摘要
采用红外衰减全反射(ATR)法测定三元乙丙橡胶(EPDM)中的乙烯含量,对聚乙烯、聚丙烯及EPDM特征谱带进行归属,绘制特征峰红外吸光度比值与乙烯含量的工作曲线,建立了ATR法测定乙烯含量的计算方法。该方法制样简单,环保快捷,测定样品的最大相对偏差为2.3%,重复性测定的相对标准偏差不大于0.5%。
Infrared attenuated total reflection(ATR)method in this article was used to determinate the ethylene content in EPDM rubber.The standard values of ethylene content were confirmed by NMR method to draw the standard curve of infrared absorbance ratio and ethylene content,through which the calculation method was get.The method has the advantages of simple operation and fast measurement.Maximum relative deviation of the samples is 2.3%,and relative standard deviation of repeatability is not greater than 0.5%.
Infrared attenuated total reflection(ATR)method in this article was used to determinate the ethylene content in EPDM rubber.The standard values of ethylene content were confirmed by NMR method to draw the standard curve of infrared absorbance ratio and ethylene content,through which the calculation method was get.The method has the advantages of simple operation and fast measurement.Maximum relative deviation of the samples is 2.3%,and relative standard deviation of repeatability is not greater than 0.5%.
引文
[1]杨清芝.实用橡胶工艺学[M].北京:化学工业出版社,2005.
[2]王秀萍,王博,张欣荣.三元乙丙橡胶的1 H-NMR定量分析[J].化工科技,2013,21(6):45-47.
[3]史新梅,潘铁英,王复,等.三元乙丙橡胶的13 C-NMR定量分析[J].分析测试学报,2002,21(2):51-54.
[4]郝军,王晓娟.傅立叶变换红外光谱法快速测定乙丙共聚物中的乙烯含量[J].应用化工,2009,38(5):752-754.
[5]俞雄飞,张伟,莫卫民.傅立叶红外光谱法测定丙烯-乙烯共聚物中丙烯单元含量[J].理化检验(化学分册),2007,43(12):1050-1052.
[6]叶煊,刘桂华,李延兵,等.红外光谱法测定乙丙橡胶中丙烯的含量[J].沈阳大学学报(自然科学版),1994(4):20-22.
[7]赵霞,徐广通,刘红梅,等.红外光谱结合偏最小二乘法快速测定二元乙丙橡胶中的结合乙烯量[J].石油炼制与化工,2011,42(12):78-81.
[8]宫立波,王博,孙文秀,等.基线校准红外光谱法快速测定三元乙丙橡胶中ENB单体含量[J].弹性体,2015,25(1):71-73.
[9]张之皖,林吟卿,韩玲玲.用红外光谱测定乙烯-丙烯共聚物的组成[J].化学通讯,1983(2):48-50.
[10]郝凤岭,田春光,尹香玉.红外光谱法测定二元乙丙橡胶中乙烯、丙烯组成[J].弹性体,2000,10(4):17-20.
[11]全国橡胶与橡胶制品标准化技术委员会合成橡胶分技术委员会.GB/T 21464-2008橡胶乙烯-丙烯-二烯烃(EPDM)三元共聚物中5-乙叉降冰片烯(ENB)或双环戊二烯(DCPD)含量的测定[S].北京:中国标准出版社,2008:1-9.
[12]王正熙.聚合物红外光谱分析和鉴定[M].成都:四川大学出版社,1989.
[2]王秀萍,王博,张欣荣.三元乙丙橡胶的1 H-NMR定量分析[J].化工科技,2013,21(6):45-47.
[3]史新梅,潘铁英,王复,等.三元乙丙橡胶的13 C-NMR定量分析[J].分析测试学报,2002,21(2):51-54.
[4]郝军,王晓娟.傅立叶变换红外光谱法快速测定乙丙共聚物中的乙烯含量[J].应用化工,2009,38(5):752-754.
[5]俞雄飞,张伟,莫卫民.傅立叶红外光谱法测定丙烯-乙烯共聚物中丙烯单元含量[J].理化检验(化学分册),2007,43(12):1050-1052.
[6]叶煊,刘桂华,李延兵,等.红外光谱法测定乙丙橡胶中丙烯的含量[J].沈阳大学学报(自然科学版),1994(4):20-22.
[7]赵霞,徐广通,刘红梅,等.红外光谱结合偏最小二乘法快速测定二元乙丙橡胶中的结合乙烯量[J].石油炼制与化工,2011,42(12):78-81.
[8]宫立波,王博,孙文秀,等.基线校准红外光谱法快速测定三元乙丙橡胶中ENB单体含量[J].弹性体,2015,25(1):71-73.
[9]张之皖,林吟卿,韩玲玲.用红外光谱测定乙烯-丙烯共聚物的组成[J].化学通讯,1983(2):48-50.
[10]郝凤岭,田春光,尹香玉.红外光谱法测定二元乙丙橡胶中乙烯、丙烯组成[J].弹性体,2000,10(4):17-20.
[11]全国橡胶与橡胶制品标准化技术委员会合成橡胶分技术委员会.GB/T 21464-2008橡胶乙烯-丙烯-二烯烃(EPDM)三元共聚物中5-乙叉降冰片烯(ENB)或双环戊二烯(DCPD)含量的测定[S].北京:中国标准出版社,2008:1-9.
[12]王正熙.聚合物红外光谱分析和鉴定[M].成都:四川大学出版社,1989.