A 60%Fe/Al_2O_3 catalyst was prepared by the co-precipitation method.It was reduced by H_2 to produce metallic Fe,which was then sulfided by CS_2 to Fe_(0.96) S and Fe_3S_4 or phosphided by triphenylphosphine(PPh3) in liquid phases to Fe2 P and Fe P.It was found that the iron sulfides(Fe0.96 S and Fe_3S_4) exhibited the low activity for the hydrodesulfurization(HDS) reactions.The HDS activity was also low on the Fe(metal)/Al_2O_3 and Fe_2 P/Al_2O_3 catalysts since they were converted into Fe0.96 S and Fe_3S_4 during the HDS reactions.In contrast,the FeP/Al_2O_3 was found to be stable and active for the HDS reactions.In particular,Fe P/Al_2O_3 possessed significantly smaller Fe P particles than Fe P/C,leading to the significant higher HDS activity of FeP/Al_2O_3 than Fe P/C.
A 60%Fe/Al_2O_3 catalyst was prepared by the co-precipitation method.It was reduced by H_2 to produce metallic Fe,which was then sulfided by CS_2 to Fe_(0.96) S and Fe_3S_4 or phosphided by triphenylphosphine(PPh3) in liquid phases to Fe2 P and Fe P.It was found that the iron sulfides(Fe0.96 S and Fe_3S_4) exhibited the low activity for the hydrodesulfurization(HDS) reactions.The HDS activity was also low on the Fe(metal)/Al_2O_3 and Fe_2 P/Al_2O_3 catalysts since they were converted into Fe0.96 S and Fe_3S_4 during the HDS reactions.In contrast,the FeP/Al_2O_3 was found to be stable and active for the HDS reactions.In particular,Fe P/Al_2O_3 possessed significantly smaller Fe P particles than Fe P/C,leading to the significant higher HDS activity of FeP/Al_2O_3 than Fe P/C.
引文
[1]Y.V.Vatutina,O.V.Klimov,K.A.Nadeina,I.G.Danilova,E.Y.Gerasimov,I.P.Prosvirin,A.S.Noskov.Appl.Catal.B:Environ.199(2016)23-32.
[2]C.S.Song,Catal.Today 86(2003)211-263.
[3]T.Fujikawa,H.Kimura,K.Kiriyama,K.Hagiwara,Catal.Today 111(2006)188-193.
[4]X.Q.Wang,P.Clark,S.T.Oyama,J.Catal.208(2002)321-331.
[5]M.Boudart,J.A.Cusumano and R.B.Levy,"New Catalytic Materials for the Liquefaction of Coal,Research Project 415,Final Report”,p.184.Catalytica Associates,Inc.,5 Palo Alto Square,Palo Alto,CA,1975.
[6]S.T.Oyama,J.Catal.216(2003)343-352.
[7]H.D.She,Y.Z.Chen,R.T.Wen,K.Zhang,G.H.Yue,D.L.Peng,Nanoscale Res.Lett.5(2010)786-790.
[8]Z.W.Yao,H.Hai,Z.C.Lai,X.H.Zhang,F.Peng,C.F.Yan,Top.Catal.55(2012)1040-1045.
[9]Q.X.Guan,W.Li,M.H.Zhang,K.Y.Tao,J.Catal.263(2009)1-3.
[10]G.J.Shi,J.Y.Shen,J.Mater.Chem.19(2009)2295-2297.
[11]Y.Zhao,Y.P.Zhao,H.S.Feng,J.Y.Shen,J.Mater.Chem.21(2011)8137-8145.
[12]L.Song,S.Zhang,Q.Ma,Chem.Eng.J.281(2015)281-285.
[13]J.E.Wang,X.G.Wang,Y.M.Yuan,A.Shuaib,J.Y.Shen,J.Energy Chem.25(2016)571-576.
[14]W.Robinson,J.N.M.vanGestel,T.I.Koranyi,S.Eijsbouts,A.M.vanderKraan,J.A.R.van Veen,V.H.J.deBeer,J.Catal.161(1996)539-550.
[15]Y.M.Yuan,H.Pei,H.Chen,L.Zuo,J.Y.Shen,Catal.Commun.100(2017)202-205.
[16]H.Y.Zhu,M.W.Xue,H.Chen,J.Y.Shen,Catal.Lett.134(2010)93-101.
[17]L.Chen,J.Y.Shen,Chin.J.Catal.33(2012)621-628.
[18]G.J.Shi,J.Y.Shen,Energy Fuels 23(2009)320-326.
[19]C.H.Bartholomew,Catal.Lett.7(1991)27-51.
[20]H.Y.Zhao,S.T.Oyama,Appl.Catal.B:Environ.164(2015)204-216.