棉Coolcool纤维交织物的生产
|
摘要
总结细号棉纱与Coolcool纤维交织物的生产要点。以4.2tex×2精梳纯棉股线为经纱;以166.5dtex的Coolcool长丝包覆44.4dtex的氨纶长丝组成的弹力网络丝为纬纱,生产了一款小提花织物;介绍了络筒、整经、浆纱、织造和后整理各工序的工艺要点和采取的技术措施。最终保证了产品的顺利生产,织机效率达88%以上,十万纬经停4.4次,十万纬纬停9.6次,下机一等品率86.5%。认为:生产的织物细腻滑爽,吸湿透气,可用作高档衬衫面料。
Production key points of fine cotton yarn and Coolcool fiber interweave fabric was summarized.4.2 tex×2 combed cotton ply was used as warp,elastic interlaced yarn as weft which was composed of 166.5 dtex Coolcool fiber filament covered with 44.4 dtex spandex filament,a kind of mini-jacquard fabric was produced.Technology points and technology measures in winding,warping,sizing,weaving and after-finish were introduced.Finally the smooth production was ensured.Loom efficiency is above 88%.Warp stop times per 100 000 weft is 4.4.Weft stop times per 100 000 weft is 9.6.The first grade percentage before cloth repairing is up to 86.5%.It is considered that produced fabric is soft &comfort and has better hygroscopicity & permeability.It can be used as high-grade shirting fabric.
Production key points of fine cotton yarn and Coolcool fiber interweave fabric was summarized.4.2 tex×2 combed cotton ply was used as warp,elastic interlaced yarn as weft which was composed of 166.5 dtex Coolcool fiber filament covered with 44.4 dtex spandex filament,a kind of mini-jacquard fabric was produced.Technology points and technology measures in winding,warping,sizing,weaving and after-finish were introduced.Finally the smooth production was ensured.Loom efficiency is above 88%.Warp stop times per 100 000 weft is 4.4.Weft stop times per 100 000 weft is 9.6.The first grade percentage before cloth repairing is up to 86.5%.It is considered that produced fabric is soft &comfort and has better hygroscopicity & permeability.It can be used as high-grade shirting fabric.
引文
[1]李竹君,朱江波.高支高密纯棉色织免烫衬衫面料的开发与生产[J].纺织导报,2016(12):36-38.
[2]张增强.Coolcool纤维弹力牛仔织物的设计与开发[J].五邑大学学报,2006(1):31-34.
[3]司志奎,王芳玲.色织高支高密织物浆纱工艺的探讨[J].纺织导报,2016(12):39-41.
[4]卞镇,葛晓华.高支棉Cooldry交织面料的研制开发[J].天津纺织科技,2013(4):26-28.
[5]马顺彬.纯棉小提花织物的工艺设计[J].棉纺织技术,2017,45(3):74-76.
[6]钟婧,陈红霞,孟红彩.纯棉特细号高密绒类面料设计与开发[J].棉纺织技术,2016,44(11):69-72.
[7]朱江波,李竹君.棉/羊绒色织免烫面料的设计与开发[J].纺织导报,2016(2):50-52.
[2]张增强.Coolcool纤维弹力牛仔织物的设计与开发[J].五邑大学学报,2006(1):31-34.
[3]司志奎,王芳玲.色织高支高密织物浆纱工艺的探讨[J].纺织导报,2016(12):39-41.
[4]卞镇,葛晓华.高支棉Cooldry交织面料的研制开发[J].天津纺织科技,2013(4):26-28.
[5]马顺彬.纯棉小提花织物的工艺设计[J].棉纺织技术,2017,45(3):74-76.
[6]钟婧,陈红霞,孟红彩.纯棉特细号高密绒类面料设计与开发[J].棉纺织技术,2016,44(11):69-72.
[7]朱江波,李竹君.棉/羊绒色织免烫面料的设计与开发[J].纺织导报,2016(2):50-52.