TA23合金不同焊接方法接头组织性能研究
|
摘要
采用CMT、TIG和EBW焊对TA23合金进行焊接,对比分析了不同焊接方法下接头微观组织和力学性能的差异。结果表明,焊接热输入直接影响焊缝晶粒尺寸和焊接接头宽度,TIG焊缝晶粒尺寸最大,CMT次之,EBW最小;EBW接头宽度为5 mm,CMT接头宽度为7 mm,TIG接头达14 mm;3种焊接方法焊缝区域组织均由马氏体α相、片层状α相和残余β相组成,热影响区组织形态介于焊缝和母材组织形态之间;3种焊接方法焊缝区显微硬度和接头抗拉强度均大于母材,其中EBW焊缝区显微硬度值最大,TIG焊接头抗拉强度最高,CMT焊缝显微硬度和接头抗拉强度均居中。
TA23 alloy sheets were welded by CMT, TIG and EBW, and the study on the microstructures and mechanical properties of the welded joints were carried out. The results showed that the welding heat input directly influenced the size of grain and the width of the joints; The size of grain by TIG process was the largest, followed by that by CMT, while the size of grain by EBW was the smallest; The width of the joint by EBW was 5 mm, the width by CMT 7 mm, and the width by TIG 14 mm; Microstructures of welded seams created by the three welding processes mainly consisted of martensite α, lamellar α and residual β phases, while the microstructures of HAZ was between those of welded seams and base metal; The micro-hardnesses and tensile strengths of the welded seams from the three processes were higher than those of the base metal, of which the micro-hardness of the EBW joint was the highest and the tensile strength of TIG was the highest, while the properties of CMT joint are between those of TIG and EBW.
TA23 alloy sheets were welded by CMT, TIG and EBW, and the study on the microstructures and mechanical properties of the welded joints were carried out. The results showed that the welding heat input directly influenced the size of grain and the width of the joints; The size of grain by TIG process was the largest, followed by that by CMT, while the size of grain by EBW was the smallest; The width of the joint by EBW was 5 mm, the width by CMT 7 mm, and the width by TIG 14 mm; Microstructures of welded seams created by the three welding processes mainly consisted of martensite α, lamellar α and residual β phases, while the microstructures of HAZ was between those of welded seams and base metal; The micro-hardnesses and tensile strengths of the welded seams from the three processes were higher than those of the base metal, of which the micro-hardness of the EBW joint was the highest and the tensile strength of TIG was the highest, while the properties of CMT joint are between those of TIG and EBW.
引文
[1] 王悔改,宋延沛.HF-HNO3体系中Ti70合金的电化学腐蚀行为[J].腐蚀与防护,2013,34(10):914—917.
[2] 孙建科,孟祥军,陈春和,等.我国船用铁合金研究、应用及发展[J].金属学报,2002,38(增刊1) :33—36.
[3] 杨修荣.超薄板的CMT冷金属过渡技术[J].焊接,2005( 12 ):52—54.
[4] 柳军,郭小辉,何刚,等.不同焊接方法对TA2焊缝变形与应力的影响[J].材料开发与应用,2013,28(5):14—17.
[5] CAO R,FENG Z,LIN Q,et al.Study on cold metal transfer welding-brazing of titanium to copper[J].Materials and Design,2014(56):165—173.
[6] LI J Z,SUN Q J,LIU Y B,et al.Cold metal transfer welding-brazing of pure titanium TA2 to aluminum alloy 6061-T6[J].Advanced Engineering Metarials,2017,19(2):1600494.
[7] SUN Q J,LI J Z,LIU Y B,et al.Microstructural characterization and mechanical properties of Al/Ti joint welded by CMT method-assisted hybrid magnetic field[J].Materials and Design,2017(116):316—324.
[8] 乔亮,苏轩,陶汪,等.TC4钛合金不同焊接工艺下组织性能对比[J].热加工工艺,2016,45 (3):19—22.
[9] 安飞鹏,熊进辉,李士凯,等.深潜器用Ti80厚板电子束焊接接头组织性能研究[J].2017(2):62—66.
[2] 孙建科,孟祥军,陈春和,等.我国船用铁合金研究、应用及发展[J].金属学报,2002,38(增刊1) :33—36.
[3] 杨修荣.超薄板的CMT冷金属过渡技术[J].焊接,2005( 12 ):52—54.
[4] 柳军,郭小辉,何刚,等.不同焊接方法对TA2焊缝变形与应力的影响[J].材料开发与应用,2013,28(5):14—17.
[5] CAO R,FENG Z,LIN Q,et al.Study on cold metal transfer welding-brazing of titanium to copper[J].Materials and Design,2014(56):165—173.
[6] LI J Z,SUN Q J,LIU Y B,et al.Cold metal transfer welding-brazing of pure titanium TA2 to aluminum alloy 6061-T6[J].Advanced Engineering Metarials,2017,19(2):1600494.
[7] SUN Q J,LI J Z,LIU Y B,et al.Microstructural characterization and mechanical properties of Al/Ti joint welded by CMT method-assisted hybrid magnetic field[J].Materials and Design,2017(116):316—324.
[8] 乔亮,苏轩,陶汪,等.TC4钛合金不同焊接工艺下组织性能对比[J].热加工工艺,2016,45 (3):19—22.
[9] 安飞鹏,熊进辉,李士凯,等.深潜器用Ti80厚板电子束焊接接头组织性能研究[J].2017(2):62—66.