摘要
研究硫化体系、硫化时间和补强体系对氯丁橡胶(CR)2442在深海环境下性能的影响。结果表明:硫化时间为60min时胶料的拉伸强度最大;增加1份炭黑N550或白炭黑能使CR2442胶料的硬度增大0. 5或0. 4度左右;最终优化配方为CR2442 100,炭黑N550 20,白炭黑10,氧化锌4,氧化镁2,芳烃油14,硬脂酸0. 5,防老剂RD 1,防老剂4010 2,硫黄2,促进剂DM 0. 15,相应胶料性能满足深海环境水密接插件性能要求。
The influence of curing system,curing time and reinforcement system on the properties of chloroprene rubber 2442(CR2442) for deep sea watertight connectors were investigated. The results showed that,the tensile strength of the compound was the best as the curing time was 60 min. The hardness of CR2442 compound could increase by 0. 4~0. 5 degree as the addition level of carbon black N550 or silica increased by 1 phr. The optimal formulation was as follows:CR2442 100,carbon black N550 20,silica10,ZnO 4,MgO 2,aromatic oil 14,stearic acid 0. 5,antioxidant RD 1,antioxidant 4010 2,sulfur 2,and accelerator DM 0. 15. The properties of the compound met the requirements of deep sea watertight connector.
引文
[1]Choi Sung-Seen,Han Dong-Hun.Recovery Prediction of Thermally Aged Chloroprene Rubber Composite Using Deformation Test[J].Journal of Applied Polymer Science,2008,110(6):3560-3565.
[2]Takenoshita Yoichiro.Update on Process in Chloroprene Rubber(CR)[J].Journal of the Society of Rubber Industry,2005,78(2):81-82.
[3]陶长元,薛红涛,刘作华,等.聚二乙烯基乙炔的氢氯化改性[J].化工进展,2011,30(s1):613-614.
[4]许宗超,温世鹏,彭同恺,等.氧化石墨烯/氯丁橡胶复合材料的制备与性能研究[J].橡胶工业,2017,64(4):202-206.
[5]代高峰,黄环宇,刘民英,等.硅氧烷硫化体系对药用氯化丁基橡胶塞性能的影响[J].橡胶工业,2016,63(1):22-26.
[6]许建雄.氯丁橡胶加工与应用[M].北京:化学工业出版社,2011:3.
[7]杨茹欣,何颖,牛承祥,等.国内外氯丁橡胶产需分析与发展前景展望[J].世界橡胶工业,2009,36(6):46-48.
[8]张泗文.氯丁橡胶在向高性能发展[J].合成橡胶工业,1992,15(3):131-134.
[9]Sae-oui P,Sirisinha C,Thepsuwan U.Property Modification of Chloroprene Rubber by Addition of Ultra-fine Acrylic Rubber Powder[J].Plastics Rubber and Composites,2014,43(7):211-216.
[10]Ahmad G R,Lina H,Mansoureh N P,et al.Investigation of Diethylthiourea and Ethyl Isothiocyanate as Potent Skin Allergens in Chloroprene Rubber[J].Contact Dermatitis,2015,72(3):139-146.