高硅钢轧制法制备技术的研究进展
|
摘要
磁性能优良的高硅钢由于室温脆性而难以采用传统轧制法生产。介绍了合金增韧法、包埋轧制法、粉末轧制法、温轧法、铸轧法等5种高硅钢特殊轧制法制备技术,给出了每种轧制法的定义、生产原理、研究方法、研究内容、工艺参数和存在问题,总结了高硅钢的主要优点及应用领域,展望了高硅钢的发展前景及研究方向。分析认为,在能源日益紧张的今天,尤其在高频信息领域,高硅钢是普通硅钢的理想替代材料。作为一种高效节能电磁材料,高硅钢必将得到高度关注及快速发展。铸轧法和温轧法相结合的制备技术将成为高硅钢轧制法今后的主要研究方向。
It's difficult to produce high silicon steel with excellent magnetic properties by conventional rolling method because of its room temperature brittleness.There are five preparation technologies of special rolling method for high silicon steel introduced in this paper,such as the method of alloy increasing ductility,embedrolling,powder rolling,warm rolling and cast-rolling.Definition,production principle,research methods and contents,process parameters and existing problems for each rolling method are given.Main advantages and application fields of high silicon steel are summarized.Development of high silicon steel and research direction of rolling method are prospected.It is analyzed that high silicon steel is the ideal alternative material for common silicon steel especially in high frequency information field at the days growing tension in the energy.High silicon steel will certainly be got the high concern and rapid development as a kind of energy-efficient electromagnetic material.Rolling technology combining cast-rolling method with warm rolling method will be the main research direction for rolling method of high silicon steel in the future.
It's difficult to produce high silicon steel with excellent magnetic properties by conventional rolling method because of its room temperature brittleness.There are five preparation technologies of special rolling method for high silicon steel introduced in this paper,such as the method of alloy increasing ductility,embedrolling,powder rolling,warm rolling and cast-rolling.Definition,production principle,research methods and contents,process parameters and existing problems for each rolling method are given.Main advantages and application fields of high silicon steel are summarized.Development of high silicon steel and research direction of rolling method are prospected.It is analyzed that high silicon steel is the ideal alternative material for common silicon steel especially in high frequency information field at the days growing tension in the energy.High silicon steel will certainly be got the high concern and rapid development as a kind of energy-efficient electromagnetic material.Rolling technology combining cast-rolling method with warm rolling method will be the main research direction for rolling method of high silicon steel in the future.
引文
[1] Kubota T,Fujikura M,Ushigami Y.Recent progress and future trend on grain-oriented silicon steel[J].Journal of Magnetism&Magnetic Materials,2000,215(00):69-73.
[2] Long Qiong.Preparing of Fe-Si coating by composite electro-deposition in magnetic field[D].Shanghai:Shanghai University,2014(in Chinese).龙琼.磁场下复合电沉积法制备Fe-Si镀层的基础研究[D].上海:上海大学,2014.
[3] Zheng Xin,Yan Biao.Properties and preparation techniques of Fe-6.5%Si high silicon steel[J].Materials Review,2012,26(19):392-396(in Chinese).郑鑫,严彪.Fe-6.5%Si高硅钢的性能及制备技术[J].材料导报,2012,26(19):392-396.
[4] Ma H L,Li Y,Geng Z R.Preparation of high silicon steel by multi-arc ion coating and diffusion[J].Rare Metal Materials&Engineering,2015,44(10):2373-2375.
[5] Matsumura S,Tanaka Y,Koga Y,et al.Concurrent ordering and phase separation in the vicinity of the metastable critical point of order-disorder transition in Fe-Si alloys[J].Materials Science&Engineering A,2001,312(1-2):284-292.
[6] Jang P,Lee B.Order-disorder transition and magnetic properties of Fe-6.5Si alloy powder cores[J].Physica Status Solidi,2007,204(12):4108-4112.
[7] Viala B,Degauque J,Baricco M,et al.Study of the brittle behaviour of annealed Fe-6.5wt%Si ribbons produced by planar flow casting[J].Materials Science&Engineering A,1996,212(1):62-68.
[8] Haiji H,Okada K,Hiratani T,et al.Magnetic properties and workability of 6.5%Si steel sheet[J].Journal of Magnetism&Magnetic Materials,1996,160(7):109-114.
[9] Lin Junpin,Ye Feng,Chen Guoliang,et al.Fabrication technology, microstructures and properties of Fe-6.5wt.%Si alloy sheets by cold rolling[J].Frontier Science,2007(2):13-26(in Chinese).林均品,叶丰,陈国良,等.6.5wt%Si高硅钢冷轧薄板制备工艺、结构和性能[J].前沿科学,2007(2):13-26.
[10] Li Hui,Liang Jinglong,Zhao Xiaoping,et al.Effect of temperature on diffusion of Si in 1.6Si non-oriented silicon steel during molten salt electro-deposit process[J].Special Steel,2014,35(6):12-14(in Chinese).李慧,梁精龙,赵晓萍,等.熔盐电沉积过程温度对1.6Si无取向硅钢Si扩散的影响[J].特殊钢,2014,35(6):12-14.
[11] Ma Hailin,Liu Xi,Xia Rongbin,et al.Fabrication of high-Si steel by vacuum thermal diffusion of sputtered Fe-Si multilayers[J].Chinese Journal of Vacuum Science and Technology,2016,36(2):154-158(in Chinese).马海林,刘曦,夏荣斌,等.双靶直流溅射多层膜的叠加结构对沉积扩散法制备高硅钢硅含量的影响[J].真空科学与技术学报,2016,36(2):154-158.
[12] Takada Y,Abe M,Masuda S,et al.Commercial scale production of Fe-6.5wt.%Si sheet and its magnetic[J].Journal of Applied Physics,1988,64(10):5367-5369.
[13] Li Qi.Low temperature plastic and rolling of Fe-6.5wt.%Si high silicon steel[D].Shenyang:Northeastern University,2009(in Chinese).李其.Fe-6.5wt.%Si低温塑性与轧制法制备[D].沈阳:东北大学,2009.
[14] Narita K,Enokizono M.Effect of nickel and manganese addition on ductility and magnetic properties of 6.5%silicon-iron alloy[J].IEEE Transactions on Magnetics,1978,14(4):258-262.
[15] Glezer A,Maleeva I,Zakharov A.Influence of alloy elements on the plasticity of high-silicon iron[J].Metal Science&Heat Treatment,1985,27(12):908-912.
[16] Lizzi T,Narasimhan K,Dulis E.The development of Goss texture in Fe-6.5%-2%Ni[J].IEEE transactions on magnetics,1986,22(5):499-501.
[17] Ferrando L,Lebourg C,Ferrara E,et al.Effect of stress on magnetic losses and role of Mn addition in FeSi rapidly solidified ribbons[J].Journal of Magnetism&Magnetic Materials,2000,215:127-129.
[18] Barros J,Ros-Ya1ez T,Vandenbossche L,et al.The effect of Si and Al concentration gradients on the mechanical and magnetic properties of electrical steel[J].Journal of Magnetism&Magnetic Materials,2005,s290-291(290):1457-1460.
[19] Huang Y,Yuan W,Qiao Z,et al.A thermo-dynamic study of the DO3-ordered intermetallic compound Fe3Al[J],Journal of Alloys&Compounds,2008,458:277-281.
[20] Bolfarini C,Silva M C A,Jr A M J,et al.Magnetic properties of spray-formed Fe-6.5%Si and Fe-6.5%Si-1.0%Al after rolling and heat treatment[J].Journal of Magnetism&Magnetic Materials,2008,320:653-656.
[21] Pan Limei,Kim Kilnam,Lin Junpin,et al.Experimental study on the influence of boron on mechanical properties of the Fe-6.5wt%Si alloys[J].Journal of Functional Materials,2004,35(6):683-685(in Chinese).潘丽梅,金吉男,林均品,等.硼元素对Fe-6.5%Si(质量分数)合金力学性能影响的试验研究[J].功能材料,2004,35(6):683-685.
[22] Kim K N,Pan L M,Lin J P,et al.The effect of boron content on the processing for Fe-6.5wt%Si electrical steel sheets[J].Journal of Magnetism&Magnetic Materials,2004,277:331-336.
[23] Wang Xu.Research of manufacturing process of high silicon steel by CVD method[D].Shanghai:East China University of Science and Technology,2013(in Chinese).王旭.CVD法制备高硅钢的工艺过程研究[D].上海:华东理工大学,2013.
[24] Sakai T,Suzuki Y,Shimosato S,et al.Magnetic properties of Fe-Si alloys by powder metallurgy[J].IEEE Transactions on Magnetics,1977,13(5):1445-1447.
[25] Wang W F.Rolling compaction,magnetic properties,and microstructural development during sintering of FeSi[J].Powder Metallurgy,1995,38(4):289-293.
[26] Kusaka K,Imaoka T,Kondo T.Relationship between magnetic properties and Si-content/sintering conditions of Fe-Si type magnetic alloys[J].Journal of the Japan Society of Powder&Powder Metallurgy,2000,47(2):195-202.
[27] Tang N W,Zhong Y B,Sun Z Q,et al.Preparing high silicon steel by sintering Fe-6.5%Si powder compacts in magnetic field[J].Journal of Iron&Steel Research(International),2012(s1):455-458.
[28] Shen Q,Zhou Y,Li J G,et al.Sintering behavior of FeSi composite powder by DPR technique[J].Key Engineering Materials,2007,336-338:2344-2346.
[29] Qu X H,Gowri S,John A.Sintering behavior and strength of Fe-Si-P compacts[J].International Journal of Powder Metallurgy,1991,27(1):9-13.
[30] Li R,Shen Q,Zhang L,et al.Magnetic properties of high silicon iron sheet fabricated by direct powder rolling[J].Journal of Magnetism&Magnetic Materials,2004,281(2-3):135-139.
[31] Yuan Wenjie,Shen Qiang,Zhang Lianmeng.Research on Fe-6.5%Si silicon steel produced by powder rolling technique[J].Powder Metallurgy Technology,2007,25(1):32-34(in Chinese).员文杰,沈强,张联盟.粉末轧制法制备Fe-6.5%Si硅钢片的研究[J].粉末冶金技术,2007,25(1):32-34.
[32] Zhang Xiang.Rolling and heat-treatment process for fabrication of high silicon steel sheet by powder metallurgy method[D].Wuhan:Wuhan University of Technology,2010(in Chinese).张翔.粉末冶金法制备高硅硅钢片的轧制和热处理工艺研究[D].武汉:武汉理工大学,2010.
[33] Walker E V,Howard J.The production of silicon-iron magnetic strip with the(110)[001]texture,by cold rolling from sintered compacts[J].Powder Metallurgy,1959,4:32-43.
[34] Wang Junjun,Liu Mingjun,Zhou Zhaoyao,et al.Research on metal powder rolling and powder application roll[J].Modern Manufacturing Engineering,2006(11):83-86(in Chinese).王俊君,刘明俊,周照耀,等.金属粉末轧制工艺及装置研究[J].现代制造工程,2006(11):83-86.
[35] Hu Changzheng.Study on fabrieation high Si-content FeSi alloy by powder metallurgy[D].Wuhan:Wuhan University of Technology,2004(in Chinese).胡长征.粉末冶金方法制备高硅铁硅合金的探索性研究[D].武汉:武汉理工大学,2004.
[36] Kong Xianggui.Study on characteristic model of deformation zone in plate and strip warm rolling process[D].Qinhuangdao:Yanshan University,2014(in Chinese).孔祥贵.板带温轧过程变形区特征模型研究[D].秦皇岛:燕山大学,2014.
[37] Qin Jin.Study of high-silicon steel with low core losses and high magnetic flux densities produced by rolling process and its coating[D].Beijing:Beijing University of Science and Technology,2016(in Chinese).秦镜.轧制法制备低铁损高磁感高硅钢及其涂层研究[D].北京:北京科技大学,2016.
[38] Xie Xiekui.High silicon electric steel[J].S&M Electric Machines,1994(3):60-61(in Chinese).谢燮揆.高硅电工钢[J].中小型电机,1994(3):60-61.
[39] Liu Yan,Liang Yongfeng,Ye Feng,et al.Mechanical and magnetic properties of cold rolled 0.02C-6.56Si high silicon steel sheet[J].Special Steel,2007,28(3):28-29(in Chinese).刘艳,梁永锋,叶丰,等.冷轧0.02C-6.56Si高硅钢薄板的力学和磁性能[J].特殊钢,2007,28(3):28-29.
[40] Liang Yongfeng,Lin Junpin,Ye Feng,et al.Effect of heat treatment on microstructure and properties of heavily cold rolled Fe-6.5wt%Si alloy sheet[J].Metallic Functional Materials,2010,17(2):43-47(in Chinese).梁永锋,林均品,叶丰,等.大变形冷轧Fe-6.5%(质量)Si高硅钢薄板组织性能的研究[J].金属功能材料,2010,17(2):43-47.
[41] Qin Jin,Yang Ping,Mao Weimin,et al.Rolling process and texture evolution of 6.4wt%silicon steel with low iron loss and high magnetic induction[J].Journal of Functional Materials,2014,45(10):10133-10137(in Chinese).秦镜,杨平,毛卫民,等.轧制法制备低铁损高磁感6.4%(质量分数)硅钢及其织构演变[J].功能材料,2014,45(10):10133-10137.
[42] Qin Zhuo,Zhu Jun,Wu Jun,et al.Research status and development of the texture evolution of high silicon steel[J].Materials Review,2014,28(11):79-83(in Chinese).秦卓,朱军,吴隽,等.高硅钢织构的研究现状及进展[J].材料导报,2014,28(11):79-83.
[43] Liu Lu,Zhang Ning,Yang Ping,et al.Deformation,recrystallization behaviors and magnetic properties of high silicon steel with an initial near columnar-grained structure[J].Chinese Journal of Engineering,2015,37(7):919-927(in Chinese).刘璐,张宁,杨平,等.高硅钢近柱状晶初始组织的形变、再结晶行为及磁性能[J].工程科学学报,2015,37(7):919-927.
[44] He Zhongzhi.Electric steel[M].Beijing:Metallurgical Industry Press,1996:990-991(in Chinese).何忠治.电工钢[M].北京:冶金工业出版社,1996:990-991.
[45] Masuda S,Fujita F,Murakami T,et al.Warm rolling method for high silicon steel strips:US4938049[P].1990-07-03.
[46] Zhang F Q,Luo Z H.Analysis of processing equipment for near-net shape manufacturing technology of materials[J].Advanced Materials Research,2012,572:390-399.
[47] Qian Yulin.The current sistuation of development of the near net shape technique-an application of double-roller strip casting technique in high Si electric steel[J].Shanghai Steel&Iron Research,2002(2):33-39(in Chinese).钱玉麟.近终形技术的开发现状—双辊薄带连铸工艺在高Si电工钢中的应用[J].上海钢研,2002(2):33-39.
[48] Li Bing,Zhang Fengquan.Newest progress in making technique of material near net shaping[J].Hebei Metallurgy,2013(6):51-55(in Chinese).李冰,张凤泉.材料近终成形制造技术的最新进展[J].河北冶金,2013(6):51-55.
[49] Zhang Zhongyu,Zhang Fengquan,Wang Feilong.Development of twin-roll caster technology to produce special alloy thin strip[J].Research on Iron&Steel,2011,39(6):57-62(in Chinese).章仲禹,张凤泉,王飞龙.特种合金双辊薄带连铸生产技术进展[J].钢铁研究,2011,39(6):57-62.
[50] Simon R W,Senk D,Mollers C,et al.State of development of direct strip casting on the Myosotis industrial pilot line[J].Stahl Und Eisen,1997:75-79.
[51] Luo Zhonghan,Wang Ruwu,Zeng Chun,et al.Effects of temper rolling rate on the microstructure,texture and magnetic properties of Fe-6.5%Si thin strip[J].Metallic Functional Materials,2015,22(1):6-10(in Chinese).骆忠汉,汪汝武,曾春,等.平整轧制量对6.5%Si硅钢薄带组织和织构及磁性能的影响[J].金属功能材料,2015,22(1):6-10.
[52] Luo Zhonghan,Zhang Fengquan,Liu Zhenyu,et al.Influence of warm rolling temperature on microstructure,texture and magnetic properties of Fe-6.5%Si thin strip[J].Research on Iron&Steel,2015,43(3):35-38(in Chinese).骆忠汉,张凤泉,刘振宇,等.温轧温度对Fe-6.5%Si薄板组织、织构和磁性的影响[J].钢铁研究,2015,43(3):35-38.
[53] Zhang Fengquan,Liu Zhenyu,Luo Zhonghan,et al.Microstructure and properties of 6.5%Si Steel thin strip produced through twin-roll continuous casting process[J].Wisco Technology,2015,53(3):20-24(in Chinese).张凤泉,刘振宇,骆忠汉,等.双辊连铸制备6.5%Si硅钢薄带的组织与性能[J].武钢技术,2015,53(3):20-24.
[54] Zhang Fengquan,Wang Ruwu,Luo Zhonghan,et al.Research progress in the preparation of high silicon steel thin strip by near net shaping[J].Materials Protection,2016,49(S1):127-130(in Chinese).张凤泉,汪汝武,骆忠汉,等.近终成形制备高硅钢薄带的研究进展[J].材料保护,2016,49(S1):127-130.
[55] Zapuskalov N M.Thin strip quality obtained in twin-roll casting[J].Cast Metals,1996,9(1):45-49.
[56] Büchner A R,Schmitz J W.Thin-strip casting of steel with a twin-roll caster-discussion of product defects of approx 1mm-Fe6%Si-strips[J].Steel Research,1992,63(1):7-11.
[57] Yang Jinsong,Xie Jianxin,Zhou Cheng.Current status and future prospect for continuous casting of near net shape[J].Materials Review,2002(12):9-11(in Chinese).杨劲松,谢建新,周成.近终形连铸技术的研究现状与发展[J].材料导报,2002(12):9-11.
[58] Yuan Wenjie.Study on the process and principle of powder rolling technology for preparation of high silicon steel sheets[D].Wuhan:Wuhan University of Technology,2007(in Chinese).员文杰.粉末轧制法制备高硅硅钢片的工艺及过程原理的研究[D].武汉:武汉理工大学,2007.
[59] Arai K,Ohmori K,Satoh T,et al.Very low core loss high silicon-iron ribbons[J].IEEE Transactions on Magnetics,1987,23(5):3221-3226.
[60] Wang Dong.Characteristics and application of high silicon electrical steel[J].Research on Iron&Steel,2001(4):42-45(in Chinese).王东.高硅电工钢的特性及应用[J].钢铁研究,2001(4):42-45.
[61] Cunningham J,Darby R,Lane D H,et al.Processing of6.5-percent Si-Fe sheet and tape[J].Magnetics IEEE Transactions on,1970,6(1):39-39.
[2] Long Qiong.Preparing of Fe-Si coating by composite electro-deposition in magnetic field[D].Shanghai:Shanghai University,2014(in Chinese).龙琼.磁场下复合电沉积法制备Fe-Si镀层的基础研究[D].上海:上海大学,2014.
[3] Zheng Xin,Yan Biao.Properties and preparation techniques of Fe-6.5%Si high silicon steel[J].Materials Review,2012,26(19):392-396(in Chinese).郑鑫,严彪.Fe-6.5%Si高硅钢的性能及制备技术[J].材料导报,2012,26(19):392-396.
[4] Ma H L,Li Y,Geng Z R.Preparation of high silicon steel by multi-arc ion coating and diffusion[J].Rare Metal Materials&Engineering,2015,44(10):2373-2375.
[5] Matsumura S,Tanaka Y,Koga Y,et al.Concurrent ordering and phase separation in the vicinity of the metastable critical point of order-disorder transition in Fe-Si alloys[J].Materials Science&Engineering A,2001,312(1-2):284-292.
[6] Jang P,Lee B.Order-disorder transition and magnetic properties of Fe-6.5Si alloy powder cores[J].Physica Status Solidi,2007,204(12):4108-4112.
[7] Viala B,Degauque J,Baricco M,et al.Study of the brittle behaviour of annealed Fe-6.5wt%Si ribbons produced by planar flow casting[J].Materials Science&Engineering A,1996,212(1):62-68.
[8] Haiji H,Okada K,Hiratani T,et al.Magnetic properties and workability of 6.5%Si steel sheet[J].Journal of Magnetism&Magnetic Materials,1996,160(7):109-114.
[9] Lin Junpin,Ye Feng,Chen Guoliang,et al.Fabrication technology, microstructures and properties of Fe-6.5wt.%Si alloy sheets by cold rolling[J].Frontier Science,2007(2):13-26(in Chinese).林均品,叶丰,陈国良,等.6.5wt%Si高硅钢冷轧薄板制备工艺、结构和性能[J].前沿科学,2007(2):13-26.
[10] Li Hui,Liang Jinglong,Zhao Xiaoping,et al.Effect of temperature on diffusion of Si in 1.6Si non-oriented silicon steel during molten salt electro-deposit process[J].Special Steel,2014,35(6):12-14(in Chinese).李慧,梁精龙,赵晓萍,等.熔盐电沉积过程温度对1.6Si无取向硅钢Si扩散的影响[J].特殊钢,2014,35(6):12-14.
[11] Ma Hailin,Liu Xi,Xia Rongbin,et al.Fabrication of high-Si steel by vacuum thermal diffusion of sputtered Fe-Si multilayers[J].Chinese Journal of Vacuum Science and Technology,2016,36(2):154-158(in Chinese).马海林,刘曦,夏荣斌,等.双靶直流溅射多层膜的叠加结构对沉积扩散法制备高硅钢硅含量的影响[J].真空科学与技术学报,2016,36(2):154-158.
[12] Takada Y,Abe M,Masuda S,et al.Commercial scale production of Fe-6.5wt.%Si sheet and its magnetic[J].Journal of Applied Physics,1988,64(10):5367-5369.
[13] Li Qi.Low temperature plastic and rolling of Fe-6.5wt.%Si high silicon steel[D].Shenyang:Northeastern University,2009(in Chinese).李其.Fe-6.5wt.%Si低温塑性与轧制法制备[D].沈阳:东北大学,2009.
[14] Narita K,Enokizono M.Effect of nickel and manganese addition on ductility and magnetic properties of 6.5%silicon-iron alloy[J].IEEE Transactions on Magnetics,1978,14(4):258-262.
[15] Glezer A,Maleeva I,Zakharov A.Influence of alloy elements on the plasticity of high-silicon iron[J].Metal Science&Heat Treatment,1985,27(12):908-912.
[16] Lizzi T,Narasimhan K,Dulis E.The development of Goss texture in Fe-6.5%-2%Ni[J].IEEE transactions on magnetics,1986,22(5):499-501.
[17] Ferrando L,Lebourg C,Ferrara E,et al.Effect of stress on magnetic losses and role of Mn addition in FeSi rapidly solidified ribbons[J].Journal of Magnetism&Magnetic Materials,2000,215:127-129.
[18] Barros J,Ros-Ya1ez T,Vandenbossche L,et al.The effect of Si and Al concentration gradients on the mechanical and magnetic properties of electrical steel[J].Journal of Magnetism&Magnetic Materials,2005,s290-291(290):1457-1460.
[19] Huang Y,Yuan W,Qiao Z,et al.A thermo-dynamic study of the DO3-ordered intermetallic compound Fe3Al[J],Journal of Alloys&Compounds,2008,458:277-281.
[20] Bolfarini C,Silva M C A,Jr A M J,et al.Magnetic properties of spray-formed Fe-6.5%Si and Fe-6.5%Si-1.0%Al after rolling and heat treatment[J].Journal of Magnetism&Magnetic Materials,2008,320:653-656.
[21] Pan Limei,Kim Kilnam,Lin Junpin,et al.Experimental study on the influence of boron on mechanical properties of the Fe-6.5wt%Si alloys[J].Journal of Functional Materials,2004,35(6):683-685(in Chinese).潘丽梅,金吉男,林均品,等.硼元素对Fe-6.5%Si(质量分数)合金力学性能影响的试验研究[J].功能材料,2004,35(6):683-685.
[22] Kim K N,Pan L M,Lin J P,et al.The effect of boron content on the processing for Fe-6.5wt%Si electrical steel sheets[J].Journal of Magnetism&Magnetic Materials,2004,277:331-336.
[23] Wang Xu.Research of manufacturing process of high silicon steel by CVD method[D].Shanghai:East China University of Science and Technology,2013(in Chinese).王旭.CVD法制备高硅钢的工艺过程研究[D].上海:华东理工大学,2013.
[24] Sakai T,Suzuki Y,Shimosato S,et al.Magnetic properties of Fe-Si alloys by powder metallurgy[J].IEEE Transactions on Magnetics,1977,13(5):1445-1447.
[25] Wang W F.Rolling compaction,magnetic properties,and microstructural development during sintering of FeSi[J].Powder Metallurgy,1995,38(4):289-293.
[26] Kusaka K,Imaoka T,Kondo T.Relationship between magnetic properties and Si-content/sintering conditions of Fe-Si type magnetic alloys[J].Journal of the Japan Society of Powder&Powder Metallurgy,2000,47(2):195-202.
[27] Tang N W,Zhong Y B,Sun Z Q,et al.Preparing high silicon steel by sintering Fe-6.5%Si powder compacts in magnetic field[J].Journal of Iron&Steel Research(International),2012(s1):455-458.
[28] Shen Q,Zhou Y,Li J G,et al.Sintering behavior of FeSi composite powder by DPR technique[J].Key Engineering Materials,2007,336-338:2344-2346.
[29] Qu X H,Gowri S,John A.Sintering behavior and strength of Fe-Si-P compacts[J].International Journal of Powder Metallurgy,1991,27(1):9-13.
[30] Li R,Shen Q,Zhang L,et al.Magnetic properties of high silicon iron sheet fabricated by direct powder rolling[J].Journal of Magnetism&Magnetic Materials,2004,281(2-3):135-139.
[31] Yuan Wenjie,Shen Qiang,Zhang Lianmeng.Research on Fe-6.5%Si silicon steel produced by powder rolling technique[J].Powder Metallurgy Technology,2007,25(1):32-34(in Chinese).员文杰,沈强,张联盟.粉末轧制法制备Fe-6.5%Si硅钢片的研究[J].粉末冶金技术,2007,25(1):32-34.
[32] Zhang Xiang.Rolling and heat-treatment process for fabrication of high silicon steel sheet by powder metallurgy method[D].Wuhan:Wuhan University of Technology,2010(in Chinese).张翔.粉末冶金法制备高硅硅钢片的轧制和热处理工艺研究[D].武汉:武汉理工大学,2010.
[33] Walker E V,Howard J.The production of silicon-iron magnetic strip with the(110)[001]texture,by cold rolling from sintered compacts[J].Powder Metallurgy,1959,4:32-43.
[34] Wang Junjun,Liu Mingjun,Zhou Zhaoyao,et al.Research on metal powder rolling and powder application roll[J].Modern Manufacturing Engineering,2006(11):83-86(in Chinese).王俊君,刘明俊,周照耀,等.金属粉末轧制工艺及装置研究[J].现代制造工程,2006(11):83-86.
[35] Hu Changzheng.Study on fabrieation high Si-content FeSi alloy by powder metallurgy[D].Wuhan:Wuhan University of Technology,2004(in Chinese).胡长征.粉末冶金方法制备高硅铁硅合金的探索性研究[D].武汉:武汉理工大学,2004.
[36] Kong Xianggui.Study on characteristic model of deformation zone in plate and strip warm rolling process[D].Qinhuangdao:Yanshan University,2014(in Chinese).孔祥贵.板带温轧过程变形区特征模型研究[D].秦皇岛:燕山大学,2014.
[37] Qin Jin.Study of high-silicon steel with low core losses and high magnetic flux densities produced by rolling process and its coating[D].Beijing:Beijing University of Science and Technology,2016(in Chinese).秦镜.轧制法制备低铁损高磁感高硅钢及其涂层研究[D].北京:北京科技大学,2016.
[38] Xie Xiekui.High silicon electric steel[J].S&M Electric Machines,1994(3):60-61(in Chinese).谢燮揆.高硅电工钢[J].中小型电机,1994(3):60-61.
[39] Liu Yan,Liang Yongfeng,Ye Feng,et al.Mechanical and magnetic properties of cold rolled 0.02C-6.56Si high silicon steel sheet[J].Special Steel,2007,28(3):28-29(in Chinese).刘艳,梁永锋,叶丰,等.冷轧0.02C-6.56Si高硅钢薄板的力学和磁性能[J].特殊钢,2007,28(3):28-29.
[40] Liang Yongfeng,Lin Junpin,Ye Feng,et al.Effect of heat treatment on microstructure and properties of heavily cold rolled Fe-6.5wt%Si alloy sheet[J].Metallic Functional Materials,2010,17(2):43-47(in Chinese).梁永锋,林均品,叶丰,等.大变形冷轧Fe-6.5%(质量)Si高硅钢薄板组织性能的研究[J].金属功能材料,2010,17(2):43-47.
[41] Qin Jin,Yang Ping,Mao Weimin,et al.Rolling process and texture evolution of 6.4wt%silicon steel with low iron loss and high magnetic induction[J].Journal of Functional Materials,2014,45(10):10133-10137(in Chinese).秦镜,杨平,毛卫民,等.轧制法制备低铁损高磁感6.4%(质量分数)硅钢及其织构演变[J].功能材料,2014,45(10):10133-10137.
[42] Qin Zhuo,Zhu Jun,Wu Jun,et al.Research status and development of the texture evolution of high silicon steel[J].Materials Review,2014,28(11):79-83(in Chinese).秦卓,朱军,吴隽,等.高硅钢织构的研究现状及进展[J].材料导报,2014,28(11):79-83.
[43] Liu Lu,Zhang Ning,Yang Ping,et al.Deformation,recrystallization behaviors and magnetic properties of high silicon steel with an initial near columnar-grained structure[J].Chinese Journal of Engineering,2015,37(7):919-927(in Chinese).刘璐,张宁,杨平,等.高硅钢近柱状晶初始组织的形变、再结晶行为及磁性能[J].工程科学学报,2015,37(7):919-927.
[44] He Zhongzhi.Electric steel[M].Beijing:Metallurgical Industry Press,1996:990-991(in Chinese).何忠治.电工钢[M].北京:冶金工业出版社,1996:990-991.
[45] Masuda S,Fujita F,Murakami T,et al.Warm rolling method for high silicon steel strips:US4938049[P].1990-07-03.
[46] Zhang F Q,Luo Z H.Analysis of processing equipment for near-net shape manufacturing technology of materials[J].Advanced Materials Research,2012,572:390-399.
[47] Qian Yulin.The current sistuation of development of the near net shape technique-an application of double-roller strip casting technique in high Si electric steel[J].Shanghai Steel&Iron Research,2002(2):33-39(in Chinese).钱玉麟.近终形技术的开发现状—双辊薄带连铸工艺在高Si电工钢中的应用[J].上海钢研,2002(2):33-39.
[48] Li Bing,Zhang Fengquan.Newest progress in making technique of material near net shaping[J].Hebei Metallurgy,2013(6):51-55(in Chinese).李冰,张凤泉.材料近终成形制造技术的最新进展[J].河北冶金,2013(6):51-55.
[49] Zhang Zhongyu,Zhang Fengquan,Wang Feilong.Development of twin-roll caster technology to produce special alloy thin strip[J].Research on Iron&Steel,2011,39(6):57-62(in Chinese).章仲禹,张凤泉,王飞龙.特种合金双辊薄带连铸生产技术进展[J].钢铁研究,2011,39(6):57-62.
[50] Simon R W,Senk D,Mollers C,et al.State of development of direct strip casting on the Myosotis industrial pilot line[J].Stahl Und Eisen,1997:75-79.
[51] Luo Zhonghan,Wang Ruwu,Zeng Chun,et al.Effects of temper rolling rate on the microstructure,texture and magnetic properties of Fe-6.5%Si thin strip[J].Metallic Functional Materials,2015,22(1):6-10(in Chinese).骆忠汉,汪汝武,曾春,等.平整轧制量对6.5%Si硅钢薄带组织和织构及磁性能的影响[J].金属功能材料,2015,22(1):6-10.
[52] Luo Zhonghan,Zhang Fengquan,Liu Zhenyu,et al.Influence of warm rolling temperature on microstructure,texture and magnetic properties of Fe-6.5%Si thin strip[J].Research on Iron&Steel,2015,43(3):35-38(in Chinese).骆忠汉,张凤泉,刘振宇,等.温轧温度对Fe-6.5%Si薄板组织、织构和磁性的影响[J].钢铁研究,2015,43(3):35-38.
[53] Zhang Fengquan,Liu Zhenyu,Luo Zhonghan,et al.Microstructure and properties of 6.5%Si Steel thin strip produced through twin-roll continuous casting process[J].Wisco Technology,2015,53(3):20-24(in Chinese).张凤泉,刘振宇,骆忠汉,等.双辊连铸制备6.5%Si硅钢薄带的组织与性能[J].武钢技术,2015,53(3):20-24.
[54] Zhang Fengquan,Wang Ruwu,Luo Zhonghan,et al.Research progress in the preparation of high silicon steel thin strip by near net shaping[J].Materials Protection,2016,49(S1):127-130(in Chinese).张凤泉,汪汝武,骆忠汉,等.近终成形制备高硅钢薄带的研究进展[J].材料保护,2016,49(S1):127-130.
[55] Zapuskalov N M.Thin strip quality obtained in twin-roll casting[J].Cast Metals,1996,9(1):45-49.
[56] Büchner A R,Schmitz J W.Thin-strip casting of steel with a twin-roll caster-discussion of product defects of approx 1mm-Fe6%Si-strips[J].Steel Research,1992,63(1):7-11.
[57] Yang Jinsong,Xie Jianxin,Zhou Cheng.Current status and future prospect for continuous casting of near net shape[J].Materials Review,2002(12):9-11(in Chinese).杨劲松,谢建新,周成.近终形连铸技术的研究现状与发展[J].材料导报,2002(12):9-11.
[58] Yuan Wenjie.Study on the process and principle of powder rolling technology for preparation of high silicon steel sheets[D].Wuhan:Wuhan University of Technology,2007(in Chinese).员文杰.粉末轧制法制备高硅硅钢片的工艺及过程原理的研究[D].武汉:武汉理工大学,2007.
[59] Arai K,Ohmori K,Satoh T,et al.Very low core loss high silicon-iron ribbons[J].IEEE Transactions on Magnetics,1987,23(5):3221-3226.
[60] Wang Dong.Characteristics and application of high silicon electrical steel[J].Research on Iron&Steel,2001(4):42-45(in Chinese).王东.高硅电工钢的特性及应用[J].钢铁研究,2001(4):42-45.
[61] Cunningham J,Darby R,Lane D H,et al.Processing of6.5-percent Si-Fe sheet and tape[J].Magnetics IEEE Transactions on,1970,6(1):39-39.