以棒状和针状两种晶型的紫钨为原料,制备了超细钨粉及超细碳化钨粉。采用扫描电镜、比表面仪、激光粒度分布仪和X射线衍射仪等对粉末进行分析,研究了棒状紫钨和针状紫钨对超细碳化钨粉粒度的影响。结果表明,以针状紫钨为原料能制备粒度更细的优质超细碳化钨粉。
Using rod-shaped and needle-shaped violet tungsten oxides as raw materials,ultra-fine tungsten powders and ultra-fine tungsten carbide powders were prepared.The effects of rod-shaped and needleshaped violet tungsten oxides on particle size of ultra-fine tungsten carbide powders were studied by using scanning electron microscope,specific surface meter,laser particle size distribution analyzer and X-ray diffractometer.The results show that high-quality ultra-fine tungsten carbide powder with finer particle size can be prepared by using needle-shaped violet tungsten oxide as the raw material.
引文
[1]姜文伟,陈响明.氧化钨微观结构的研究[J].稀有金属与硬质合金,2009,37(3):8-11.
[2]陈绍衣.超细钨粉、碳化钨粉研制方法的述评——推荐用传统流程生产超细碳化钨粉[J].中国钨业,1999,14(5/6):146-149.
[3]廖寄乔,黄志锋,吕海波,等.不同氧化钨氢还原制取超细钨粉[J].中南大学学报(自然科学版),2000,31(1):51-55.
[4]陈绍衣.紫色氧化钨制取钨粉[J].中南矿冶学院学报,1994(5):607-611.
[5]彭泽辉,李玲.紫色氧化钨制取工艺的研究及其应用[J].稀有金属与硬质合金,2003,31(2):8-11.
[6]张秋和,谢中华,陈树茂,等.超细碳化钨粉工业生产实践[J].中国钨业,2009,24(6):32-34.
[7]宋志华,郭亨群,吴冲浒,等.以紫钨为原料制备纳米钨粉体的研究[J].稀有金属材料与工程,2011,40(12):2 216-2 220.