针对甘肃某氧化型锰矿进行了工艺矿物学及选矿试验研究,原矿中Mn含量为21.48%。通过重选方法 "原矿-磨矿-重选"工艺,可得到锰品位25.50%,回收率为58.73%,尾矿中锰17.10%,损失率41.27%。通过原矿-磨矿-湿式强磁选工艺,在-0.074 mm含量为68.45%,用1650 mT的磁场强度下进行湿式强磁选所得到的锰精矿和尾矿,锰精矿含锰28.75%,回收率55.59%,尾矿中含锰15.96%,损失率为44.41%。将试验所获得的"精矿+中矿"合并焙烧后锰精矿锰品位可提高到29.21%以上,质量达到国标冶金用锰矿石A类A5Ⅱ组标准。
The process mineralogy and minernal processing experimental study of one oxidized manganese ore in Gansu was carried out,the Mn content in raw ore is 21. 48%. The manganese with the grade 25. 50%,and recovery rate 58. 73% can be got,the manganese content in tailings is 17. 10%,and the loss ratio is 41. 27% by means of the gravity separation method that "raw ore-ore grindinggravity separation". Under the conditions that the mesh of grind is-0. 074 mm,the proportion is 68. 45%,by means of raw ore-ore grinding-wet high-intensity magnetic separation process,the manganese concentrate and tailings can be get under 1650 mT magnetic field intensity by wet high-intensity magnetic separation,that the manganese content in manganese concentrate is 28. 75%,the recovery rate is 55. 59%,the manganese content in tailings is 15. 96%,the loss ratio is 44. 41%. The "concentrate + middlings" obtained from the test shall be roasted mixed,and the manganese grade of the manganese concentrate can be improved to above 29. 21%,which quality can reach to A5 Ⅱgroup standard,Class A of the National Standard about Metallurgical manganese ore.
引文
[1]朱志刚.中国锰矿资源开发利用现状[J].中国锰业,2016,34(2):1-3.
[2]李小英,李俊.低品位含磷锰矿脱磷提锰研究[J].云南冶金,2016,45(6):33-38.
[3]李国栋,魏志聪.云南某低品位软锰矿强磁选工艺研究[J].中国锰业,2016,34(1):29-31,36.
[4]林海.某银锰矿矿泥选矿工艺试验[J].现代矿业,2017(6):120-123.
[5]杨永斌,吕鹏,李骞.某高铁菱锰矿选矿试验研究[J].矿冶工程,2017,37(2):68-70.
[6]谭鑫,蔡化文,黄成宝.广西天等锰矿碳酸锰选矿现状及发展方向[J].中国锰业,2017,35(4):17-19.
[7]潘加彬,刘子帅.广西某低品位碳酸锰矿选矿试验研究[J].云南冶金,2016,45(4):25-28.