改性聚丙烯被广泛的应用于汽车内外饰件上,是用量最大的车用塑料。但因其表面硬度相对较低,在使用中容易被划伤发白,影响外观。因此,配方中常需添加耐刮擦剂。本文对改性聚丙烯经氙灯光老化和高温热老化后的耐刮擦性进行了研究,发现老化后耐刮擦性出现不同程度的下降。从而对改性聚丙烯长期使用中耐刮擦性能的评估具有一定参考意义。
Modified polypropylene is widely used in automotive interior and exterior trims and is the most used automotive plastic. However, due to its relatively low surface hardness, it is easily scratched, then affecting the appearance. Therefore, it is often necessary to add a scratch-resistant agent to the formulation. In this paper, the scratch resistance of modified polypropylene after aging was studied. It was found that the scratch resistance after aging showed a different degree of decline. Therefore, it has reference significance for the evaluation of scratch resistance of modified polypropylene in long-term use.
引文
[1]黄险波,罗忠富,杨波.车用聚丙烯改性材料技术及应用[M].北京:科学出版社,2016.11.
[2]林秀玲.乘用车注塑外观塑料零件刮擦性能研究[J].合成材料老化与应用,2012,41(3):40-44.
[3]傅轶,唐昌伟,彭志宏,等.耐刮擦、软触感聚丙烯的制备与表征[J].合成材料老化与应用,2015,44(4):22-24.
[4]袁海兵.硅酮耐刮擦剂对车用PP复合材料性能的影响[J].工程塑料应用,2017,45(9):120-124.
[5]张立娟,戴婷,张超.车用塑料耐刮擦测试方法概述[J].广州化学,2014,39(3):68-72.
[6]SAE J2412-2015-08,(R)Accelerated Exposure of Automotive Interior Trim Components Using a Controlled Irradiance XenonArc Apparatus[S].