针对高压气瓶锻造收口裂纹问题,从影响锻造收口的主要因素入手,分析引起裂纹的原因,并提出解决措施。通过实际操作,验证了解决措施的正确性,避免了高压气瓶锻造收口裂纹问题。
In view of the problem of forging cracks at necked-in section in high-pressure bottle,proceeding with the major factor affecting forging of the necked-in section, the causes of cracks were analyzed and countermeasures were proposed. Through the actual operation, the correctness of the countermeasures was verified, and the problem of forging crack defects at necked-in section in high-pressure bottle was eliminated.