镁质球团矿的研究现状与应用进展
|
摘要
综合国内球团矿的试验研究和生产实践,简要介绍了镁质球团矿的研究背景及MgO改善球团矿高温性能的基理,重点阐述了镁质添加剂及生产工艺的选择,论述了不同MgO/SiO_2比值对球团矿高温性能的影响,并列举、分析了镁质球团矿在高炉实践中的应用情况。
According to the domestic experimental researches and production practices of MgO-containing pellets, the research background in terms of MgO-containing pellets and the basic mechanism for improving the high temperature behavior of the pellets by adding MgO were introduced briefly. Particularly the magnesian additive agents and selections of productive technologies were explained. And then the effect of different ratios of MgO to SiO_2 on the high temperature behavior of pellets was discussed. Finally the applications of MgO-containing pellets for ironmaking in BF were analyzed by the enumeration method.
According to the domestic experimental researches and production practices of MgO-containing pellets, the research background in terms of MgO-containing pellets and the basic mechanism for improving the high temperature behavior of the pellets by adding MgO were introduced briefly. Particularly the magnesian additive agents and selections of productive technologies were explained. And then the effect of different ratios of MgO to SiO_2 on the high temperature behavior of pellets was discussed. Finally the applications of MgO-containing pellets for ironmaking in BF were analyzed by the enumeration method.
引文
[1]任伟,杨熙鹏,孙俊波,等.富镁膨润土用于铁矿球团的试验研究[C]//2014年全国炼铁生产技术会暨炼铁学术年会文集(上).郑州:中国金属学会,2014:436-442.
[2]周明顺,翟立委,李艳茹.鞍钢烧结矿适宜Mg O含量的试验研究[J].烧结球团,2005,30(6):1-4.
[3]谭德波,节永烈,龙红明.马钢生产镁质球团的工业试验[J].烧结球团,2011,36(2):28-31.
[4]吴锦文,李贵松,许彦斌.氧化镁对酸性球团冶金性能的影响[J].烧结球团,1983(4):14-22.
[5]宋招权.Mg O对球团矿质量的影响[J].烧结球团,2001,26(6):22-24.
[6]范晓慧,谢路奔,甘敏,等.高镁球团焙烧特性及其固结强化机理[J].中南大学学报(自然科学版),2013,44(2):449-454.
[7]青格勒,吴铿,刘洪松,等.焙烧温度对低硅含镁球团矿还原膨胀率的影响及机理[J].中国有色金属学报,2015,25(10):2901-2912.
[8]侯恩俭,王斌,马文,等.鞍钢球团矿添加镁质复合粘结剂的研究[J].鞍钢技术,2017(4):10-14.
[9]张树江,蒋中秋,朱立光,等.球团矿添加镁质添加剂的研究[J].河北理工大学学报(自然科学版),2011,33(4):22-23.
[10]朱晓航.鲅鱼圈链篦机—回转窑镁质球团矿的开发研究[D].辽宁:辽宁科技大学,2014.
[11]张贤平.球团理论的工业运用与鞍钢球团经济技术指标的比较[D].辽宁:辽宁科技大学,2007.
[12]谢路奔.含镁球团焙烧固结强化及其机理研究[D].湖南:中南大学,2012.
[13]孙涛,孙广伟,陈伟,等.球团配加高镁精矿改善冶金性能的工业试验[J].河南冶金,2014,22(4):8-9(22).
[14]王代军,吴胜利.赤铁矿制备镁球团矿的研究与应用[J].钢铁,2015,50(10):19-25.
[15]黄永君,周明顺,翟立委,等.铁矿球团适宜Mg O/Si O2比值的试验研究[J].鞍钢技术,2008(3):14-17.
[16]李艳茄,李金莲,任伟.高效镁质添加剂用于铁矿球团的试验研究[J].钢铁,2010,45(5):17-19.
[17]张晓萍,金俊,覃德波,等.马钢生产镁质球团矿的可行性研究[J].烧结球团,2010,35(5):16-19.
[18]周国凡,杨福.添加Mg O对球团矿成球性能及强度的影响[J].钢铁研究,2009,37(2):10-12.
[19]邬虎林,薛向欣,陈革,等.含氟氧化镁球团矿的研究与实践[J].钢铁,2005,40(7):9-12.
[20]许天龙,夏涛,丁文虎.高炉冶炼含Mg O球团矿的实践[J].炼铁技术通讯,2005(3):9-10.
[21]李崇贵,张云平,胡焕琼,等.球团添加镁粉生产试验[J].烧结球团,2012,37(5):40-44.
[22]姜鑫.高炉炉料中合理利用含Mg O原料的基础理论研究[D].辽宁:东北大学,2008
[23]隋孝利,王英杰,牛宏伟,等.承钢圆形竖炉焙烧镁质球团的研究[J].烧结球团,2015,40(1):28-31.
[24]贺建峰,刘国防.济钢生产镁质球团矿的试验研究与实践[J].山东冶金,2011,33(1):31-33.
[25]刘文旺,李明,青格勒,等.首钢京唐高镁球团工业试验[J].烧结球团,2012,37(5):36-39.
[26]李崇贵,张云平,胡焕琼,等.球团添加镁粉生产试验[J].烧结球团,2012,37(5):40-44.
[27]严纪文,曾才兵.配加高镁精矿提高球团矿Mg O含量的实践[J].烧结球团,2012,36(4):28-31.
[28]王英杰.高镁质球团矿的生产实践[J].北方钒钛,2014(4):1-3.
[29]周明顺,沈峰满,翟立委,等.Mg O添加方式对改善球团矿冶金性能的影响[J].钢铁,2012,47(4):14-18.
[30]吴迪.钒钛烧结矿工艺优化研究[J].河北冶金,2016,249(9):25-27.
[31]隋孝利,王英杰,牛宏伟,等.承钢圆形竖炉焙烧镁质球团的研究[J].烧结球团,2015,40(1):28-31.
[2]周明顺,翟立委,李艳茹.鞍钢烧结矿适宜Mg O含量的试验研究[J].烧结球团,2005,30(6):1-4.
[3]谭德波,节永烈,龙红明.马钢生产镁质球团的工业试验[J].烧结球团,2011,36(2):28-31.
[4]吴锦文,李贵松,许彦斌.氧化镁对酸性球团冶金性能的影响[J].烧结球团,1983(4):14-22.
[5]宋招权.Mg O对球团矿质量的影响[J].烧结球团,2001,26(6):22-24.
[6]范晓慧,谢路奔,甘敏,等.高镁球团焙烧特性及其固结强化机理[J].中南大学学报(自然科学版),2013,44(2):449-454.
[7]青格勒,吴铿,刘洪松,等.焙烧温度对低硅含镁球团矿还原膨胀率的影响及机理[J].中国有色金属学报,2015,25(10):2901-2912.
[8]侯恩俭,王斌,马文,等.鞍钢球团矿添加镁质复合粘结剂的研究[J].鞍钢技术,2017(4):10-14.
[9]张树江,蒋中秋,朱立光,等.球团矿添加镁质添加剂的研究[J].河北理工大学学报(自然科学版),2011,33(4):22-23.
[10]朱晓航.鲅鱼圈链篦机—回转窑镁质球团矿的开发研究[D].辽宁:辽宁科技大学,2014.
[11]张贤平.球团理论的工业运用与鞍钢球团经济技术指标的比较[D].辽宁:辽宁科技大学,2007.
[12]谢路奔.含镁球团焙烧固结强化及其机理研究[D].湖南:中南大学,2012.
[13]孙涛,孙广伟,陈伟,等.球团配加高镁精矿改善冶金性能的工业试验[J].河南冶金,2014,22(4):8-9(22).
[14]王代军,吴胜利.赤铁矿制备镁球团矿的研究与应用[J].钢铁,2015,50(10):19-25.
[15]黄永君,周明顺,翟立委,等.铁矿球团适宜Mg O/Si O2比值的试验研究[J].鞍钢技术,2008(3):14-17.
[16]李艳茄,李金莲,任伟.高效镁质添加剂用于铁矿球团的试验研究[J].钢铁,2010,45(5):17-19.
[17]张晓萍,金俊,覃德波,等.马钢生产镁质球团矿的可行性研究[J].烧结球团,2010,35(5):16-19.
[18]周国凡,杨福.添加Mg O对球团矿成球性能及强度的影响[J].钢铁研究,2009,37(2):10-12.
[19]邬虎林,薛向欣,陈革,等.含氟氧化镁球团矿的研究与实践[J].钢铁,2005,40(7):9-12.
[20]许天龙,夏涛,丁文虎.高炉冶炼含Mg O球团矿的实践[J].炼铁技术通讯,2005(3):9-10.
[21]李崇贵,张云平,胡焕琼,等.球团添加镁粉生产试验[J].烧结球团,2012,37(5):40-44.
[22]姜鑫.高炉炉料中合理利用含Mg O原料的基础理论研究[D].辽宁:东北大学,2008
[23]隋孝利,王英杰,牛宏伟,等.承钢圆形竖炉焙烧镁质球团的研究[J].烧结球团,2015,40(1):28-31.
[24]贺建峰,刘国防.济钢生产镁质球团矿的试验研究与实践[J].山东冶金,2011,33(1):31-33.
[25]刘文旺,李明,青格勒,等.首钢京唐高镁球团工业试验[J].烧结球团,2012,37(5):36-39.
[26]李崇贵,张云平,胡焕琼,等.球团添加镁粉生产试验[J].烧结球团,2012,37(5):40-44.
[27]严纪文,曾才兵.配加高镁精矿提高球团矿Mg O含量的实践[J].烧结球团,2012,36(4):28-31.
[28]王英杰.高镁质球团矿的生产实践[J].北方钒钛,2014(4):1-3.
[29]周明顺,沈峰满,翟立委,等.Mg O添加方式对改善球团矿冶金性能的影响[J].钢铁,2012,47(4):14-18.
[30]吴迪.钒钛烧结矿工艺优化研究[J].河北冶金,2016,249(9):25-27.
[31]隋孝利,王英杰,牛宏伟,等.承钢圆形竖炉焙烧镁质球团的研究[J].烧结球团,2015,40(1):28-31.