摘要
使用氩弧熔覆技术在铸态ZTA15钛合金表面预置石墨粉,获得厚度约1mm的钛基复合材料熔覆层。熔覆层内主要相为α-Ti和TiC,且TiC相以树枝晶形态弥散分布。熔覆层显微硬度最高可达HV_1443,相比铸态基体硬度值提高了33%。
The titanium matrix composite cladding layer with thickness of about 1 mm could be fabricated by using argon arc cladding technique to prefabricate graphite powder on the surface of cast ZTA15 titanium alloy.In the cladding layer, the main phases were α-Ti and TiC, and the TiC phases were dispersed with dendritic morphology. The microhardness of the cladding layer was up to 443 HV1, with an increase of 33% compared with that of the as-cast matrix.
引文
[1]李勇.钛合金发展现状及展望[J].工艺与设备,2018(1):216-217.
[2]费有静.钛及钛合金材料的应用分析[J].新材料产业,2017,3:15-18.
[3]原国森,兖利鹏,韩艳艳.钛合金的应用进展[J].热加工工艺,2017,46(4):13-16.
[4]张晓丹.国内外钛合金研究及应用现状[J].新材料产业,2017(3):7-10.
[5]张文毓.钛合金表面耐磨处理技术研究现状[J].全面腐蚀控制,2017,31(2):25-29,87.
[6]付颖,张艳,包星宇,等.钛合金表面耐磨涂层研究进展[J].中国腐蚀与防护学报,2018,38(2):117-123.
[7]孟君晟,吉泽升. TC4合金氩弧熔覆Ni60+B4 C复合涂层组织及耐磨性[J].材料热处理学报,2013,34(3):140-144.
[8]何波,兰姣姣,杨光,等.激光原位合成TiB-TiC颗粒增强钛基复合材料的组织与其耐磨性能[J].稀有金属材料与工程,2017,46(12):3805-3810.
[9]杨光,王向明,王维,等.激光熔覆制备Ti C颗粒增强涂层的组织和性能[J].红外与激光工程,2014,43(3):795-799.
[10]宋思利,邹增大,王新洪,等.钨极氩弧熔敷技术制备含Ti C颗粒增强涂层的研究[J].山东大学学报(工学版),2006,36(3):1-4,12.
[11]王振廷,陈丽丽,张显友.钛合金表面氩弧熔覆Ti C增强复合涂层组织与性能分析[J].焊接学报,2008,29(9):43-45.
[12]王振廷,高红明,梁刚,等. Ti6Al4V合金表面氩弧熔覆原位合成TiC-TiB2增强钛基复合涂层组织与耐磨性[J].稀有金属材料与工程,2012,41(7):1259-1262.
[13]牛静,张立文,张全忠,等. BT20钛合金电火花沉积Ti C涂层的微观组织研究[J].金属热处理,2006,31(4):59-61.