摘要
本文按激励方式对智能窗进行了简单分类,详细阐述了温致变色智能窗的变色机理与结构,找出了影响温致变色智能窗相变温度的因素,分析了低相变温度温致变色玻璃的性能及应用,从而为低相变温度温致变色玻璃的市场推广做了铺垫。
引文
[1]廖嘉琳.智能调节“透反射率”节能玻璃膜浅析[J].住宅产业,2015(002):54-55.
[2]Wang L, R adue E,Kittiwatanakul S.Surface plasmon polaritons in VO2 thin films fortunable low-loss plasmonic applications[J].Optics Letters,2012,37 20 4335-4337.
[3]Morin F J. Oxides which show a Metal-to-InsulatorTransition at the Neel temperature[J].Phys. R eview Letter,1959,(3):34-36.
[4]Goodenough J. The two components of the crystallographic transition in VO2[J].J. Solid State Chem,1971,3(4):490-500.
[5]刘东青,郑文伟,程海峰等.温致变色二氧化钒薄膜的研究进展[J].材料导报,2009,23(11):105-109.
[6]Kana Kana J B,Ndjaka J M,Owono Ateba P, et al. Thermochromic VO2 thin films synthesized by rf-inverted cylindrical magnetron sputtering[J]. Surface science,2008,254(13):3959-3963.
[7]范蕾蕾,耿浩然,丁留伟.掺杂二氧化钒薄膜研究进展[J].现代制造工程,2009(05):126-128.
[8]Koo Hyun,Yoon Sejin,Kwon O-Jong. Effect of lattice misfit on the transition temperature of VO2 thin film[J].Journal of Material Science,2012,47(17):6397-6401.
[9]Fabien Béteille,Léo Mazerolles.Microstructure and metal-insulating transition of VO2 thin films[J]. Materials R esearch Bulletin,1999,34(14/15):2177-2184.
[10]梁继然,胡明,阚强等.晶粒尺寸对氧化钒薄膜电学与光学相变特性的影响[J].材料工程,2011,4:58-62.
[11]Chiu T W,Tonookaa K N,Kikuehia. Growth of b-axis oriented VO2thin films on glass Substrates using ZnO buffer layer[J]. Appl. Surf. Sci.,2010,256(22):6834-6837.
[12]李宏,李云,罗开飞,夏梦玲,王桂荣.热致变色VO2薄膜制备与影响相变因素[J].硅酸盐通报,2013,