摘要
采用特制的乳化沥青作为结合料,配制了OGFC-13冷拌冷铺乳化沥青混合料,对所制备的试件采用烘箱养生,养生温度为90℃,养生时间为24 h。养生后的试件进行了路用性能测试与评价,包括高温、低温和抗车辙性能、抗水损害性能、动态模量和静态模量试验。结果表明,乳化型冷拌冷铺沥青混合料的路用性能都能满足热拌改性沥青混合料相应的技术要求。研究成果对冷拌冷铺沥青混合料的开发及应用具有实际的借鉴意义。
OGFC-13 cold mix cold emulsified asphalt mixture was prepared by using special emulsified asphalt as binder. The prepared test pieces were oven-conditioned, the curing temperature was 90 ℃, and the curing time was 24 h. After the health test, the road performance test and evaluation were carried out, including high temperature, low temperature and rutting resistance, water damage resistance, dynamic modulus and static modulus test. The results show that the road performance of the emulsified cold mix cold asphalt asphalt mixture can meet the corresponding technical requirements of the hot mix modified asphalt mixture. The research results have practical reference significance for the development and application of cold mixed cold asphalt mixture.
引文
[1]刘鹏.常温拌和沥青混合料性能评价与改善研究[D].北京:北京建筑大学,2017.
[2]瞿鑫. OGFC防水粘结层材料性能研究[D].长沙:长沙理工大学,2010.
[3]刘好.超薄磨耗层沥青混合料性能对比研究[D].西安:长安大学,2011.
[4]田俊壮,孙增智,武书华,等.基于模拟试验的沥青路面层间黏结性能研究[J].公路,2016,61(04):1-6.
[5]冯建亮.就地冷再生设备配里及工程运用[J].筑路机械与施工机械化,2008,(02):53-54.
[6] Zoorob S E, Hassan K E, Setyawan A. Cold Mix, Cold Laid Semi-Flexible Grouted Macadams, Mix Designs and Properties[C]//Proceedings of the 4th European Symposium on Performance of Bituminous and Hydraulic Materials in Pavements, Bitmat 4, 11-12 April 2002, Nottingham, Uk. 2002.
[7] Shu-Guang L I. Application of Cold Mix and Cold Laid Technology in Asphalt Pavement Patching of Rural Highway[J]. Northern Communications, 2012.
[8] MANES, Francisco, Maria, et al. Asphalt BinderModifying Additive Useful to Manufacture Hot Mix,Cold-Laid Bituminous Mixtures and Process for Manufacturing Both the Additive and the Mixtures[J].2002.
[9] Mcdade B S, Platt J, Clayton A. Cold mix asphalt aggregate paving material[J]. 2015.
[10] Serfass J P, Poirier J E, Henrat J P, et al. Influence of curing on cold mix mechanical performance[J].Materials and Structures, 2004,37(5):365-368.
[11] Zhang D. Design of Mixture Mixing Ratio for Emulsified Bitumen Cold Regenerated Surface[J]. Urban Roads Bridges&Flood Control, 2010.