放射线对不同材料充填治疗龋损牙边缘微渗漏的影响
|
摘要
目的:观察放射线照射对FiltekZ350纳米树脂和FX-Ⅱ加强型玻璃离子水门汀充填治疗龋损牙对边缘微渗漏的影响。方法:40颗离体前磨牙随机分为4组,每组10颗,分别为放射线照射A1组和A2组,对照B1组和B2组。40颗离体牙均在颊侧面备洞,A1、B1组样本牙使用FiltekZ350纳米树脂充填窝洞,A2、B2组样本牙使用FX-Ⅱ加强型玻璃离子水门汀充填。A1和A2组样本牙每天进行一次放射线照射,每次2.0Gy,累计总照射剂量为70Gy;B1和B2组样本牙不做放射线照射。4组样本经500次冷热循环后,使用2.0%亚甲基蓝溶液染色,体式显微镜下测量每组样本牙的微渗漏值。结果:使用相同充填材料,放射线照射组与对照组微渗漏值比较,差异无统计学意义(P>0.05)。不论是否放射线照射,不同充填材料微渗漏值比较,差异均无统计学意义(P>0.05)。结论:临床上对于准备实施放射治疗的头颈部肿瘤患者,选择FiltekZ350纳米树脂和FX-Ⅱ加强型玻璃离子水门汀充填治疗龋损牙,均能获得较稳定的边缘密封效果。
Objective: To observe the effects of radiographic exposure on marginal microleakage for treating dental caries with Filtek Z350 nano resin and FX-Ⅱ reinforced glass ionomer cement. Methods: 40 premolars were randomly divided into four groups with 10 teeth in each group: radiographic exposure group A1 and A2,control group B1 and B2.Cavities were prepared on the buccal side of all the teeth, then the teeth in group A1 and B1 were filled with Filtek Z350 nano resin, and the teeth in group A2 and B2 were filled with FX-II reinforced glass ionomer cement. The teeth in group A1 and A2 were irradiated once a day and 2.0 Gy a time, and the total exposure was 70 Gy; While the teeth in group B1 and B2 were not irradiated. All the teeth were dyed with 2.0% methylene blue solution after 500 times thermocycling, and the microleakage depth were measured under somatic microscope. Results: Filled with same filling materials, there was no significant difference in microleakage depth between radiographic exposure group and control group(P>0.05). Radiation or not, there was no significant difference in microleakage depth between different filling materials(P>0.05). Conclusions: For patients with head and neck tumor who are prepared for radiotherapy in clinic, Filtek Z350 nano resin and FX-Ⅱ reinforced glass ionomer cement can be used to treat dental caries, they all can obtain fairly stable edge sealing effects.
Objective: To observe the effects of radiographic exposure on marginal microleakage for treating dental caries with Filtek Z350 nano resin and FX-Ⅱ reinforced glass ionomer cement. Methods: 40 premolars were randomly divided into four groups with 10 teeth in each group: radiographic exposure group A1 and A2,control group B1 and B2.Cavities were prepared on the buccal side of all the teeth, then the teeth in group A1 and B1 were filled with Filtek Z350 nano resin, and the teeth in group A2 and B2 were filled with FX-II reinforced glass ionomer cement. The teeth in group A1 and A2 were irradiated once a day and 2.0 Gy a time, and the total exposure was 70 Gy; While the teeth in group B1 and B2 were not irradiated. All the teeth were dyed with 2.0% methylene blue solution after 500 times thermocycling, and the microleakage depth were measured under somatic microscope. Results: Filled with same filling materials, there was no significant difference in microleakage depth between radiographic exposure group and control group(P>0.05). Radiation or not, there was no significant difference in microleakage depth between different filling materials(P>0.05). Conclusions: For patients with head and neck tumor who are prepared for radiotherapy in clinic, Filtek Z350 nano resin and FX-Ⅱ reinforced glass ionomer cement can be used to treat dental caries, they all can obtain fairly stable edge sealing effects.
引文
[1]孟柳燕.头颈部癌患者放疗后的口腔并发症及其防治措施[J].口腔医学研究,2003,19(6):526-527.
[2]Deng J,Jackson L,Epstein J B,et al.Dental demineralization andcaries in patients with head and neck cancer[J].Oral Oncology,2015,51(9):824-831.
[3]Galv?o-Moreira LV,da Cruz MC.Dental demineralization,radiation caries and oral microbiota in patients with head and neck cancer[J].Oral Oncology,2015,51(12):e89-e90.
[4]Catelan A,Padilha AC,Salzedas LM,et al.Effect of radiotherapy on the radiopacity and flexural strength of a composite resin[J].Acta Odontol Latinoam,2008,21(2):159-162.
[5]Viero FL,Boscolo FN,Demarco FF,et al.Effect of radiotherapy on the hardness and surface roughness of two composite resins[J].Gen Dent,2011,59(4):e168-172.
[6]Brandeburski SBN,Della Bona A.Effect of ionizing radiation on properties of restorative materials[J].Dent Mater,2018,34(2):221-227.
[7]Hegde MN,Vyapaka P,Shetty S.A comparative evaluation of microleakage of three different newer direct composite resins using a self etching primer in class V cavities:An in vitro study[J].J Conserv Dent,2009,12(4):160-163.
[8]汪信洋,刘卫红,卞颖颖,等.复合树脂充填近中牙合面洞颈壁边缘微渗漏的研究[J].牙体牙髓牙周病学杂志,2009,19(4):215-217.
[9]Bulucu B,Avsar A,Demiryürek EO,et al.Effect of radiotherapy on the microleakage of adhesive systems[J].J Adhes Dent,2009,11(4):305-309.
[10]Mount GJ,Tyas MJ,Ferracane JL,et al.A revised classification for direct tooth-colored restorative materials[J].Quintessence Int,2009,40(8):691-697.
[2]Deng J,Jackson L,Epstein J B,et al.Dental demineralization andcaries in patients with head and neck cancer[J].Oral Oncology,2015,51(9):824-831.
[3]Galv?o-Moreira LV,da Cruz MC.Dental demineralization,radiation caries and oral microbiota in patients with head and neck cancer[J].Oral Oncology,2015,51(12):e89-e90.
[4]Catelan A,Padilha AC,Salzedas LM,et al.Effect of radiotherapy on the radiopacity and flexural strength of a composite resin[J].Acta Odontol Latinoam,2008,21(2):159-162.
[5]Viero FL,Boscolo FN,Demarco FF,et al.Effect of radiotherapy on the hardness and surface roughness of two composite resins[J].Gen Dent,2011,59(4):e168-172.
[6]Brandeburski SBN,Della Bona A.Effect of ionizing radiation on properties of restorative materials[J].Dent Mater,2018,34(2):221-227.
[7]Hegde MN,Vyapaka P,Shetty S.A comparative evaluation of microleakage of three different newer direct composite resins using a self etching primer in class V cavities:An in vitro study[J].J Conserv Dent,2009,12(4):160-163.
[8]汪信洋,刘卫红,卞颖颖,等.复合树脂充填近中牙合面洞颈壁边缘微渗漏的研究[J].牙体牙髓牙周病学杂志,2009,19(4):215-217.
[9]Bulucu B,Avsar A,Demiryürek EO,et al.Effect of radiotherapy on the microleakage of adhesive systems[J].J Adhes Dent,2009,11(4):305-309.
[10]Mount GJ,Tyas MJ,Ferracane JL,et al.A revised classification for direct tooth-colored restorative materials[J].Quintessence Int,2009,40(8):691-697.