摘要
分别采用不同Si_3N_4原料制备陶瓷球试样,研究Si_3N_4原料对陶瓷球的密度、孔隙度、压碎载荷比、硬度和断裂韧性的影响。结果表明:杂质含量低,粒度较小的Si_3N_4原料粉末生产的陶瓷球孔隙度较好,压碎载荷比和硬度较高,密度均匀性好;杂质含量高,粒度较大的原料粉末生产的陶瓷球断裂韧性较高。
The ceramic ball samples are prepared by using different Si_3N_4 raw materials. The effect of Si_3N_4 raw materials on density, porosity, crushing load ratio, hardness and fracture toughness of ceramic balls is studied. The results show that the ceramic balls prepared by Si_3N_4 raw material powers with low impurity content and small particle size are characterized by better porosity and density homogeneity, higher crushing load ratio and hardness. The ceramic balls prepared by Si_3N_(4 )raw material powers with high impurity content and large particle size feature higher fracture toughness.
引文
[1] 袁玉同,李洪涛,李鸿亮.氮化硅陶瓷滚子轴承的抗断油能力试验[J].轴承,2016(10):33-35.
[2] 黄传真,杨为清,艾兴.新型陶瓷轴承研究的现状与展望[J].中国陶瓷工业,1999,6(2):25-27.
[3] 李贵佳,孙峰.利用国外专利技术,解决国内氮化硅陶瓷轴承球产业化问题[J].中国陶瓷,2015,51(10):43-47.
[4] 张丽,张培志,何万宝,等.GPS-HIP工艺制备Si3N4陶瓷的研究[J].陶瓷科学与艺术,2009(1):4-6.
[5] 周长灵,邢政鹏,范景林,等.β-氮化硅陶瓷烧结致密化的研究[J].硅酸盐通报,2004(6):52-55.
[6] 滚动轴承高碳铬轴承钢零件热处理技术条件:JB/T 1255—2014[S].
[7] 精细陶瓷室温硬度试验方法:GB/T 16534—2009[S].
[8] 赵江铭,杨晓蔚,张永乾,等.氮化硅陶瓷毛坯球材料性能试验研究[J].轴承,2001(2):29-32.
[9] LEE K M,LEE W H,KOH Y H,et al.Microstructural evolution and mechanical properties of gas pressure sintered Si3N4 with Yb2O3 as a sintering aid[J].Journal of Materials Research,1999,14(5):1904-1909.