激光焊焊前预热和焊后热处理对焊缝质量的影响
|
摘要
为了研究激光焊接热处理工艺对焊缝组织和性能的影响,制定了焊前预热和焊后热处理的试验方案。采用金相显微镜和扫描电镜对焊缝组织观察分析,并用HV0.1显微硬度计检测焊缝区域硬度。结果表明,经过焊前预热和焊后热处理的金相组织铁素体明显增多,而珠光体较少,硬度较低,其中焊后热处理对组织和性能改善的最为显著。
In order to study the effect of laser welding heat treatment process on the microstructure and properties of weld,pre-welding and post-welding heat treatment were established. Metallographic microscope and scanning electron microscope were used to observe and analyze the microstructure of the weld,and used HV0.1 microhardness tester to measure the hardness of the weld area. The results showed that by means of pre-welding and post-welding heat treatment, the ferrite in the metallographic structure increased obviously,while the pearlite was less and the hardness was lower,especially the post-welding heat treatment improved the microstructure and properties most significantly.
In order to study the effect of laser welding heat treatment process on the microstructure and properties of weld,pre-welding and post-welding heat treatment were established. Metallographic microscope and scanning electron microscope were used to observe and analyze the microstructure of the weld,and used HV0.1 microhardness tester to measure the hardness of the weld area. The results showed that by means of pre-welding and post-welding heat treatment, the ferrite in the metallographic structure increased obviously,while the pearlite was less and the hardness was lower,especially the post-welding heat treatment improved the microstructure and properties most significantly.
引文
[1]倪加明,李铸国,吴毅雄.殷瓦薄板高速激光焊接的热裂纹敏感性[J].中国激光,2011,38(4):1-4.
[2]朱萍.浅谈薄壁管和管塞的焊接[J].机电信息,2018(27):103-105.
[3]刘占起,张文明,王新宇.机器人在薄板焊接中的应用[J].电焊机,2016,46(10):66-68.
[4]陈根余,周宇,张明军,等.大功率光纤激光厚板自熔焊焊缝表面质量改善研究[J].中国激光,2013,40(11):137-142.
[5]黄坚,李铸国,唐新华.中厚板的高功率激光焊接[J].航空制造技术,2010(2):27-29.
[2]朱萍.浅谈薄壁管和管塞的焊接[J].机电信息,2018(27):103-105.
[3]刘占起,张文明,王新宇.机器人在薄板焊接中的应用[J].电焊机,2016,46(10):66-68.
[4]陈根余,周宇,张明军,等.大功率光纤激光厚板自熔焊焊缝表面质量改善研究[J].中国激光,2013,40(11):137-142.
[5]黄坚,李铸国,唐新华.中厚板的高功率激光焊接[J].航空制造技术,2010(2):27-29.