摘要
研究了常化工艺对CSP流程生产无取向电工钢35W440的组织、织构及电磁性能影响规律,结果表明:在常化温度为900~960℃范围内,随着常化温度提高,铁损P1.5/50呈下降趋势,磁感B50呈上升趋势;常化工艺为930℃×(2~3)min范围内能获得较好的磁性能,且对应的有利织构组分较高;后工序热处理工艺组合采用930℃×3 min常化+930℃×(2~3)min退火可获得较好的磁性能,且能耗低。
The effects of normalization process on microstructure, texture and magnetic properties of non-oriented silicon steel 35 W440 were investigated in this paper. The results show that with the increase of normalizing temperature, the iron loss P1.5/50 tends to decrease, and the magnetic B50 susceptibility increases in the normal temperature range of 900~960 ℃. Excellent electromagnetic properties of 35 W440 and the corresponding favorable texture components can be obtained from the normalization process 930 ℃×2~3 min. Better magnetic properties and lower energy cost can be realized by the combination of normalization process 930 ℃ × 2~3 min and annealing process 930 ℃×3 min.
引文
[1]朱翠翠,陈卓.高效电机推广进程及未来冷轧硅钢需求的预测[C]//中国钢铁年会,2013.
[2]李超,谷佳琪,苏雅,等.高效电机的节能经济分析及应用[J].能源与节能,2015(1):78-80.
[3]王爱华.世界主要国家的高效电机及其标准[J].电机技术,2013(4):40-43.
[4]王立涛,邓陈虹,裴陈新,等.高效电机用无取向电工钢组织和析出物研究及产品开发[J].钢铁研究学报,2011,23(1):31-35.
[5]朱涛,岳尔斌,项利,等.CSP生产高牌号无取向电工钢常化试验研究[J].钢铁研究学报,2010,1(1):32-32.
[6]金自力,齐建波,韩强,等.低牌号冷轧无取向硅钢的织构及电磁性能的对比分析[J].金属功能材料,2006,13(1):1-3.
[7]施立发,王立涛,何志坚,等.常化温度对CSP流程生产的2.5%Si硅钢析出物和磁性能影响[J].电工材料,2017(4):12-15.