摘要
用恒粘剂盐酸羟胺(HH)对天然橡胶(NR)杯凝胶进行恒粘改性,研究HH质量分数对NR性能的影响,并探究恒粘NR在V带底胶中的应用性能。结果表明:通过改变HH质量分数可以制备门尼粘度不同的恒粘NR;HH改性的恒粘NR生胶的弹性模量减小,损耗因子增大;恒粘NR制备的V带底胶不仅加工性能改善,硫化速率增大,密炼能耗降低,生产效率提高,而且物理性能、耐屈挠性能和炭黑分散性提高;用质量分数为0.005的HH改性的恒粘NR制备的V带底胶拉伸强度最高,耐屈挠性能最好。
Constant viscosity modification of natural rubber(NR) cup lump with viscosity stabilizer hydroxylamine hydrochloride(HH) was investigated. The effect of HH mass fraction on NR performance and the application of constant viscosity NR in V-belt base rubber were studied. The results showed that,the constant viscosity NR with different Mooney viscosity could be prepared by changing the HH mass fraction.The elastic modulus of constant viscosity raw NR modified by HH decreased,and the loss factor increased. The processability of the V-belt base rubber prepared by constant viscosity NR modified by HH was improved,the vulcanization speed increased,mixing energy consumption was reduced,production efficiency was improved,and the physical properties,flexing resistance and carbon black dispersion were improved. The V-belt base rubber with constant viscosity NR modified by HH with the mass fraction of 0.005 had the highest tensile strength and the best flexing resistance.
引文
[1]李金风.凝胶片悬挂贮存对NR性能的影响[D].海口:海南大学,2013.
[2]杨清芝.实用橡胶工艺学[M].北京:化学工业出版社,2005:4.
[3]李志君,赵艳芳.恒黏天然橡胶理化性能的研究[J].弹性体,2002,12(5):10-13.
[4]杨全运,符永胜.天然橡胶门尼黏度的调控技术[J].热带农业工程,2003(2):13-15.
[5]杨可喜,叶兴泉.几种天然橡胶恒黏剂恒黏特性的研究[J].推进技术,1991,12(6):50-54.
[6]段志松.新型恒黏剂MT对天然橡胶性能及其硫化动力学的影响研究[D].海口:海南大学,2012.
[7]王永周,张北龙,黄茂芳,等.恒黏剂对恒黏天然橡胶生胶分子结构及动态力学性能的影响[J].合成橡胶工业,2013,36(5):369-371.
[8]孙东华,赵丽春.羰基试剂对NR恒粘效果的研究[J].广东化工,2006,33(7):28-29.
[9]王永周,张北龙,黄红海,等.恒粘剂硫酸联胺对天然橡胶硫化特性的影响[J].橡胶工业,2016,63(1):27-30.
[10]段志松,廖建和,廖禄生,等.恒粘剂2-巯基苯并噻唑对天然橡胶性能的影响[J].橡胶工业,2013,60(5):279-283.
[11]钱寒东,贺炅皓,邵红琪.恒粘剂OPRHAZ对天然橡胶性能的影响[J].橡胶工业,2015,13(8):13-17.
[12]潘俊任,黎燕飞,桂红星,等.新型保存剂HY在低氨浓缩天然胶乳中的应用研究[J].广东化工,2017,44(9):116-117.
[13]唐淼.聚合物弹性体材料网络结构对流变学行为和力学性能影响的研究[D].合肥:中国科学技术大学,2017.
[14]张会丰,蒋冰清,赵富春,等.NR贮存过程中分子交联网络分析[J].热带作物学报,2017,38(5):939-944.
[15]邹玉荣.天然橡胶分子量与炭黑分散性对天然橡胶/炭黑复合胶料动态性能的影响[D].青岛:青岛科技大学,2013.