摘要
为解决毫/纳秒激光加工微孔质量差的问题,利用515 nm皮秒激光对厚度为0.1 mm的不锈钢进行环切法加工直径100μm的微孔实验。采用激光共聚焦显微镜对加工后形貌和质量进行观察与表征,研究激光能量密度、扫描速度和离焦量等因素对加工后微孔形貌与质量的影响规律。实验结果表明,能量密度对微孔内壁质量有直接的影响,在保证去除能力前提下,控制能量密度在6.45 J/cm~2以下,可有效减小微孔内壁的热影响区。同时实验还发现,适当增加扫描速度能够改善环切加工微孔切口和内壁的质量。在激光能量密度6.45 J/cm~2、扫描速度200 mm/s时,孔锥度为2.72°。随着扫描速度的增大,锥度减小,最后稳定在2.29°左右,正离焦加工也能一定程度上减小孔的锥度。此研究结果表明,优化工艺参数能够加工出热影响区小、边缘质量好且锥度小的微孔。
In order to solve the problem of poor microhole quality in millisecond/nanosecond laser processing, the 515 nm picosecond laser was used to ring cutting stainless steel with a thickness of 0.1 mm to process microholes with a diameter of 100 μm. Laser confocal microscopy was used to observe and characterize the morphology and quality of the processed microstructure. The effects of laser energy density, scanning speed and defocusing amount on the morphology and quality of microholes after processing were studied. The experimental results show that the energy density has a direct influence on the inner wall quality of the microholes. Controlling the energy density below 6.45 J/cm~2 can effectively reduce the heat affected zone of the inner wall of the microholes under the premise of ensuring the removal ability. At the same time, it is found that appropriately increasing the scanning speed can improve the quality of the microhole incision and the inner wall of the ring cutting. When the laser energy density is 6.45 J/cm~2 and the scanning speed is 200 mm/s, the hole taper is 2.72 degrees. As the scanning speed increases, the taper decreases, and finally stabilizes at about 2.29 degrees. The taper of the hole can also be reduced to some extent by the positive defocusing process. The results of this study show that the optimized process parameters can process microholes with small heat affected zone, good edge quality and small taper.
引文
[1] 辛凤兰.高质量激光打孔技术研究[D].北京:北京工业大学,2006.
[2] 夏博,姜澜,王素梅,等.飞秒激光微孔加工[J].中国激光,2013,40(2):1-12.
[3] 王砚丽.激光旋转打孔技术的研究[D].武汉:华中科技大学,2012.
[4] 姜靖.皮秒激光对金属材料微孔加工技术研究[D].北京:北京工业大学,2014.
[5] 王国彪.光制造科学与技术的现状和展望[J].机械工程报,2011,47(21):157-169.
[6] SEZER H K,LI L,SCHMIDT M,et al.Effect of beam angle on HAG,recast and oxide layer characteristics in laser drilling of TBC nickel super alloys[J].International Journal of Machine Tools and Manufacture,2006,46(15):1972-1982.
[7] LEIGH S,SEZER K,LI L,et al.Recast and oxide formation in laser-drilled acute holes in CMSX-4 nickel single-crystal superalloy[J].Proceeding of the Institution of Mechanical Engineers,Part B:Journal of Engineering Manufacture,2010,224(B7):1005-1016.
[8] LI X,JIANG L,WANG C,et al.Transient localized material properties changes by ultra-fast laser pulse manipulation of electron dynamics in micro/nano manufacturing[C]//San Francisco:Materials Research,Spring Meeting,2011(1365):3-8.
[9] MAO S S,QUERE F,GUIZARD S,et al.Dynamics of femtosecond laser interactions with dielectrics[J].Applied Physics A:Materials Science & Processing,2004,79(7):1695-1709.
[10] JIANG L,TSAI H L.Prediction of crater shaper in femtosecond laser ablation of dielectrics[J].Journal of Physics D:Applied Physics,2004,37(10):1492-1496.
[11] 赵华龙,周仁魁,赵卫,等.飞秒激光倒锥微孔加工的反射式扫描装置设计[J].光子学报,2014,43(9):1-6.
[12] 刚肖.皮秒激光在微纳加工中的应用现状与展望[J].科技视界,2016(23):419.
[13] 刘路,阮亮,张天润,等.皮秒激光加工不锈钢微孔实验研究[J].应用激光,2015,35(4):472-478.
[14] 孙树峰,廖惠鹏,吴旭浩,等.皮秒激光旋切加工微孔试验研究[J].激光技术,2018,42(2):234-238.
[15] LOW D K Y.Spatter and taper control in laser percussion drilling[D].Manchester:University of Manchester Institute of Science and Technology(UMIST),2001:7-8.
[16] 晏绪光,高文斌,杨水其,等.激光脉冲和工件参数对激光微孔加工质量的影响[J].应用激光,1994,14(3):127-130.