摘要
采用自主设计的串联式连续混炼设备,在保证下游连续混炼机各段机筒控制温度一定的条件下,研究下游连续混炼机转子转速对胶料内部硅烷偶联反应程度的影响。结果表明,在下游连续混炼机喂料段、混炼段、挤出段机筒控制温度分别为145,135,125℃的条件下,当转子转速为30 r·min~(-1)时,胶料停留时间为2.75 min,排胶温度为154℃,胶料内部硅烷偶联反应程度最高,白炭黑补强效果最好。
Taking independently developed series type continuous mixing equipment,the effect of rotor speed for downstream continuous mixer on the degree of silane coupling reaction in the compound was investigated at controlled temperature for each section of the mixer barrel. The results showed that,when the temperatures of feeding section,mixing section and extruding section were 145℃,135℃ and 125℃,respectively,the rotor speed was set at 30 r·min~(-1),the residence time of compound was 2.75 min,and the discharging temperature was 154℃,the degree of silane coupling reaction reached the highest value and the best reinforcing effect of silica was obtained.
引文
[1]边慧光,汪传生,李月春,等.串联式混炼工艺对不同用量白炭黑配方胶料的适应性研究[J].橡胶工业,2016,63(12):751-755.
[2]王薇.橡胶连续混炼设备与技术[J].橡胶工业,2003,50(4):237-238.
[3]沈宏,邓宇峰.橡胶混炼技术与设备的研究[J].机械工程师,2012(8),127-128.
[4]刘丽,张仁广,刘婧,等.串联密炼机组的研发和应用概况[J].橡胶科技,2014,12(3):5-11.
[5]汪传生.同步转子密炼机混炼橡胶的理论和实验研究[D].北京:北京化工大学,2000.
[6]王石.串联式密炼机新型转子研制及其试验研究[D].青岛:青岛科技大学,2014.