摘要
采用化学激发的手段来提高微碳铬铁粉渣的早期活性及微碳铬铁粉渣制品的强度。研究结果表明:激发剂Na_2CO_3、Na_2SO_4、硫铝酸盐水泥对于微碳铬铁粉渣浆体均具有比较好的调凝作用,激发剂Na_2CO_3、Na_2SO_4、普通硅酸盐水泥对于微碳铬铁粉渣发泡浆体的强度均有激发作用,以Na_2CO_3的效果最好。复掺Na_2CO_3和普通硅酸盐水泥,微碳铬铁粉渣发泡浆体的强度较单掺有显著提高,通过选择适当的配比,可以配置出符合工程需要的微碳铬铁粉渣发泡砌块。
The method of chemical activation was used to improve the early activity of micro carbon ferrochrome slag and the strength of micro carbon ferrochrome slag products.The result shows that: The activators of Na_2CO_3,Na_2SO_4 and sulphoaluminate cement have better coagulation adjusting effect on the micro carbon ferrochromium slag powder slurry.The activators of Na_2CO_3,Na2SO_4 and Portland cement have excitation effect on the strength of micro carbon ferrochromium slag powder foam slurry,and the best one is Na_2CO_3.Mixing Na_2CO_3 and Portland cement with micro carbon ferrochromium powder at the appropriate ratio,the strength of its slurry foaming block is significantly increased.With the appropriate ratio,the micro carbon ferrochromium slag powder foam block can be configured to meet engineering needs.
引文
[1]丁少良,邱伟坚.从微碳铬铁渣中回收金属的试验[J].铁合金,1992(2):44-46.
[2]郭军,李松峰,宣兆军.中、低碳铬铁炉渣抗粉化的试验研究[J].铁合金,2013(4):17-19.
[3]陈永浓,王俐.用微碳铬铁粉渣作水泥活性混合材[J].重庆环境科学,1993,15(4):61-62.
[4]茅涟,何文伟,潘健武.微碳铬铁渣的综合利用—MS型彩色水泥的研制[J].上海金属,1990,12(2):45-48.
[5]刘柏杨,杨玉飞,岳波,黄启飞.铬铁渣资源化利用技术研究现状及发展趋势[J].环境工程,2016,34(S1):679-683.
[6]杨南如,岳文海.无机非金属材料图谱手册[M].武汉:武汉工业大学出版社,2000.65-92.