摘要
采用溶胶-凝胶法制备了钨掺杂镍酸锂正极材料(LiNi_(1-x)W_xO_2,x=1%、3%),研究了钨掺杂对LiNiO_2正极材料电化学性能的影响。结果表明,钨掺杂明显地改善了LiNiO_2的充放电循环性能,在100 mA·g~(-1)的电流密度和2.5~4.5 V电压范围的测试条件下,LiNi_(0.99)W_(0.01)O_2材料循环400次后的容量保持率为62.51%,而LiNiO_2在相同循环条件下的保持率仅为47.06%。同时,钨掺杂也提升了LiNiO_2的充放电倍率性能,掺杂材料在每一个倍率下放电比容量均高于未掺杂材料。
W-doping LiNiO_2(LiNi_(1-x)W_xO_2, x=1% and 3%) cathode materials were prepared by sol-gel method. The effects of W-doping on electrochemical performances of LiNiO_2 materials were studied. The results showed that W-doping significantly improved the cycle performance of LiNiO_2 during charge-discharge process. The capacity retention of the LiNi_(0.99)W_(0.01)O_2 was 62.51% at a current density of 100 mA·g~(-1) after 400 cycles in the voltage of 2.5~4.5 V, while the LiNiO_2 was only 47.06%. In addition, the rate performance of LiNiO_2 was improved at the same current rates.
引文
[1]Li J,Klopsch R,Stan M C,et al.J.Power Sources,2011,196(10):4821-4825
[2]Yabuuchi N,Yoshii K,Myung S T,et al.J.Am.Chem.Soc.2011,133(12):4404-4419
[3]Park K S,Cho M H,Jin S J,et al.Solid State Ionics,2004,171(1/2):141-146
[4]Martha S K,Nanda J,Veith G M,et al.J.Power Sources2012,199:220-226
[5]Thackeray M M,Kang S H,Johnson C S,et al.J.Mater.Chem.,2007,17(30):3112-3125
[6]Ogasawara T,Débart A,Holzapfel M,et al.J.Am.Chem.Soc.,2006,128(4):1390-1393
[7]Toprakci O,Toprakci H A K,Li Y,et al.J.Power Sources2013,241:522-528
[8]Wu F,Wang Z,Su Y F,et al.J.Power Sources,2014,24720-25
[9]Mohanty D,Kalnaus S,Meisner R A,et al.J.Power Sources2013,229:239-248
[10]Gallagher K G,Croy J R,Balasubramanian M,et al.Electrochem.Commun.,2013,33:96-98
[11]Croy J R,Gallagher K G,Balasubramanian M,et al.J.Phys.Chem.C,2013,117(13):6525-6536
[12]Bloom I,Trahey L,Abouimrane A,et al.J.Power Sources2014,249:509-514
[13]Sang H P,Park K S,Yang K S,et al.Electrochim.Acta2002,46(8):1215-1222
[14]Liu Z C,Zhen H H,Kim Y,et al.J.Power Sources,2011196(23):10201-10206
[15]Cui P,Jia Z J,Li L Y,et al.J.Phys.Chem.Solids,2011,72(7):899-903
[16]Yoon C S,Choi M J,Jun D W,et al.Chem.Mater.,2018,30(5):1808-1814
[17]Muto S,Tatsumi K,Kojima Y,et al.J.Power Sources,2012,205(2):449-455
[18]Nishida Y,Nakane K,Satoh T.J.Power Sources,1997,68(2):561-564
[19]Cho G B,Choe H J,Kim B M,et al.J.Alloys Compd.,2009,488(1):L17-L20
[20]Kwon S N,Song J,Mumm D R.Ceram.Int.,2011,37(5):1543-1548
[21]LIU Hong-Fei(刘红飞),JIA Tie-Kun(贾铁昆).Journal of Ningxia University:Natural Science Edition(宁夏大学学报:自然科学版),2011,32(2):144-146
[22]Wang Y D,Chen T,Mu Q Y.J.Mater.Chem.,2011,21(16):6006-6013
[23]Xia A,Huang J H,Tan G Q,et al.Ceram.Int.,2014,40(9):14845-14850
[24]ZHENG Zhen-Huan(郑振环),LI Qiang(李强).Introduction to Rietveld Refinement with X-Ray Power Diffraction Data GSAS Software(X射线多晶衍射数据Rietveld精修及GSAS软件入门).Beijing:China Building Materials Press,2016.
[25]Zeng X L,Wu P,Luo F L,et al.J.Phys.Chem.Solids,2010,71(9):1404-1409
[26]Gupta A,Chemelewski W D,Buddie Mullins C,et al.Adv.Mater.,2015,27(39):6063-6067
[27]Amine K,Tukamoto H,Yasuda H,et al.J.Electrochem.Soc.,1996,143(5):1607-1613
[28]Mansour A N.Surf.Sci.Spectra,1994,3(3):279-286
[29]Shaju K M,Rao G V S,Chowdari B V R.Electrochim.Acta,2003,48(11):1505-1514
[30]Carley A F,Jackson S D,O′shea J N,et al.Surf.Sci.,1999440(3):L868-L874
[31]Blackman C S,Piccirillo C,Binions R,et al.Thin Solid Films,2009,517(16):4565-4570
[32]Qi H,Wang C Y,Liu J J.Adv.Mater.,2003,15(5):411-414
[33]Kubo K,Fujiwara M,Yamada S,et al.J.Power Sources,1997,68(2):553-557
[34]Li W,Reimers J N,Dahn J R.Solid State Ionics,1993,67(1/2):123-130
[35]Ohzuku T,Ueda A,Yamamoto N,et al.J.Power Sources,1995,54(1):99-102
[36]ZHANG Na(张娜),TANG Zhi-Yuan(唐致远),HUANGQing-Hua(黄庆华),et al.Chemistry Online(化学通报网络版),2005,68(1):1-5