摘要
轻型纸松厚度较高、纸面粗糙。选用松厚度较高的机械浆,添加松厚剂,加填硅酸钙等密度小的填料等措施来提高松厚度,使用返黄抑制剂控制机械浆返黄,表面施胶淀粉添加增强剂提高表面强度改善掉毛掉粉,或表面微涂改善纸面细腻度,进而改善印刷性能,提高色彩还原性。
Low density printing paper has high bulk and rough surface. The mechanical pulp with higher bulk, thickness aids and filler with lower density such as calcium silicate are selected to improve the thickness. The yellowing inhibitor is used to control the yellowing of the mechanical pulp. The surface sizing starch is added with wet strength agent to improve the surface strength and flour drop, or the surface micro-coating improves the fineness of the paper surface, thereby improving the printing performance and color reduction.
Low density printing paper has high bulk and rough surface. The mechanical pulp with higher bulk, thickness aids and filler with lower density such as calcium silicate are selected to improve the thickness. The yellowing inhibitor is used to control the yellowing of the mechanical pulp. The surface sizing starch is added with wet strength agent to improve the surface strength and flour drop, or the surface micro-coating improves the fineness of the paper surface, thereby improving the printing performance and color reduction.
引文
[1]路葳,周洋,张俊青,等.杨木BECMP抄造轻型纸纤维体系的研究[J].纸和造纸,2012,31(5):3-5.
[2]邓拥军,房桂干,韩善明,等.杨木加工剩余物制漂白化学机械浆及配抄轻型纸的研究[J].林产化学与工业,2009,29(S1):262-262.
[3]傅其军,陆琪,吴明刚,等.速生桉木P-RC APMP工业化生产[J].中国造纸,2010,29(12):42-45.
[4]傅其军,陆琪,李小林,等.桉木与杨木混合生产P-RC APMP[J].中华纸业,2011,32(20):70-72.
[5]傅其军,陆琪,李小林,等.桉木与竹子混合生产P-RC APMP[J].中国造纸,2011,30(10):47-51.
[6]常洽,覃德山,吴守耀,等.麦草化学机械浆制浆造纸性能研究[J].造纸科学与技术,2009,28(2):12-14.
[7]栗敏,杨汝男,李士勇,等.红麻全杆APMP配抄轻型纸的研究[J].中华纸业,2006,27(11):36-37.
[8]万洪安,焦国栋,李跃进.棉秆化机浆配抄轻型纸技术研究[J].河南科技,2016(11):72-75.
[9]赵雨萌,刘忠,李群,等.全棉秆高白度化机浆的制备及其应用[J].纸和造纸,2015,34(3):7-11.
[10]杜伟民.松厚性助剂对高松厚性纸张性能的影响[J].造纸化学品,2010,22(3):48-52.
[11]金海兰,罔山隆之,于钢.轻型纸的制备及其纤维间结合力分析[J].中国造纸学报,2012,27(4):10-13.
[12]金海兰,赵骏衡,罔山隆之.松厚纸张的孔隙结构分析[J].中华纸业,2018(6):12-16.
[13]彭建军,张权,陈铃华,等.合成硅酸钙在轻型纸中的应用研究[J].中国造纸,2015,34(1):13-18.
[14]王成海,孙俊民,王玉珑,等.硅酸钙加填轻型纸的应用研究[J].中华纸业,2014(20):27-30.
[15]宋顺喜,郝宁,张美云,等.粉煤灰基碳酸钙-细小纤维-CPAM共絮聚改善加填纸张物理性能的研究[J].陕西科技大学学报,2015,33(6):6-9.
[16]王玉珑,唐春霞,刘艳新,等.多孔硅酸钙加填轻型纸的生产实践与分析[J].中华纸业,2016,37(16):59-62.
[17]王洪振,赵传山,于淑慧.木粉与化机浆配抄轻型纸的研究[J].造纸化学品,2010,22(1):36-39.
[18]马丽,赵传山,韩金梅.木素改型水溶性酚醛树脂用于轻型纸[J].纸和造纸,2011,30(2):13-16.
[19]刘永顺,顾秀梅,赵新军,等.阳离子瓜尔胶在轻型纸中的应用[J].造纸化学品,2012(1):31-34.
[20]刘燕韶,赵传山,马厚悦,等.新闻纸机改产轻型纸后AKD施胶的生产实践[J].中华纸业,2011,32(22):63-65.
[21]王代启,胡开堂,何北海.BCTMP的特性及其对ASA中性施胶的影响[J].中华纸业,2005,26(4):33-36.
[22]刘建杰,李群,胡开堂,等.杨木APMP浆ASA中性施胶特性分析[J].中国造纸,2010,29(4):8-13.
[23]王进喜,陈嘉川,杨桂花.EDTA后处理抑制纸浆手抄片返黄的研究[J].中国造纸,2004,23(10):4-6.
[24]尤纪雪,景宜,张凯,等.漆酶/木聚糖酶体系处理抑制漂白化学机械浆返黄的研究[J].中国造纸学会学术年报,2008.
[25]覃炳达.新型受阻胺类化机浆光返黄抑制剂的研究[D].广西大学,2008.
[26]冯桂平,田中粟,李翠.α-淀粉酶在轻型纸表面施胶中的应用[J].纸和造纸,2011,30(2):13-16.
[27]冯桂平,田中粟,张勇.改型MF树脂在轻型纸表面施胶中的应用[J].中华纸业,2012,33(18):82-83.
[28]徐腾.轻型印刷纸表面施胶工艺探讨[J].中华纸业,2008,29(10):70-72.
[29]李树俭.微量涂布轻型纸工艺技术的研究与实践[D].齐鲁工业大学,2016.
[2]邓拥军,房桂干,韩善明,等.杨木加工剩余物制漂白化学机械浆及配抄轻型纸的研究[J].林产化学与工业,2009,29(S1):262-262.
[3]傅其军,陆琪,吴明刚,等.速生桉木P-RC APMP工业化生产[J].中国造纸,2010,29(12):42-45.
[4]傅其军,陆琪,李小林,等.桉木与杨木混合生产P-RC APMP[J].中华纸业,2011,32(20):70-72.
[5]傅其军,陆琪,李小林,等.桉木与竹子混合生产P-RC APMP[J].中国造纸,2011,30(10):47-51.
[6]常洽,覃德山,吴守耀,等.麦草化学机械浆制浆造纸性能研究[J].造纸科学与技术,2009,28(2):12-14.
[7]栗敏,杨汝男,李士勇,等.红麻全杆APMP配抄轻型纸的研究[J].中华纸业,2006,27(11):36-37.
[8]万洪安,焦国栋,李跃进.棉秆化机浆配抄轻型纸技术研究[J].河南科技,2016(11):72-75.
[9]赵雨萌,刘忠,李群,等.全棉秆高白度化机浆的制备及其应用[J].纸和造纸,2015,34(3):7-11.
[10]杜伟民.松厚性助剂对高松厚性纸张性能的影响[J].造纸化学品,2010,22(3):48-52.
[11]金海兰,罔山隆之,于钢.轻型纸的制备及其纤维间结合力分析[J].中国造纸学报,2012,27(4):10-13.
[12]金海兰,赵骏衡,罔山隆之.松厚纸张的孔隙结构分析[J].中华纸业,2018(6):12-16.
[13]彭建军,张权,陈铃华,等.合成硅酸钙在轻型纸中的应用研究[J].中国造纸,2015,34(1):13-18.
[14]王成海,孙俊民,王玉珑,等.硅酸钙加填轻型纸的应用研究[J].中华纸业,2014(20):27-30.
[15]宋顺喜,郝宁,张美云,等.粉煤灰基碳酸钙-细小纤维-CPAM共絮聚改善加填纸张物理性能的研究[J].陕西科技大学学报,2015,33(6):6-9.
[16]王玉珑,唐春霞,刘艳新,等.多孔硅酸钙加填轻型纸的生产实践与分析[J].中华纸业,2016,37(16):59-62.
[17]王洪振,赵传山,于淑慧.木粉与化机浆配抄轻型纸的研究[J].造纸化学品,2010,22(1):36-39.
[18]马丽,赵传山,韩金梅.木素改型水溶性酚醛树脂用于轻型纸[J].纸和造纸,2011,30(2):13-16.
[19]刘永顺,顾秀梅,赵新军,等.阳离子瓜尔胶在轻型纸中的应用[J].造纸化学品,2012(1):31-34.
[20]刘燕韶,赵传山,马厚悦,等.新闻纸机改产轻型纸后AKD施胶的生产实践[J].中华纸业,2011,32(22):63-65.
[21]王代启,胡开堂,何北海.BCTMP的特性及其对ASA中性施胶的影响[J].中华纸业,2005,26(4):33-36.
[22]刘建杰,李群,胡开堂,等.杨木APMP浆ASA中性施胶特性分析[J].中国造纸,2010,29(4):8-13.
[23]王进喜,陈嘉川,杨桂花.EDTA后处理抑制纸浆手抄片返黄的研究[J].中国造纸,2004,23(10):4-6.
[24]尤纪雪,景宜,张凯,等.漆酶/木聚糖酶体系处理抑制漂白化学机械浆返黄的研究[J].中国造纸学会学术年报,2008.
[25]覃炳达.新型受阻胺类化机浆光返黄抑制剂的研究[D].广西大学,2008.
[26]冯桂平,田中粟,李翠.α-淀粉酶在轻型纸表面施胶中的应用[J].纸和造纸,2011,30(2):13-16.
[27]冯桂平,田中粟,张勇.改型MF树脂在轻型纸表面施胶中的应用[J].中华纸业,2012,33(18):82-83.
[28]徐腾.轻型印刷纸表面施胶工艺探讨[J].中华纸业,2008,29(10):70-72.
[29]李树俭.微量涂布轻型纸工艺技术的研究与实践[D].齐鲁工业大学,2016.