煤焦油沥青基炭材料的研究进展
|
摘要
我国煤沥青面临加工技术水平落后、附加值低的困境,如何提高沥青产品的经济价值非常重要。本文概述了沥青的基本性质,并重点介绍了活性炭、泡沫炭、炭纤维、碳量子点和包覆沥青的研究进展。并指出炭材料产品虽已经获得了广泛的应用,但是原料沥青的改性调控对产品的性能至关重要,需要系统地研究开发煤沥青分子调控技术。
How to improve the economic value of bitumen products is very important in China because of the backward processing technology and the low added value for coal tar pitches. This paper summarized the fundamental properties and solvent composition of the coal tar pitches, and focused on the preparations of activated carbon, carbon foam, carbon fiber, carbon quantum dots, and coating pitch with coal tar pitch as precursors. It is put forth that modification for pitches has great effect on the performance of pitch-based products, so the research and development techniques for pitch molecule modifications are essential.
How to improve the economic value of bitumen products is very important in China because of the backward processing technology and the low added value for coal tar pitches. This paper summarized the fundamental properties and solvent composition of the coal tar pitches, and focused on the preparations of activated carbon, carbon foam, carbon fiber, carbon quantum dots, and coating pitch with coal tar pitch as precursors. It is put forth that modification for pitches has great effect on the performance of pitch-based products, so the research and development techniques for pitch molecule modifications are essential.
引文
[1]肖南,邱介山.煤沥青基功能炭材料的研究现状及前景[J].化工进展, 2016, 35(6):1804-1811.
[2]花双平.煤沥青基中间相沥青的制备与性能研究[D].北京:北京化工大学, 2010.
[3]王晓瑞,金鸣林,郑玉丽.煤沥青预处理工艺对活性炭孔结构的影响[J].煤炭转化, 2004, 27(4):59-63.
[4]金鸣林,郑玉丽,王晓瑞.煤沥青热聚合过程对微孔炭特性的影响[J].材料导报, 2007, 21(2):137-140.
[5]王晓瑞,金鸣林.炭素前驱体性质对活性炭比表面积的影响[J].煤炭转化, 2006, 29(3):68-70.
[6]朱由余,陈明鸣,杨斌,等.沥青树脂基复合球形活性炭的制备及研究[J].材料导报, 2015, 29(10):39-42.
[7]王云龙,张生万,杜文,等.沥青活性炭的制备方法[J].新型炭材料, 2006, 21(4):369-373.
[8]王耀斌.一种沥青活性炭的制备方法[P]. CN105565318A,2016.
[9]李开喜.一种高导热性沥青基球状活性炭的制备方法[P]. CN106348290A,2017-01-25.
[10]伍孝,李于,鲍烈华.一种球状活性炭及其制备方法[P].CN104030287A,2014-09-10.
[11]钟继鸣,王新营,郁铭芳,等.石墨化碳泡沫导热性能研究[J].材料导报, 2006, 20(s1):268-270.
[12]陈秀男.泡沫炭及其导热复合材料的制备和性能研究[D].上海:东华大学, 2012.
[13]陈秀男,吕永根,蒋俊祺.低温低压下发泡制备泡沫炭的结构与性能研究[J].当代化工, 2013(2):131-134.
[14]周萍.煤焦油净化制备泡沫炭[D].贵阳:贵州大学,2016.
[15]James Klett, Rommie Hardy, Ernie Romine,et al. Highthermal-conductivity, mesophase-pitch-derived carbon foams:effect of precursor on structure and properties[J].Carbon,2000,38(7):953-973.
[16]陈石林,段桂英,卢梦哲,郭建光,陈林.鳞片石墨/中间相沥青基石墨化泡沫炭的结构与性能研究[J].炭素技术,2018,37(4):43-47.
[17]王春晓.泡沫炭的石墨烯改性及大尺寸结构控制[D].上海:华东理工大学, 2013.
[18]王鹏.超临界流体制备沥青泡沫炭及其结构控制的研究[D].上海:东华大学, 2008.
[19]冯志海,余立琼,樊桢,等.一种高导热石墨泡沫/碳复合材料及其制备方法[P]. CN105272256A,2016-01-27.
[20]于宝军.氧化—缩聚两步法制备煤沥青基纺丝沥青及其性能研究[D].天津:天津大学, 2012.
[21]徐兵,陈胜春,李轩科.煤沥青基同性纺丝沥青的制备及表征[J].煤炭转化, 2016, 39(2):65-68.
[22]夏文丽,陈剑铭,舒欣,等.同步氢化/热缩聚法制备中间相沥青的工艺研究[J].功能材料, 2012, 43(3):367-370.
[23]刘均庆,史景利,魏兴海,等.沥青组分对炭纤维径向结构影响的研究[J].化工新型材料, 2011, 39(12):100-102.
[24]刘均庆,史景利,高晓晴,等.中间相沥青炭纤维径向辐射结构形成机理研究[J].化工新型材料, 2011, 39(2):84-87.
[25]刘安华,姚艳波,舒欣,等.沥青原料对沥青基炭纤维结构与性能的影响[J].功能材料, 2011, 42(6):1119-1122.
[26]黄启同,林小凤,李飞明,等.碳量子点的合成与应用[J].化学进展, 2015, 27(11):1604-1614.
[27]周瑞琪,吕华,陈佳慧,等.碳量子点的合成、表征及应用[J].药学进展, 2013, 37(1):24-30.
[28]李跃辉.煤沥青基碳量子点的制备及荧光检测中的应用[D].大连:大连理工大学,2017.
[29]孟勋.煤基荧光碳点的制备及其性能调控[D].太原:中北大学, 2017.
[30]吴其修,张万红.用作锂离子电池负极包覆层材料的高软化点沥青及其制备[P]. CN101108918,2008-01-23.
[31]吴其修,刘明东,李佳坤,郭庆.一种制备用于包覆锂离子电池天然石墨负极材料的高软化点沥青的方法[P].CN103897714A,2014-07-02.
[2]花双平.煤沥青基中间相沥青的制备与性能研究[D].北京:北京化工大学, 2010.
[3]王晓瑞,金鸣林,郑玉丽.煤沥青预处理工艺对活性炭孔结构的影响[J].煤炭转化, 2004, 27(4):59-63.
[4]金鸣林,郑玉丽,王晓瑞.煤沥青热聚合过程对微孔炭特性的影响[J].材料导报, 2007, 21(2):137-140.
[5]王晓瑞,金鸣林.炭素前驱体性质对活性炭比表面积的影响[J].煤炭转化, 2006, 29(3):68-70.
[6]朱由余,陈明鸣,杨斌,等.沥青树脂基复合球形活性炭的制备及研究[J].材料导报, 2015, 29(10):39-42.
[7]王云龙,张生万,杜文,等.沥青活性炭的制备方法[J].新型炭材料, 2006, 21(4):369-373.
[8]王耀斌.一种沥青活性炭的制备方法[P]. CN105565318A,2016.
[9]李开喜.一种高导热性沥青基球状活性炭的制备方法[P]. CN106348290A,2017-01-25.
[10]伍孝,李于,鲍烈华.一种球状活性炭及其制备方法[P].CN104030287A,2014-09-10.
[11]钟继鸣,王新营,郁铭芳,等.石墨化碳泡沫导热性能研究[J].材料导报, 2006, 20(s1):268-270.
[12]陈秀男.泡沫炭及其导热复合材料的制备和性能研究[D].上海:东华大学, 2012.
[13]陈秀男,吕永根,蒋俊祺.低温低压下发泡制备泡沫炭的结构与性能研究[J].当代化工, 2013(2):131-134.
[14]周萍.煤焦油净化制备泡沫炭[D].贵阳:贵州大学,2016.
[15]James Klett, Rommie Hardy, Ernie Romine,et al. Highthermal-conductivity, mesophase-pitch-derived carbon foams:effect of precursor on structure and properties[J].Carbon,2000,38(7):953-973.
[16]陈石林,段桂英,卢梦哲,郭建光,陈林.鳞片石墨/中间相沥青基石墨化泡沫炭的结构与性能研究[J].炭素技术,2018,37(4):43-47.
[17]王春晓.泡沫炭的石墨烯改性及大尺寸结构控制[D].上海:华东理工大学, 2013.
[18]王鹏.超临界流体制备沥青泡沫炭及其结构控制的研究[D].上海:东华大学, 2008.
[19]冯志海,余立琼,樊桢,等.一种高导热石墨泡沫/碳复合材料及其制备方法[P]. CN105272256A,2016-01-27.
[20]于宝军.氧化—缩聚两步法制备煤沥青基纺丝沥青及其性能研究[D].天津:天津大学, 2012.
[21]徐兵,陈胜春,李轩科.煤沥青基同性纺丝沥青的制备及表征[J].煤炭转化, 2016, 39(2):65-68.
[22]夏文丽,陈剑铭,舒欣,等.同步氢化/热缩聚法制备中间相沥青的工艺研究[J].功能材料, 2012, 43(3):367-370.
[23]刘均庆,史景利,魏兴海,等.沥青组分对炭纤维径向结构影响的研究[J].化工新型材料, 2011, 39(12):100-102.
[24]刘均庆,史景利,高晓晴,等.中间相沥青炭纤维径向辐射结构形成机理研究[J].化工新型材料, 2011, 39(2):84-87.
[25]刘安华,姚艳波,舒欣,等.沥青原料对沥青基炭纤维结构与性能的影响[J].功能材料, 2011, 42(6):1119-1122.
[26]黄启同,林小凤,李飞明,等.碳量子点的合成与应用[J].化学进展, 2015, 27(11):1604-1614.
[27]周瑞琪,吕华,陈佳慧,等.碳量子点的合成、表征及应用[J].药学进展, 2013, 37(1):24-30.
[28]李跃辉.煤沥青基碳量子点的制备及荧光检测中的应用[D].大连:大连理工大学,2017.
[29]孟勋.煤基荧光碳点的制备及其性能调控[D].太原:中北大学, 2017.
[30]吴其修,张万红.用作锂离子电池负极包覆层材料的高软化点沥青及其制备[P]. CN101108918,2008-01-23.
[31]吴其修,刘明东,李佳坤,郭庆.一种制备用于包覆锂离子电池天然石墨负极材料的高软化点沥青的方法[P].CN103897714A,2014-07-02.