摘要
研究了改变热处理工艺对使用真空感应+电渣重熔工艺冶炼、经锻造成型的ψ80 mmAM355不锈钢棒的力学性能的改进及相关机理。试验结果表明,与传统热处理工艺(1 070℃×1 h空冷+(-70℃)×8 h+200℃×2 h空冷)相比,新的热处理工艺(1 000℃×1 h空冷+(-70℃)×8 h+450℃×2 h空冷+200℃×2 h空冷)可使ψ80 mm AM355不锈钢棒得到较高的强度和硬度,并保留一定的塑韧性。新的热处理工艺处理的AM355不锈钢棒的抗拉强度可提高120 MPa、屈服强度可提高400 MPa、硬度可提高5HRC,同时,冲击吸收功可保持大于40 J。对该钢棒经2种热处理工艺后产生的碳化物的类型和析出行为进行了观察研究之后指出,淬火温度对AM355不锈钢的晶粒度、碳化物类型及分布、残余奥氏体的转变都具有较大的影响,M23C6型碳化物的存在对钢的强化非常重要。
Different heat treatment process on AM355 steel bars were searched, which were produced by VIM+ESR technique and forged into φ80mm. Mechanical properties were tested after different quench temperatures, followed by same deep cold and different temperature. The results show that, with a contrast of traditional heat treatment(1 070 ℃×1 h AC+(-70 ℃)×8 h+200 ℃×2 h AC), new heat treatment process(1 000 ℃×1 h AC+(-70 ℃)×8 h+450 ℃×2 h AC+200 ℃×2 h AC) can lead a rise of about 100 MPa in strength and 5HRC in hardness. Details of mechanical property are: Rm=1 630 MPa, Re=1 380 MPa, A=16%, Z=59%, impact energy 51 J, 50 HRC. Sorts and precipitations of carbides in this AM355 bar were carried out by SEM and TEM, and strengthening mechanism were also searched. In conclusion, the quenching temperature has main effect on grain size, carbides, remained austenite, etc., and the exist of M23C6 carbide can lead a high strength.
Different heat treatment process on AM355 steel bars were searched, which were produced by VIM+ESR technique and forged into φ80mm. Mechanical properties were tested after different quench temperatures, followed by same deep cold and different temperature. The results show that, with a contrast of traditional heat treatment(1 070 ℃×1 h AC+(-70 ℃)×8 h+200 ℃×2 h AC), new heat treatment process(1 000 ℃×1 h AC+(-70 ℃)×8 h+450 ℃×2 h AC+200 ℃×2 h AC) can lead a rise of about 100 MPa in strength and 5HRC in hardness. Details of mechanical property are: Rm=1 630 MPa, Re=1 380 MPa, A=16%, Z=59%, impact energy 51 J, 50 HRC. Sorts and precipitations of carbides in this AM355 bar were carried out by SEM and TEM, and strengthening mechanism were also searched. In conclusion, the quenching temperature has main effect on grain size, carbides, remained austenite, etc., and the exist of M23C6 carbide can lead a high strength.
引文
[1]孙永庆,杨志勇,梁剑雄,等.中国商用飞机高强度不锈钢的现状及发展趋势[J].钢铁研究学报,2009,21(6):1.
[2]刘长新,黄洁.我国不锈钢工业面临的形势及应采取的对策[J]中国冶金,1995,2(5):13.
[3]古立新,金建军.回火温度对1CrlSNi4Mo3N钢组织和性能的影响[J].材料工程,2007(1):7.
[4]杨晓燕,郭春河.某型机载投放装置锁制机构发生粘着磨损故障分析[J].航空兵器,2008(2):56.
[5]孙永庆,梁剑雄,杨志勇,等.化学成分和热处理对AM355不锈钢组织和力学性能的影响[J].钢铁,2011,48(5):68.
[6]赵振业.超高强度钢中二次硬化现象的研究[J].航空材料学报,2002,22(4):46.
[7]陆世英.不锈钢[M].北京:原子能出版社,1995.
[8]赵振业.合金钢设计[M].北京:国防工业出版社,1999.
[9]吴奎林,谭俊哲,曹铁山.热处理工艺对1Cr15Ni4Mo3N钢组织和性能的影响[J].理化检验:物理分册,2012,48(2):76.
[10]杨军,吴有彩.航天用1Crl5Ni4Mo3N不锈钢棒材研制总结[J].重庆工业高等专科学校学报,2002,17(10):117.
[11]雍岐龙.钢铁材料中的第二相[M].北京:冶金工业出版社,2006.
[12]赵先存,宋为顺,杨志勇,等.高强度超高强度不锈钢[M].北京:冶金工业出版社,2008.
[2]刘长新,黄洁.我国不锈钢工业面临的形势及应采取的对策[J]中国冶金,1995,2(5):13.
[3]古立新,金建军.回火温度对1CrlSNi4Mo3N钢组织和性能的影响[J].材料工程,2007(1):7.
[4]杨晓燕,郭春河.某型机载投放装置锁制机构发生粘着磨损故障分析[J].航空兵器,2008(2):56.
[5]孙永庆,梁剑雄,杨志勇,等.化学成分和热处理对AM355不锈钢组织和力学性能的影响[J].钢铁,2011,48(5):68.
[6]赵振业.超高强度钢中二次硬化现象的研究[J].航空材料学报,2002,22(4):46.
[7]陆世英.不锈钢[M].北京:原子能出版社,1995.
[8]赵振业.合金钢设计[M].北京:国防工业出版社,1999.
[9]吴奎林,谭俊哲,曹铁山.热处理工艺对1Cr15Ni4Mo3N钢组织和性能的影响[J].理化检验:物理分册,2012,48(2):76.
[10]杨军,吴有彩.航天用1Crl5Ni4Mo3N不锈钢棒材研制总结[J].重庆工业高等专科学校学报,2002,17(10):117.
[11]雍岐龙.钢铁材料中的第二相[M].北京:冶金工业出版社,2006.
[12]赵先存,宋为顺,杨志勇,等.高强度超高强度不锈钢[M].北京:冶金工业出版社,2008.