采用溶胶-凝胶法制备出了CaSiO_3:Eu~(3+),主要研究Eu~(3+)在CaSiO_3中的发光机理及它们浓度变化对其光谱性质的影响.
CaSiO_3:Eu~(3+)were prepared by means of Sol-Gel method and researched the luninescence properties of CaSiO_3:Eu~(3+).
引文
[1]Porcher P,Caro P.Crystal Field Parameters for Eu3+in KY3F10 Intensity Parameters[J]. J Chem phys,1978,68(9):4176-4187.
[2]Brecher C.Europium in the Ultraphosphate Lattice:Polarized Spectra and Structure of Eu P5O14[J]. The Journal of Chemical Physics,1974,61(6):2297-2315.
[3]wu Changfeng,QIN Weiping,et al. Photoluminescence from Surfactant-assembled Y2O3:Eu Nanotubes[J].Appl Phys Lett,2003,82(4):520-522.
[4]Dexpert-Ghys J,Mauricotr,Facueher M D. Spectroscopy of Eu3+Ions in Monazite Type Lanthanide Orthophosphates Ln PO4,Ln=La and Eu[J]. J Lumin,1996(59):203-215.
[5]Bihart B,Eilers H,Tissue B M.Spectra and Dynamics of Eu2O3and Eu3+:Y2O3,Nanocrystals[J].J Lumin,1997(75):1-10.
[6]于立新,曹林,杨殿范,等.CaSiO3Eu的发光性质[J].硅酸盐学报,2003,31(9):900-902.
[7]苏吉益,马宏图,曲明磊,等.b-Tm掺杂钨酸盐纳米晶的制备及发光性能研究[J].吉林化工学院学报,2018(1):51-53.
[8]路大勇.钛酸钡介电陶瓷中变价稀土离子的价态鉴定及缺陷化学的研究进展[J].吉林化工学院学报,2018(7):8-13.
[9]刘文彦,盖啸尘.溶胶-凝胶法制备Ca Si O3Eu3+Bi3+[J].大学物理实验,2017(6):4-6.
[10]袁启霖,郝国豪,吴姝丹,等.共轭荧光分子光子晶体发光材料的可控制备与性能研究[J].大学物理实验,2016(3):5-8.
[11]朱丽丽,林晓敏,陈剑锋.Ce0.8Pr0.2-xNdxO2-δ(x=0.02,0.05,0.1)固溶体的合成与性质研究[J].大学物理实验,2017(3):1-4+42.