摘要
窑皮对延长危险废物焚烧回转窑耐火砖寿命有非常关键的作用,耐火砖所占的比例特别大,如果掉窑砖造成停窑,火砖的费用不算,产量的损失更大。文章通过对挂窑皮所需物料化学成分、烧成温度和火焰控制、喂料量和窑速等因素进行研究,并对生料熔渣进行分析,探索出最佳窑皮建立工艺。
Adhering coating is very critical to extend the service time of refractory bricks of rotary kiln. When some refractory bricks dropped, the loss of production is huge except the price of refractory bricks. In the paper the optimum technology of adhering coating were obtained by studying chemical component of material used to adhering coating, firing temperature of coating, flame control, feeding quantity and speed of rotary kiln. In addition, raw material and slag were analyzed.
引文
[1]张绍坤.回转窑处理危险废物的工程应用[J].工业炉,2010,32(2):26-29,
[2]张绍坤.回转窑处理危险废物的工程设计[J].冶金设备,2010,(2):58-62.
[3]游铭金.危险废物回转窑焚烧处理工艺探讨[J].中国高新技术企业,2014,(21):71-73.
[4]周冠东.窑皮的作用及影响因素[J].河南建材,2010,(5):138.
[5]周伟,韩忠毅,王凌龙,等.水泥回转窑耐火砖挂窑皮评价方法[N].中国建材报,2013-10-22(8).
[6]谢克平.预分解窑如何挂牢和维护窑皮[J].水泥,2012,(9):18-19.
[7]曾大凡,张用宾.水泥窑烧成带用砖的“挂窑皮性能”[N].中国建材报,2013-12-31(8).
[8]张东伟,杨红芬,高明智.危险废物回转窑焚烧系统工程概述[J].中国环保产业,2010,(10):56-58.
[9]孙夏明.回转窑筒体的热应力分析[J].有色设备,1992,(6):27-30.
[10]赵林茂.一次红窑事故的原因分析及处理措施[J].水泥,2014,(5):33.
[11]刘刚.典型危险废物回转窑热处置特性和技术研究[D].浙江大学,2006.
[12]刘刚,池涌,蒋旭光,等.模拟危险废物颗粒回转窑内运动特性试验研究[J].工程热物理学报,2005,26(2):343-346.
[13]赵娟,周纳,刘晓娟.浅谈保护窑皮的措施[J].中国水泥,2013,(7):87.
[14]孙伟卿.浅谈影响窑皮的因素及解决措施[J].新世纪水泥导报,2006,12(1):17-19