Cu基药芯焊丝TIG焊TA1/Q235B接头微观组织和显微硬度
|
摘要
利用Cu基(Cu-Cr-Co-Ni)药芯焊丝对TA1/Q235B异种金属对接与搭接接头进行了TIG焊接试验.通过SEM、EDS和XRD对接头微观组织进行了详细分析,通过显微硬度测试了接头的硬度分布.结果表明,采用Cu基药芯焊丝进行TA1/Q235B TIG焊接,对接和搭接均得到了无缺陷的接头.两种接头的焊缝与母材界面处组织分布类似,其中TA1侧主要由β-Ti固溶体、FeTi和CuTi2化合物组成;Q235B侧主要由Fe,Cu基固溶体和Fe2Ti化合物组成.对接焊缝主要由Cu基固溶体,CuTi,FeTi,Cu4Ti,τ2和τ3金属间化合物组成,而搭接焊缝主要由Cu基固溶体、τ2和Cu4Ti组成.对接接头的平均硬度为449 HV0.1,搭接接头的平均硬度为335 HV0.1.
TA1/Q235B dissimilar butt and lap joints were obtained by tungsten inert gas(TIG) welding method with Cu-Cr-Co-Ni flux-cored wires.The microstructures of the joints were characterized by SEM,EDS and XRD.Microhardness tests were conducted to reveal the hardness distribution of the joints.The results showed that butt and lap welded joints were obtained without defects.Similar microstructures were observed in these two welded joints.Microstructure near TA1 interface consisted of β-Ti solid solution,FeTi and CuTi_2 compounds,and microstructure near Q235 B consisted of Fe and Cu solid solution and Fe_2Ti compounds.The butt weld was composed of Cu solid solution,CuTi,Fe_2Ti,Cu_4Ti,τ_2 and τ_3 compounds.While in the lap joints,the weld was composed of Cu solid solution,τ_2 and Cu_4Ti compounds.The average hardness of the butt joint was 449 HV0.1,while that of the lap joint was 335 HV0.1.
TA1/Q235B dissimilar butt and lap joints were obtained by tungsten inert gas(TIG) welding method with Cu-Cr-Co-Ni flux-cored wires.The microstructures of the joints were characterized by SEM,EDS and XRD.Microhardness tests were conducted to reveal the hardness distribution of the joints.The results showed that butt and lap welded joints were obtained without defects.Similar microstructures were observed in these two welded joints.Microstructure near TA1 interface consisted of β-Ti solid solution,FeTi and CuTi_2 compounds,and microstructure near Q235 B consisted of Fe and Cu solid solution and Fe_2Ti compounds.The butt weld was composed of Cu solid solution,CuTi,Fe_2Ti,Cu_4Ti,τ_2 and τ_3 compounds.While in the lap joints,the weld was composed of Cu solid solution,τ_2 and Cu_4Ti compounds.The average hardness of the butt joint was 449 HV0.1,while that of the lap joint was 335 HV0.1.
引文
[1]Tomashchuk I,Sallamand P,Andrzejewski H,et al.The formation of intermetallics in dissimilar Ti6Al4V/copper/AISI 316 Lelectron beam and Nd:YAG laser joints[J].Intermetallics,2011,19(10):1466-1473.
[2]王廷,张秉刚,陈国庆,等.TA15钛合金与不锈钢的电子束焊接[J].焊接学报,2010,31(5):53-56.Wang Ting,Zhang Binggang,Chen Guoqing,et al.Electron beam welding of TA15 titanium alloy to 304 stainless steel[J].Transactions of the China Welding Institution,2010,31(5):53-56.
[3]Wang T,Zhang B,Feng J,et al.Effect of a copper filler metal on the microstructure and mechanical properties of electron beam welded titanium-stainless steel joint[J].Materials Characterization,2012,73:104-113.
[4]Lee M K,Lee J G,Choi Y H,et al.Interlayer engineering for dissimilar bonding of titanium to stainless steel[J].Materials Letters,2010,64:1105-1108.
[5]王廷,张秉刚,张艳娇,等.采用不同结构Cu/V填充层的钛合金/不锈钢电子束焊接试验[J].焊接学报,2014,35(8):71-74.Wang Ting,Zhang Binggang,Zhang Yanjiao,et al.Experimental research on electron beam welding of titanium to stainless steel based on Cu/V filler metals with different shapes[J].Transactions of the China Welding Institution,2014,35(8):71-74.
[6]Wang T,Zhang B,Chen G.High strength electron beam welded titanium-stainless steel joint with V/Cu based composite filler metals[J].Vacuum,2013,94(6):41-47.
[7]Chu Q,Zhang M,Li J.Experimental investigation of explosionwelded CP-Ti/Q345 bimetallic sheet filled with Cu/V based fluxcored wire[J].Materials and Design,2015,67:606-614.
[8]He P,Zhang J,Zhou R,et al.Diffusion bonding technology of titanium alloy to stainless steel with Ni interlayer[J].Materials Characterization,1999,43(5):287-292.
[9]Kundu S,Chatterjee S.Characterization of diffusion bonded joint between titanium and 304 stainless steel using a Ni interlayer[J].Materials Characterization,2008,59(5):631-637.
[10]Dharmendra C,Rao KP,Wilden J,et al.Study on laser weldingbrazing of zinc coated steel to aluminium alloy with a zinc based filler[J].Materials Science and Engineering A,2011,528:1497-1503.
[11]Froes F H.Titanium:Physical metallurgy,processing and applications[M].Ohio:ASM International,2015.
[12]Bo H,Duarte L I,Zhu W J,et al.Experimental study and thermodynamic assessment of the Cu-Fe-Ti system[J].Calphad:Computer Coupling of Phase Diagrams and Thermochemistry,2013,40:24-33.
[13]Beek J A V,Kodentsov A A,Loo F J J V.Phase equilibria in the Cu-Fe-Ti system at 1123 K[J].Journal of Alloys and Compounds,1995,217(1):97-103.
[2]王廷,张秉刚,陈国庆,等.TA15钛合金与不锈钢的电子束焊接[J].焊接学报,2010,31(5):53-56.Wang Ting,Zhang Binggang,Chen Guoqing,et al.Electron beam welding of TA15 titanium alloy to 304 stainless steel[J].Transactions of the China Welding Institution,2010,31(5):53-56.
[3]Wang T,Zhang B,Feng J,et al.Effect of a copper filler metal on the microstructure and mechanical properties of electron beam welded titanium-stainless steel joint[J].Materials Characterization,2012,73:104-113.
[4]Lee M K,Lee J G,Choi Y H,et al.Interlayer engineering for dissimilar bonding of titanium to stainless steel[J].Materials Letters,2010,64:1105-1108.
[5]王廷,张秉刚,张艳娇,等.采用不同结构Cu/V填充层的钛合金/不锈钢电子束焊接试验[J].焊接学报,2014,35(8):71-74.Wang Ting,Zhang Binggang,Zhang Yanjiao,et al.Experimental research on electron beam welding of titanium to stainless steel based on Cu/V filler metals with different shapes[J].Transactions of the China Welding Institution,2014,35(8):71-74.
[6]Wang T,Zhang B,Chen G.High strength electron beam welded titanium-stainless steel joint with V/Cu based composite filler metals[J].Vacuum,2013,94(6):41-47.
[7]Chu Q,Zhang M,Li J.Experimental investigation of explosionwelded CP-Ti/Q345 bimetallic sheet filled with Cu/V based fluxcored wire[J].Materials and Design,2015,67:606-614.
[8]He P,Zhang J,Zhou R,et al.Diffusion bonding technology of titanium alloy to stainless steel with Ni interlayer[J].Materials Characterization,1999,43(5):287-292.
[9]Kundu S,Chatterjee S.Characterization of diffusion bonded joint between titanium and 304 stainless steel using a Ni interlayer[J].Materials Characterization,2008,59(5):631-637.
[10]Dharmendra C,Rao KP,Wilden J,et al.Study on laser weldingbrazing of zinc coated steel to aluminium alloy with a zinc based filler[J].Materials Science and Engineering A,2011,528:1497-1503.
[11]Froes F H.Titanium:Physical metallurgy,processing and applications[M].Ohio:ASM International,2015.
[12]Bo H,Duarte L I,Zhu W J,et al.Experimental study and thermodynamic assessment of the Cu-Fe-Ti system[J].Calphad:Computer Coupling of Phase Diagrams and Thermochemistry,2013,40:24-33.
[13]Beek J A V,Kodentsov A A,Loo F J J V.Phase equilibria in the Cu-Fe-Ti system at 1123 K[J].Journal of Alloys and Compounds,1995,217(1):97-103.