聚苯硫醚合成过程中钠盐分离的研究
|
摘要
在聚苯硫醚生产过程中采用过滤的方式将产品和钠盐分离,考察了滤网目数和过滤速率对分离效果的影响。通过红外、热分析、钠含量以及灰分的测试对产品进行了表征测试。结果表明:在600 L反应釜中,当滤网目数为600目,过滤速率在800 L/h时,该法可将钠盐从聚苯硫醚反应物料中较好地分离出来,分离率为93.0%。
The product and sodium salt were separated by filtration in the synthesis process of PPS. The effects of mesh number and filtration rate on the separation efficiency were investigated. The product was characterized by IR and DSC, and the sodium content and ash were tested. The results show that the sodium salt can be separated from the PPS reaction material with a separation rate of 93.0% by this method in a 600 L reactor, when the mesh number is 600 and the filtration rate is 800 L/h.
The product and sodium salt were separated by filtration in the synthesis process of PPS. The effects of mesh number and filtration rate on the separation efficiency were investigated. The product was characterized by IR and DSC, and the sodium content and ash were tested. The results show that the sodium salt can be separated from the PPS reaction material with a separation rate of 93.0% by this method in a 600 L reactor, when the mesh number is 600 and the filtration rate is 800 L/h.
引文
[1] 张翔,刘钊,王孝军,等.PPS/PA66/GF复合材料的制备及性能研究[J].中国塑料,2018,32(10):20-26.
[2] 严光明,李艳,李志敏,等.聚芳硫醚树脂的合成、性能及应用发展概况[J].中国材料进展,2015,34(12):877-882.
[3] 徐俊怡,刘钊,洪瑞,等.聚苯硫醚的产业发展概况与复合改性进展[J].中国材料进展,2015,34(12):883-888.
[4] 时盼盼,王明明,姜一男,等.低熔点线形高相对分子质量聚苯硫醚的制备[J].当代化工,2016,45(10):2277-2279.
[5] 衡林,杨永彬,刘建容.碱金属醋酸盐催化合成高线型聚苯硫醚[J].石油化工,2016,45(5):564-569.
[6] 沈发治.无机盐Na2S加压合成聚苯硫醚树脂工艺研究[J].现代盐化工,2015(6):5-9.
[7] 邢剑,刘志,阮芳涛,等.聚苯硫醚及其纤维的抗氧化改性研究进展[J].合成纤维工业,2018,37(4):46-51.
[8] 赵一兰,胡程耀,魏春,等.聚酰亚胺表面处理玻璃纤维/环氧树脂复合材料力学性能[J].复合材料学报,2018,35(7):1850-1856.
[9] 程丽,薛平,金志明.聚苯硫醚改性方法及成型研究进展[J].工程塑料应用,2015,43(11):118-121.
[10] 张坤,龚跃武,张守玉,等.界面改性剂对聚苯硫醚/碳纤维复合材料力学和热力学性能的影响[J].塑料工业,2013,41(1):100-103.
[11] 卫晓明,陈建野,王孝军,等.环氧树脂对PPS/PA6合金形貌及性能影响的研究[J].塑料工业,2011,39(2):33-36.
[12] 高晓薇,张爱欣,张旭.东丽聚苯硫醚生产工艺专利状况分析[J].新材料产业,2017(8):44-48.
[13] 郭强宗,王彦宁.聚苯硫醚反应过程中钠盐分离的研究[J].当代化工,2018,47(1):53-55.
[14] 雷连英,余晓平,郭亚飞,等.聚苯硫醚(PPS)生产废盐中微量硫化物分析方法研究[J].盐科学与化工,2017,46(12):28-32.
[15] 王欢,李珑,李晶,等.聚苯硫醚副产物综合利用研究进展[J].盐科学与化工,2017,46(7):9-12.
[16] 周美进,邓飞.聚苯硫醚高盐有机生产废水工业化处理技术路线分析[J].合成技术及应用,2018,33(2):49-52.
[2] 严光明,李艳,李志敏,等.聚芳硫醚树脂的合成、性能及应用发展概况[J].中国材料进展,2015,34(12):877-882.
[3] 徐俊怡,刘钊,洪瑞,等.聚苯硫醚的产业发展概况与复合改性进展[J].中国材料进展,2015,34(12):883-888.
[4] 时盼盼,王明明,姜一男,等.低熔点线形高相对分子质量聚苯硫醚的制备[J].当代化工,2016,45(10):2277-2279.
[5] 衡林,杨永彬,刘建容.碱金属醋酸盐催化合成高线型聚苯硫醚[J].石油化工,2016,45(5):564-569.
[6] 沈发治.无机盐Na2S加压合成聚苯硫醚树脂工艺研究[J].现代盐化工,2015(6):5-9.
[7] 邢剑,刘志,阮芳涛,等.聚苯硫醚及其纤维的抗氧化改性研究进展[J].合成纤维工业,2018,37(4):46-51.
[8] 赵一兰,胡程耀,魏春,等.聚酰亚胺表面处理玻璃纤维/环氧树脂复合材料力学性能[J].复合材料学报,2018,35(7):1850-1856.
[9] 程丽,薛平,金志明.聚苯硫醚改性方法及成型研究进展[J].工程塑料应用,2015,43(11):118-121.
[10] 张坤,龚跃武,张守玉,等.界面改性剂对聚苯硫醚/碳纤维复合材料力学和热力学性能的影响[J].塑料工业,2013,41(1):100-103.
[11] 卫晓明,陈建野,王孝军,等.环氧树脂对PPS/PA6合金形貌及性能影响的研究[J].塑料工业,2011,39(2):33-36.
[12] 高晓薇,张爱欣,张旭.东丽聚苯硫醚生产工艺专利状况分析[J].新材料产业,2017(8):44-48.
[13] 郭强宗,王彦宁.聚苯硫醚反应过程中钠盐分离的研究[J].当代化工,2018,47(1):53-55.
[14] 雷连英,余晓平,郭亚飞,等.聚苯硫醚(PPS)生产废盐中微量硫化物分析方法研究[J].盐科学与化工,2017,46(12):28-32.
[15] 王欢,李珑,李晶,等.聚苯硫醚副产物综合利用研究进展[J].盐科学与化工,2017,46(7):9-12.
[16] 周美进,邓飞.聚苯硫醚高盐有机生产废水工业化处理技术路线分析[J].合成技术及应用,2018,33(2):49-52.