Nd对车用镀层Zn-5Al-0.2Ti合金组织和耐蚀性的影响
|
摘要
采用扫描电镜(SEM)和X射线衍射(XRD)研究稀土Nd对Zn-5Al-0.2Ti合金显微组织和耐蚀性的影响。结果表明:Zn-5Al-0.2Ti合金添加Nd元素能促进α(Al)形核,阻碍η-Zn初生相的生长,提升了合金中的共晶组织含量。随着Nd含量增加,共晶组织平均粒径先降低再增大。当Nd含量等于0.1%时,合金具有最均匀的组织结构和最小平均粒径。随Nd含量增加,合金的耐腐蚀性能先上升后下降。当合金中Nd含量为0.1%时,合金具有最大的极化电阻与最小的腐蚀电流密度,有助于提升共晶组织的均匀性与致密性,获得最优耐蚀性。
The effects of Nd addition on the microstructure and corrosion resistance of Zn-5Al-0.2Ti alloy were investigated by SEM and XRD. The results show that Nd elements addition in Zn-5 Al-0.2 Ti alloy can promote the α(Al)nucleation and hinder the η-Zn growth, which can improve the eutectic content in the alloy. As Nd content increases, the average particle size of eutectic microstructure firstly decreases and then increases. When Nd content is 0.1%, the alloy has the most uniform microstructure and minimum average particle size. With the increase of Nd content, the corrosion resistance of the alloy firstly rises and then falls. When the Nd content in the alloy is 0.1%, the alloy has the largest polarization resistance and minimum corrosion current density, which can improve the uniformity and compactness of eutectic microstructure, and, then, the optimum corrosion resistanc can be obtained.
The effects of Nd addition on the microstructure and corrosion resistance of Zn-5Al-0.2Ti alloy were investigated by SEM and XRD. The results show that Nd elements addition in Zn-5 Al-0.2 Ti alloy can promote the α(Al)nucleation and hinder the η-Zn growth, which can improve the eutectic content in the alloy. As Nd content increases, the average particle size of eutectic microstructure firstly decreases and then increases. When Nd content is 0.1%, the alloy has the most uniform microstructure and minimum average particle size. With the increase of Nd content, the corrosion resistance of the alloy firstly rises and then falls. When the Nd content in the alloy is 0.1%, the alloy has the largest polarization resistance and minimum corrosion current density, which can improve the uniformity and compactness of eutectic microstructure, and, then, the optimum corrosion resistanc can be obtained.
引文
[1]贺志荣,何应,刘继拓,等.Al和RE对Zn-Al合金镀层组织和耐蚀性的影响[J].中国有色金属学报,2014,24(8):2020-2025.
[2]谢理明,李子全,刘劲松,等.稀土Nd对Mg-6Zn-Mn镁合金组织和腐蚀性能的影响[J].热加工工艺,2015,44(7):55-59.
[3]胡成杰,储双杰,王俊,等.稀土La对热镀锌层耐蚀性能的影响[J].腐蚀与防护,2011,32(7):517-520.
[4]杨廷志,吴长军,王建华,等.冷却条件和Ce含量对Galfan合金凝固组织及其耐蚀性的影响[J].稀有金属,2015,39(7):583-588.
[5]张国英,刘春明,魏丹,等.锌铝合金中稀土及杂质的晶界行为[J].东北大学学报(自然科学版),2007,28(2):209-212.
[6]许乔瑜,曾秋红.稀土在锌镀层中的应用及研究进展[J].腐蚀与防护,2009,30(1):19-21.
[7]赵国际,蓝秀琼,陈建华.微量Nd对Sn-6.5Zn合金及钎料/Cu界面结构的影响[J].热加工工艺,2013,42(15):204-206.
[8]王建华,王先德,苏旭平,等.镧对锌铝合金显微组织和力学性能的影响[J].铸造,2011,60(2):171-174.
[2]谢理明,李子全,刘劲松,等.稀土Nd对Mg-6Zn-Mn镁合金组织和腐蚀性能的影响[J].热加工工艺,2015,44(7):55-59.
[3]胡成杰,储双杰,王俊,等.稀土La对热镀锌层耐蚀性能的影响[J].腐蚀与防护,2011,32(7):517-520.
[4]杨廷志,吴长军,王建华,等.冷却条件和Ce含量对Galfan合金凝固组织及其耐蚀性的影响[J].稀有金属,2015,39(7):583-588.
[5]张国英,刘春明,魏丹,等.锌铝合金中稀土及杂质的晶界行为[J].东北大学学报(自然科学版),2007,28(2):209-212.
[6]许乔瑜,曾秋红.稀土在锌镀层中的应用及研究进展[J].腐蚀与防护,2009,30(1):19-21.
[7]赵国际,蓝秀琼,陈建华.微量Nd对Sn-6.5Zn合金及钎料/Cu界面结构的影响[J].热加工工艺,2013,42(15):204-206.
[8]王建华,王先德,苏旭平,等.镧对锌铝合金显微组织和力学性能的影响[J].铸造,2011,60(2):171-174.