘冬梅,等.基于模糊理论的在役管道内涂层寿命评价方法[J].天然气与石油,2012,30(6):5-8.
[6]杨晓光,耿瑞,周燕佩.热障涂层氧化和热疲劳寿命实验研究[J].航空动力学报,2003,18(2):195-200.
[7]石江波.压水堆核电站关键材料的在线腐蚀监检测[D].天津:天津大学,2010.
[8]LEE S H,LEE J D,KIM M Y,et al.Evaluation of accelerated Ageing cables used in nuclear power plant[J].Proceedings Of2012 IEEE International Conference on Condition Monitoring and Diagnosis(IEEE CMD 2012),2012:681-684.
[9]VLCEK L.The current status of new Czech corrosion fatigue evaluation proposal for WWER nuclear power plants[J].Procedia Materials Science,2016,12:18-23.
[10]HORVATH D A,COLAIANNI R P.Updated aging assessment approach and use with electric cable insulation[J].Nuclear Technology,2003,143(143):161-170.