针对动车组在运行过程中发现的铝合金安装底座的锈蚀情况,分别从材质和结构方面进行分析,初步推断铝合金底座的锈蚀原因。通过性能检测和抗锈蚀性能试验确定了锈蚀的主要原因是底座用的2A11铝合金易发生晶间腐蚀,与不锈钢支架接触时电偶腐蚀敏感性高,底座与支架之间的间隙会积存电解液。提出了多项整治措施,为类似安装底座的防锈蚀设计提供参考。
The causes for the corrosion of aluminum alloy mounting base found during the running of electric multiple unit were preliminarily deduced by analyzing the material and structure. Three main causes were determined based on property tests and corrosion tests:(1) the mounting base made of 2 A11 aluminum alloy easily suffers from intergranular corrosion;(2) the galvanic corrosion sensitivity is high when mounting base is connected with the mounting bracket made of stainless steel; and(3) there exists electrolyte in the gap between the base and bracket. Some remedial measures were presented, providing a reference for the anticorrosion design of similar mounting base.
引文
[1]苏景新,张昭,曹发和,等.铝合金的晶间腐蚀与剥蚀[J].中国腐蚀与防护学报, 2015, 25(3):187-192.
[2]王玲,宣卫芳,牟献良. 2A11铝合金/碳钢偶接件在强化自然环境条件下的腐蚀特性[J].表面技术, 2011, 40(5):1-4.
[3]卞贵学,陈跃良,张勇,等.飞机用铝合金腐蚀行为和腐蚀预测研究现状及问题分析[J].装备环境工程, 2018, 15(5):48-55.
[4]徐火平,刘慧丛,朱立群,等.盐雾环境中高强铝合金点腐蚀行为与暴露面积的关系[J].航空材料学报, 2010, 30(4):59-64.