在热轧产品Q345B中出现批量的横向唇状疤块缺陷裂纹,利用金相显微镜观察带钢的微观组织,分析现场生产的实际情况与试验数据,对热轧产品Q345B表面唇状疤块缺陷的形成原因进行了分析,发现唇状疤块缺陷裂纹处附近的组织晶粒存在较大差异,且缺陷的产生与轧制过程的冷却不均有关。
In the hot rolled product Q345 B,transverse lip-like scar cracks appeared in batch.The microstructure of the strip was observed by metallographic microscope,and the actual situation of the on-the-spot production and test data were analyzed.The formation of lip scar defects on the surface of hot rolled Q345 B was analyzed.It was found that there were great differences in the microstructure grains near the defects in the hot rolled Q345 B,and the defects were related to the inhomogeneity of cooling during rolling.