40CrMnMoA辊轴锻件缺陷分析
|
摘要
40CrMnMoA辊轴锻件在锻后超声检测过程中发现内部存在连续性的超标缺陷。通过对其超标缺陷部位进行解剖定性分析,结果表明:40CrMnMoA辊轴锻件的缺陷为夹渣,夹渣的主要成分为Al、Si、Ca等元素。
Continuous defects beyond the standard inside of 40 CrMnMoA roll axle forgings have been found out by ultrasonic defection after forging. By conducting anatomical and qualitative analyses on defects position,the result showed that defects of 40 CrMnMoA roll axle forgings belonged to slag inclusion,the main contents included Al,Si,Ca and other elements.
Continuous defects beyond the standard inside of 40 CrMnMoA roll axle forgings have been found out by ultrasonic defection after forging. By conducting anatomical and qualitative analyses on defects position,the result showed that defects of 40 CrMnMoA roll axle forgings belonged to slag inclusion,the main contents included Al,Si,Ca and other elements.
引文
[1]庞钧.大型铸锻件缺陷分析图谱[M].北京:机械工业出版社,1990:64-85.
[2]姜锡山.钢中非金属夹杂物[M].北京:冶金工业出版社,2011:252-253.
[3]徐匡迪,肖丽俊.特殊钢精炼中的脱氧及夹杂物控制[J].钢铁,2012,47(10):1-13.
[4]王恩庆,徐贵林,王少波,等.支承辊用YB-70钢冶炼工艺的研究[J].大型铸锻件,2002(1):21-23.
[5]董立,王亚明,王晓燕,等.降低精炼钢钢中夹杂物的研究[J].大型铸锻件,2012(4):10-14.
[2]姜锡山.钢中非金属夹杂物[M].北京:冶金工业出版社,2011:252-253.
[3]徐匡迪,肖丽俊.特殊钢精炼中的脱氧及夹杂物控制[J].钢铁,2012,47(10):1-13.
[4]王恩庆,徐贵林,王少波,等.支承辊用YB-70钢冶炼工艺的研究[J].大型铸锻件,2002(1):21-23.
[5]董立,王亚明,王晓燕,等.降低精炼钢钢中夹杂物的研究[J].大型铸锻件,2012(4):10-14.