摘要
在利用三层交联型碱溶胀法制备中空苯丙乳胶粒的基础上,采用粒径分析仪、粘度计、扫描电镜(SEM)、透射电镜(TEM)和紫外-可见分光光度计(UV-Vis spectrophotometry)等测试方法考察了壳层厚度对中空乳胶粒结构形态和遮盖性的影响。研究结果表明,壳层的厚度对中空聚合物乳胶粒的形态和遮盖性具有重要影响,随着壳层厚度的增加,乳胶粒粒径先减小后增大,并在壳/中间层包覆核的比值等于7时达到最小值,乳液粘度也一直减小。同时,在壳层厚度增加的过程中,中空聚合物乳胶粒表面粗糙程度逐渐降低,破裂和塌陷的乳胶粒逐渐减少,遮盖性先增强后减弱。壳/中间层包覆核的最佳比值为7~9。
Based on the preparation of hollow styrene-acrylic latex particles by three-layer cross-linking alkali swelling method,in this work the effects of shell thickness on morphology and opacity ability of hollow polymer latex particles were investigated via characterizations of particle size analysis,viscosity measurement,SEM,TEM and UV-Vis spectrophotometry. The results confirmed the significant effect of shell layer thickness on the hollow latex particles. An increasing shell thickness can result in a biphasic(increase → decrease) change in size of the latex particles,which has a minimum value while shell/intermediate layer thickness ratio is 7,and also a monotonically decreasing latex viscosity. Moreover,when the shell thickness increases,the hollow polymer latex particles undergo a decrease of surface roughness,less rupture and collapse,and a"rise and fall"change in opacity ability. The most satisfactory shell/intermediate layer ratio of the latex were determined to be 7—9.
引文
1 Yuan T,Shao Q H,Hu J Q,et al.Journal of Applied Polymer Science,2015,132(30),9229.
2 Ye C,Wen X F,Lan J L,et al.Pigment and Resin Technology,2016,45(1),45.
3 Zhang F,Ma J Z,Xu Q N,et al.Colloids and Surfaces A-Physicochemical and Engineering Aspects,2015,484,325.
4 Wang Z B,Hong Q,Shi Y X,et al.Polymer Science Series B,2015,57(6),600.
5 Samyn P,Deconinck M,Schoukens G,et al.Progress in Organic Coatings,2010,69,442.
6 Bao Y,Ma J Z,Zhang X,et al.Journal of Materials Science,2015,50(21),6839.
7 Huang X Y,Li L X,Xu M,et al.Journal of Applied Polymer Science,2015,132(37),6839.
8 Fang Y J,Deng W,Zuo H,et al.Acta Polymerica Sinica,2015,8,927.
9 Syoufian A,Manako Y,Nakashima K.Powder Technology,2015,280,207.
10 Nakayama S,Fukuhara K,Nakamura Y,et al.Chemistry Letters,2015,44(6),773.
11 Sun N,Zhao X,Xiao Z G,et al.Journal of Nanoscience and Nanotechnology,2015,15(6),4676.
12 Takeoka H,Hamasaki H,Harada Y,et al.Colloid and Polymer Science,2015,293(5),1483.
13 Deng W,Guo H C,Zhang W N,et al.Colloid and Polymer Science,2014,292(10),2687.
14 Jiang Y M,Li B T,Wang W J,et al.Chinese Journal of Polymer Science,2014,32(2),177.
15 Jiang Y M,Li B T,Deng W,et al.Chinese Journal of Polymer Science,2014,32(1),21.
16 Zhang W H,Huang Y,Tian W.Progress in Chemistry,2013,411,41.
17 Kong X Z,Jiang W Q,Jiang X B,et al.Polymer Chemistry,2013,24(4),5776.
18 Zhao Y L,Yin G N,Zheng Z,et al.Journal of Polymer Science Part A:Polymer Chemistry,2011,49(24),5257.
19 Mc Donald C J,Devon M J.Advances in Colloid and Interface Science,2002,99(3),181.
20 Pavlyuchenko V N,Sorochinskaya O V,Ivanchev S S,et al.Polymer Science,2001,39(9),1435.