摘要
Cold-rolled martensitic steel sheets are becoming widely applied in the automotive industry because of their ultra-high strength,which may result in satisfactory weight reduction. The grades of martensitic steel sheets are classified based on their tensile strength,which ranges from 980 to 1 700 MPa. The main applications include a series of structural parts of uniform cross-section or simple shape,such as bumper beams,door beams and door sills,etc. The study and development of cold-rolled martensitic steel sheets date back to 2007 in Baosteel,and some grades became commercially available in 2009. By 2015,Baosteel had commercially supplied thousands of tons of these steel sheets with tensile strength up to 1 400 MPa. Currently,1 500 MPa martensitic steel sheet is commercially available and 1 700 MPa martensitic steel sheet has been successfully produced. The process technology and application guides of Basoteel 's cold-rolled martensitic steels are summarized and analyzed in order to assist ongoing research and ensure correct applications of these ultra-high strength steel sheets.
Cold-rolled martensitic steel sheets are becoming widely applied in the automotive industry because of their ultra-high strength,which may result in satisfactory weight reduction. The grades of martensitic steel sheets are classified based on their tensile strength,which ranges from 980 to 1 700 MPa. The main applications include a series of structural parts of uniform cross-section or simple shape,such as bumper beams,door beams and door sills,etc. The study and development of cold-rolled martensitic steel sheets date back to 2007 in Baosteel,and some grades became commercially available in 2009. By 2015,Baosteel had commercially supplied thousands of tons of these steel sheets with tensile strength up to 1 400 MPa. Currently,1 500 MPa martensitic steel sheet is commercially available and 1 700 MPa martensitic steel sheet has been successfully produced. The process technology and application guides of Basoteel 's cold-rolled martensitic steels are summarized and analyzed in order to assist ongoing research and ensure correct applications of these ultra-high strength steel sheets.
引文
[1] NAKAOKA K,ARAKI K and KUBOTERA H.Development of w ater quenching technique for cold rolled steel strip[J]. Tetsu-to-Hagane,1976,62(6):634-643.
[2] ZHOU S,CHEN N L,ZHANG W M,et al. Cooling pow er measurement of w ater at various temperatures and flow rates[J]. Heat Treatment of M etals,2008,33(6):69-72.
[3] XIA L F. Metal heat treatment technology[M]. 5th ed.Harbin:Harbin Institute of Technology Press,2012:34-40.
[4] PAN J S and HU M J. Heat treatment technology[M].Beijing:Higher Education Press,2009:83-110.
[5] SATO M,UTSUMI Y and WATANABE K. Ultra-highstrength,quench-type,hot-rolled steel sheets of 1 620 MPa grade for automobile door impact beams[J]. Kobelco Technology Review,2008,28(10):13-17.
[6] MOHRBACHER H. Delayed cracking in ultra-high strength automotive steels:damage mechanisms and remedies by microstructural engineering[J]. M aterials Science and Technology,2008,24:1744-1755.